Product Description |
Injection molding, Medium viscosity, High toughness at low temperature |
General |
Form Resin Pellets |
Feature Low Temperature Impact F1 Medium Viscosity |
Uses Telecommunications |
Physical Nominal Value Test Method |
Density / Specific Gravity(23 °C) 1.19 g/cm³ ISO 1183 |
Melt Viscosity(300 °C;1.0e+3 s-1) 600 Pa. s ISO 11443-A |
Melt Volume-Flow Rate, MVR(300 °C;1.2 kg) 10 cm³/10 min ISO 1133 |
Molding shrinkage, parallel(60x60x2;500 bar) 0.72 % ISO 2577 |
Molding shrinkage, normal(60x60x2;500 bar) 0.68 % ISO 2577 |
Mechanical Nominal Value Test Method |
Tensile Modulus(1 mm/min;23 °C) 2200 MPa ISO 527-1/-2 |
Tensile Stress, Yield(5 mm/min;23 °C) 60.0 MPa ISO 527-1/-2 |
Tensile Stress, Break(5 mm/min;23 °C) 70.0 MPa ISO 527-1/-2 |
Tensile Strain, Yield(5 mm/min;23 °C) 5.5 % ISO 527-1/-2 |
Tensile Strain, Break(5 mm/min;23 °C) 150 % ISO 527-1/-2 |
Flexural Modulus(2 mm/min;23 °C) 2300 MPa ISO 178 |
Flexural Stress(2 mm/min;23 °C) 90.0 MPa ISO 178 |
Notched Izod Impact Strength ISO 7391 |
23 °C;3 mm 70 kJ/m² |
-20 °C;3 mm 60 kJ/m² |
-30 °C;3 mm 60 kJ/m² |
-40 °C;3 mm 60 kJ/m² |
Thermal Nominal Value Test Method |
Vicat Softening Temperature(120 °C/h;50 N) 136 °C ISO 306 |
Flame Rating UL 94 |
1.5 mm V-0 |
2 mm 5VB |
2.5 mm 5VB |
Processing |
Nominal Value |
Drying Temperature - Dry Air Dryer<Injection> |
100 °C |
Drying Time - Dry Air Dryer<Injection> |
4.0 hr |
Mold Temperature<Injection> |
80 °C |
Standard Melt Temperature<Injection> |
280 - 300 °C |