2511HXGA5 is a PP Block co-polymer with 25% Glass fiber filler for extrusion process, features low melt flow, high flexural modulus and high heat resistance. It is suitable for auto parts and electrical appliances. | |||
General | |||
Form | Resin Pellets | ||
Filler | 25 % Glass Fiber | ||
Low Flow Block Copolymer Good Thermal Good Hardness |
|||
Uses Appliance Components Automotive Electrical | |||
Physical | Nominal Value | Test Method | |
Density / Specific Gravity | 1.07 g/cm³ | ASTM D792 | |
Melt Mass-Flow Rate, MFR(230 °C;2.16 kg) | 1.1 g/10min | ASTM D1238 | |
Rockwell Hardness, R-Scale(23 °C) | 96 | ASTM D785 | |
Mechanical | Nominal Value | Test Method | |
Tensile Strength, Yield(23 °C) | 63.3 MPa | ASTM D638 | |
Tensile Elongation, Break(23 °C) | 7.0 % | ASTM D638 | |
Flexural Modulus(23 °C) | 4810 MPa | ASTM D790 | |
Flexural Strength, Yield(23 °C) | 72.6 MPa | ASTM D790 | |
Notched Izod Impact, Area(23 °C) | 20.1 kJ/m² | ASTM D256 | |
Thermal | Nominal Value | Test Method | |
Deflection Temperature Under Load, Unannealed(0.45 MPa) | 159 °C | ASTM D648 | |
Processing | Nominal Value | ||
Drying Temperature<Extrusion> | 80 - 85 °C | ||
Drying Time<Extrusion> | 2.0 - 3.0 hr | ||
Melt Temperature<Extrusion> | 190 - 240 °C |