| Feature: | Oxidative Degradable |
|---|---|
| CAS No.: | 32131-17-2 |
| Formula: | (C12h22n2o2)N |
| Samples: |
BAG
|
|---|
| Customization: |
|---|
|
Shipping Cost:
Estimated freight per unit. |
about shipping cost and estimated delivery time. |
|---|
| Payment Method: |
|
|---|---|
| Initial Payment Full Payment |
| Currency: | US$ |
|---|
| Return&refunds: | You can apply for a refund up to 30 days after receipt of the products. |
|---|
Suppliers with verified business licenses
Audited Supplier Heat Conducting Nylon Unreinforced Heat Stabilized High Viscosity Polyamide 66
https://forever-plastics.en.made-in-china.com/product/rJwRvlcdZpWD/China-Nylon-PA6-GF33-PA66-Granules-PA6-with-30GF-Polyamide-PA66-30-GF-PA6-Material.html Heat-conducting nylon
| Product Description | ||
| Unreinforced, Heat Stabilized, High Viscosity Polyamide 66 | ||
| General | ||
| Form Resin Pellets | ||
| Feature High Viscosity | Good Thermal | |
| Physical | Nominal Value | Test Method |
| Density, dry | 1.14 g/cm³ | ISO 1183 |
| Dry: Molding Shrinkage, Across Flow | 1.3 % | ISO 294-4 |
| Dry: Molding Shrinkage, Flow | 1.3 % | ISO 294-4 |
| Dry: Water Absorption, Saturation(23 °C;2 mm) | 8.5 % | ISO 62 |
| Dry: Water Absorption, Equilibrium(50% RH;23 °C;2 | mm) 2.6 % | ISO 62 |
| Dry: Viscosity Number, (90% HCOOH) | 310 cm³/g | ISO 307 |
| Dry: Melt Density | 0.980 g/cm³ | |
| Mechanical | Nominal Value | Test Method |
| Dry: Tensile Modulus | 3100 MPa | ISO 527-2 |
| Condition: Tensile Modulus | 1200 MPa | ISO 527-2 |
| Dry: Tensile Stress, Yield | 84.0 MPa | ISO 527-2 |
| Condition: Tensile Stress, Yield | 55.0 MPa | ISO 527-2 |
| Dry: Tensile Strain, Yield | 4.3 % | ISO 527-2 |
| Condition: Tensile Strain, Yield | 29 % | ISO 527-2 |
| Dry: Nominal Tensile Strain at Break | 35 % | ISO 527-2 |
| Dry: Flexural Modulus | 2800 MPa | ISO 178 |
| Dry: Charpy Notched Impact Strength | ISO 179 1eA | |
| -30 °C | 6.0 kJ/m² | |
| 23 °C | 7.0 kJ/m² | |
| Condition: Charpy Notched Impact Strength | ISO 179 1eA | |
| -30 °C | 4.0 kJ/m² | |
| 23 °C | 21 kJ/m² | |
| Dry: Charpy Unnotched Impact Strength(23 °C) | No Break | ISO 179 1eU |
| Dry: Notched Izod Impact Strength(23 °C) | 6.0 kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Test Method |
| Dry: Heat Deflection Temperature, Unannealed | ||
| 0.45 MPa | 200 °C | ISO 75-2/B |
| 1.8 MPa | 70.0 °C | ISO 75-2/A |
| Dry: Vicat softening temperature | 221 °C | ISO 306/B50 |
| Dry: Melting Temperature(10 °C;min) | 262 °C | ISO 11357-3 |
| Dry: CLTE, Flow | 1.0E-4 cm/cm/°C | ISO 11359-2 |
| Dry: CLTE, Transverse | 1.0E-4 cm/cm/°C | ISO 11359-2 |
| Dry: Oxygen index | 20 % | ISO 4589-2 |
| Dry: FMVSS Flammability | DNI | FMVSS 302 |
| Dry: Thermal Conductivity of Melt | 0.16 W/m-K | |
| Dry: Specific Heat Capacity of Melt | 2790 J/kg/°C | |
| Electrical | Nominal Value | Test Method |
| Dry: Volume Resistivity | > 1E+11 ohms ·cm | IEC 62631-3-1 |
| Condition: Volume resistivity | 1E+9 ohms ·cm | IEC 62631-3-1 |
| Dry: Comparative Tracking Index | 600 V | IEC 60112 |
| Processing | Nominal Value | |
| Drying Temperature<Injection> | 80 °C | |
| Drying Time - Desiccant Dryer<Injection> | 2.0 - 4.0 hr | |
| Suggested Max Moisture<Injection> | 0.050 % | |
| Processing Temp, Melt<Injection> | 280 - 300 °C | |
| Melt Temperature, Optimum<Injection> | 290 °C | |
| Mold Temperature<Injection> | 50 - 90 °C | |
| Mold Temperature, Optimum<Injection> | 70 °C | |
| Holding Pressure<Injection> | 50.0 - 100 MPa | |
| Drying Recommended <Injection> | YES | |
| Hold Pressure Time<Injection> | 4.00 s/mm | |
| Maximum Screw Tangential Speed <Injection> | 24 m/min | |
| Drying Temperature<Extrusion> | 80 °C | |
| Drying Time<Extrusion> | 4.0 - 6.0 hr | |
| Suggested Max Moisture<Extrusion> | 0.050 % | |
| Melt Temperature<Extrusion> | 280 - 290 °C | |
| Extrusion Melt Temperature, Optimum<Extrusion> | 285 °C | |
| Dry: Ejection Temperature | 190 °C | |