Product Description | ||||
Superior flow, injection molding ABS. Good impact. For thin-wall applications. | ||||
General | ||||
Form | ||||
Feature | ||||
UL Yellow Card E207780-256888 | ||||
Appliances Electronic Displays Automotive Exterior |
Lighting Applications Lawn And Garden Equipment Constraction |
Industrial Applications 3d Printing Automotive Outdoor |
||
Physical | Nominal Value | Test Method | ||
Density / Specific Gravity | 1.04 g/cm³ | ASTM D792 | ||
Melt Mass-Flow Rate, MFR 230 °C;3.8 kg 220 °C;5 kg |
12 g/10min 12 g/10min |
ASTM D1238 ISO 1133 |
||
Molding Shrinkage, Flow(3.2 mm) | 0.50 - 0.80 % | Internal Method | ||
Melt Viscosity(240 °C;1.0e+3 sec^-1) | 172 Pa · s | ASTM D3835 | ||
Mechanical | Nominal Value | Test Method | ||
Tensile Modulus(5 mm/min) | 2480 MPa | ASTM D638 | ||
Tensile Strength, Yield(5 mm/min;Type I) | 46.0 MPa | ASTM D638 | ||
Tensile Strength, Break(5 mm/min;Type I) | 35.0 MPa | ASTM D638 | ||
Tensile Elongation, Yield(5 mm/min;Type I) | 2.0 % | ASTM D638 | ||
Tensile Elongation, Break(5 mm/min;Type I) | 18 % | ASTM D638 | ||
Flexural Modulus(1.3 mm/min;50 mm;Span) | 2620 MPa | ASTM D790 | ||
Flexural Strength, Yield(1.3 mm/min;50 mm;Span) | 79.0 MPa | ASTM D790 | ||
Notched Izod Impact(23 °C) | 240 J/m | ASTM D256 | ||
Instrumented Dart Impact, Total Energy(23 °C) | 21.0 J | ASTM D3763 |
Thermal | Nominal Value | Test Method |
Deflection Temperature Under Load, Unannealed 0.45 MPa;3.2 mm 1.8 MPa;3.2 mm |
95.0 °C 82.0 °C |
ASTM D648 |
Vicat Softening Temperature(50 °C/h;50 N;Rate A;Loading 2) | 98.0 °C | ASTM D1525 |
CLTE, Flow(-40 - 40 °C) | 8.8E-5 cm/cm/°C | ASTM E831 |
CLTE, Transverse(-40 - 40 °C) | 8.5E-5 cm/cm/°C | ASTM E831 |
RTI Elec | 60.0 °C | UL 746 |
RTI Imp | 60.0 °C | UL 746 |
RTI Str | 60.0 °C | UL 746 |
Flame Rating(1.5 mm) | HB | UL 94 |
Processing | Nominal Value | |
Drying Temperature<Injection> | 80 - 90 °C | |
Drying Time<Injection> | 2.0 - 4.0 hr | |
Suggested Max Moisture<Injection> | 0.10 % | |
Suggested Shot Size<Injection> | 50 - 70 % | |
Rear Temperature<Injection> | 190 - 200 °C | |
Middle Temperature<injection> | 200 - 210 °C | |
Front Temperature<Injection> | 205 - 225 °C | |
Nozzle Temperature<Injection> | 205 - 245 °C | |
Processing Temp, Melt<Injection> | 205 - 245 °C | |
Mold Temperature<Injection> | 50 - 70 °C | |
Back Pressure<Injection> | 0.300 - 0.700 MPa | |
Screw Speed<Injection> | 30 - 60 rpm | |
Vent Depth<Injection> | 0.038 - 0.051 mm | |
Drying Time, Cumulative<Injection> | 8 hrs |