PA66 Flexible Toughened and Plasticized Black Polyamide Resin Intended for Extrusion

• Feature: Oxidative Degradable
• CAS No.: 32131-17-2
• Formula: (C12h22n2o2)N
• Shipping Cost: Estimated freight per unit.: about shipping cost and estimated delivery time.
• Currency: US$
• Return&refunds: You can apply for a refund up to 30 days after receipt of the products.
• Model NO.: PA66-LC7602
• EINECS: 211-024-8
• Material: Polyamide(Nylon 6.66)/PA
• Usage: General Plastics, Engineering Plastics, Specialty Plastics
• Plastic Properties After Heated: Thermoplastic Plastics
• Plastic Forming Method: Injection
• Color: Black
• Form: Resin Pellets
• Chemical Substances: Nylon
• Processing Mode: Injection Molding/Extrusion
• UV: Fr
• Use: Electrical Appliances, Auto Parts, Office Supplies
• Certificates: ISO9001:2008.SGS.RoHS
• Filler: 10%-60% Glass Fiber
• Transport Package: Bag
• Specification: 25KG
• Trademark: Forever
• Origin: China
• HS Code: 390740000
• Production Capacity: 50000t/Year
• Package Size: 75.00cm * 55.00cm * 15.00cm
• Package Gross Weight: 25.010kg

Product Description

PA66 flexible toughened and plasticized black polyamide resin intended for extrusion
 Heat-conducting nylon

Product Description

Product Description
LC7602 BK010A is a flexible, toughened and plasticized black polyamide resin intended for extrusion applications. LCPA long chain polyamide resins provide an innovative and growing portfolio of flexible polymers with excellent thermal, chemical, and hydrolysis resistance. The diverse selection of LCPA grades is targeted for a range of performance characteristics, balancing temperature resistance, flexibility and low permeation.
General
Form	Resin Pellets
Feature	Hydrolysis Resistance   Outdoor	Chemical Resistant           Good Thermal
Physical		Nominal Value	Test Method
Resin ID		PA-HIP	ISO 1043
Part Marking Code, ISO 11469		PA-HIP	ISO 11469
Density, dry		1.03 g/cm³	ISO 1183
Dry: Melt Mass-Flow Rate, MFR(240 °C;5 kg)		12 g/10min	ISO 1133
Dry: Viscosity Number, (96% H2SO4)		144 cm³/g	ISO 307
Mechanical		Nominal Value	Test Method
Dry: Tensile Modulus		650 MPa	ISO 527-1/-2
Dry: Tensile Stress(50% Strain)		26.0 MPa	ISO 527-1/-2
Dry: Tensile Strain, Break		> 50 %	ISO 527-1/-2
Dry: Flexural Modulus		620 MPa	ISO 178
Dry: Charpy Notched Impact Strength			ISO 179 1eA
-40 °C		15 kJ/m²
23 °C		110 kJ/m²
Dry: Charpy Unnotched Impact Strength			ISO 179 1eU
-30 °C		No Break
23 °C		No Break
Condition: Charpy Unnotched Impact Strength(23 °C)		No Break	ISO 179 1eU
Thermal		Nominal Value	Test Method
Dry: Heat Deflection Temperature, Unannealed
0.45 MPa		55.0 °C	ISO 75-2/B
1.8 MPa		39.0 °C	ISO 75-2/A
Dry: Glass Transition Temperature(10 °C/min)		50.0 °C	ISO 11357-2
Conditioned: Glass Transition Temperature, Tg(10 °C/min)		40.0 °C	ISO 11357-2
Dry: Melting Temperature(10 °C/min)		208 °C	ISO 11357-3
Dry: Burning rate(1 mm;FMVSS 302)		< 100 mm/min	FMVSS 302;ISO 3795
Dry: FMVSS Flammability		B	FMVSS 302;ISO 3795
Processing			Nominal Value
Drying Temperature<Extrusion>			75 - 80 °C
Drying Time<Extrusion>			3.0 - 4.0 hr
Suggested Max Moisture<Extrusion>			≤ 0.060 %
Melt Temperature<Extrusion>			220 - 230 °C
Extrusion Melt Temperature, Optimum<Extrusion>			225 °C

 

                                                                                                                  Forever Co.,Ltd

 

With almost 20 years in the modified engineering plastics,Forever Plastics is a high-tech manufacture integrating R&D, production and sales of high-performance resin or polymer ,including PC,PP,PA6,PA66, PBT,PET, PC/ABS, PC/PBT, PC/PET alloy compounds,TPE,TPU, PE for rotomolding with the property of the flame retardant, glass fiber reinforced, high glossy, UV resistance.....with the annual output value of USD 65 million in 2021. 