Product Description | ||||
XHT2141 is a high flow, high heat polycarbonate copolymer. It is available in a range of opaque and limited transparent colors. | ||||
General | ||||
Form | Resin Pellets | |||
Feature | Good Thermal | |||
UL Yellow Card | E207780-100127670 | |||
Uses Automotive | Consumer | Electrical | ||
Physical | Nominal Value | Test Method | ||
Density / Specific Gravity | 1.2 1.2 g/cm³ |
ASTM D792 ISO 1183 |
||
Mold Shrinkage, Flow(3.2 mm) | 0.6 - 0.9 % | Method | ||
Melt Flow Rate[MFR](330 °C;2.16 kgf) | 46 g/10min | ASTM D1238 | ||
Water Absorption(23 °C;saturated) | 0.3 % | ISO 62-1 | ||
Moisture Absorption(50% RH;23 °C) | 0.23 % | ISO 62 | ||
Melt Volume Rate, MVR(2.16 kg;330 °C) | 43 cm³/10 min | ISO 1133 | ||
Mechanical | Nominal Value | Test Method | ||
Izod Impact, Notched 23 °C -30 °C 80*10*4;23 °C 80*10*4;-30 °C |
115 J/m 75 J/m 11 kJ/m² 10 kJ/m² |
ASTM D256 ASTM D256 ISO 180/1A ISO 180/1A |
||
Instrumented Dart Impact, Total Energy(23 °C) | 68 J | ASTM D3763 | ||
Unnotched Izod Impact Strength unnotched;80*10*3;23 °C 0 unnotched;80*10*3;-30 °C 0 |
NB kJ/m² NB kJ/m² |
ISO 180/1U | ||
Notched Izod Impact Strength notched;80*10*3;23 °C 0 notched;80*10*3;-30 °C 0 |
10 kJ/m² 9 kJ/m² |
ISO 180/1A | ||
C harpy Impact, V-Notched 23 °C;Edgew;80*10*3;sp =62mm 0 -30 °C;Edgew;80*10*3;sp =62mm 0 |
12 kJ/m² 9 kJ/m² |
ISO 179 1eA | ||
C harpy Impact, Unnotched 23 °C;Edgew;80*10*3;sp =62mm 0 -30 °C;Edgew;80*10*3;sp =62mm 0 |
NB kJ/m² NB kJ/m² |
ISO 179 1eU | ||
Tensile Stress, Yield | ||||
50 mm/min;Type I | 70 MPa | ASTM D638 | ||
50 mm/min | 70 MPa | ISO 527 | ||
Tensile Stress, Break | ||||
50 mm/min;Type I | 60 MPa | ASTM D638 | ||
50 mm/min | 60 MPa | ISO 527 | ||
Tensile Strain, Yield | ||||
50 mm/min;Type I | 6.5 % | ASTM D638 | ||
50 mm/min | 6.5 % | ISO 527 | ||
Tensile Strain, Break | ||||
50 mm/min;Type I | 90 % | ASTM D638 | ||
50 mm/min | 90 % | ISO 527 | ||
Tensile Modulus | ||||
5 mm/min | 2600 MPa | ASTM D638 | ||
1 mm/min | 2600 MPa | ISO 527 | ||
Flexural Stress, Yield | ||||
1.3 mm/min;50 mm;span | 110 MPa | ASTM D790 | ||
2 mm/min | 100 MPa | ISO 178 | ||
Flexural Modulus | ||||
1.3 mm/min;50 mm;span | 2550 MPa | ASTM D790 | ||
2 mm/min | 2450 MPa | ISO 178 | ||
Thermal | Nominal Value | Test Method | ||
UL Recognized(≥ 1.5 mm) | HB | UL 94 | ||
Glow Wire Ignition Temperature [GWIT](3 mm) | 875 °C | IEC 60695-2-13 | ||
Glow Wire Flammability Index 3 mm 2 mm 1 mm |
960 °C 960 °C 960 °C |
IEC 60695-2-12 | ||
Vicat Softening Temperature | ||||
Rate B/50 | 161 °C | ASTM D1525 | ||
Rate B/50 | 160 °C | ISO 306 | ||
Rate B/120 | 162 °C | ISO 306 | ||
Heat Deflection Temperature[HDT], Unannealed 0.45 MPa;3.2 mm 3.2 mm;1.82 MPa |
155 °C 145 °C |
ASTM D648 | ||
CTE, Flow | ||||
-40 - 40 °C | 6.0E-05 1/°C | ASTM E831 | ||
-40 - 40 °C | 6.0E-05 1/°C | ISO 11359-2 | ||
CTE, XFlow | ||||
-40 - 40 °C | 6.0E-05 1/°C | ASTM E831 | ||
-40 - 40 °C | 6.0E-05 1/°C | ISO 11359-2 | ||
Thermal Conductivity @ 25 °C(25 °C) | 0.2 W/m-K | ASTM C177 | ||
Ball Pressure Test(125°C +/- 2°C) | PASSES | IEC 60695-10-2 | ||
HDT/Bf(0.45) | 155 °C | ISO 75/Bf | ||
HDT/Af(1.8) | 142 °C | ISO 75/Af | ||
Metallized Haze Onset | 155 °C | Method | ||
Relative Temp Index, Elec | 150 °C | UL 746B | ||
Relative Temp Index, Mechanical with Impact | 130 °C | UL 746B | ||
Relative Temp Index, Mechanical without Impact | 150 °C | UL 746B | ||
Electrical | Nominal Value | Test Method | ||
Volume Resistivity | > 1.0E+17 ohms ·cm | ASTM D257 | ||
Surface Resistivity | > 1.E+17 ohms | ASTM D257 | ||
Dielectric Strength, in Oil(3.2 mm) | 22.6 kV/mm | ASTM D149 | ||
Dissipation Factor 100 Hz 1.0e+6 Hz |
3 3.1 |
ASTM D150 | ||
Comparative Tracking Index, CTI | PLC 3 | UL 746A | ||
Hot-wire Ignition, HWI(1.5 mm) | PLC 3 | UL 746A | ||
High Amp Arc Ignition, HAI(1.5 mm) | PLC 0 | UL 746A | ||
Processing | Nominal Value | |||
Drying Temperature<Injection> | 125 °C | |||
Drying Time<Injection> | 4 - 6 hrs | |||
Maximum Moisture Content<Injection> | 0.02 % | |||
Melt Temperature<Injection> | 290 - 350 °C | |||
Nozzle Temperature<Injection> | 285 - 345 °C | |||
Front, Zone 3 Temperature<Injection> | 290 - 350 °C | |||
Middle, Zone 2 Temperature<Injection> | 280 - 340 °C | |||
Rear, Zone 1 Temperature<Injection> | 270 - 330 °C | |||
Mold Temperature<Injection> | 85 - 130 °C | |||
Back Pressure<Injection> | 0.3 - 0.7 MPa | |||
Screw Speed <Injection> | 40 - 90 rpm | |||
Shot To Cylinder Size<Injection> | 40 - 60 % | |||
Vent Depth <Injection> | 0.025 - 0.08 mm |