Rzl36 Compound Is Based on Nylon 66 Resin Containing 30% Milled Glass 15% PTFE PA66

• Feature: Oxidative Degradable
• CAS No.: 32131-17-2
• Formula: (C12h22n2o2)N
• Shipping Cost: Estimated freight per unit.: about shipping cost and estimated delivery time.
• Currency: US$
• Return&refunds: You can apply for a refund up to 30 days after receipt of the products.
• Model NO.: PA66-RZL36
• EINECS: 211-024-8
• Material: Polyamide(Nylon 6.66)/PA
• Usage: General Plastics, Engineering Plastics, Specialty Plastics
• Plastic Properties After Heated: Thermoplastic Plastics
• Plastic Forming Method: Injection
• Color: Black
• Form: Resin Pellets
• Chemical Substances: Nylon
• Processing Mode: Injection Molding/Extrusion
• UV: Fr
• Use: Electrical Appliances, Auto Parts, Office Supplies
• Certificates: ISO9001:2008.SGS.RoHS
• Filler: 10%-50% Glass Fiber
• Transport Package: Bag
• Specification: 25KG
• Trademark: Forever
• Origin: China
• HS Code: 390740000
• Production Capacity: 50000t/Year
• Package Size: 75.00cm * 55.00cm * 15.00cm
• Package Gross Weight: 25.010kg

Product Description

RZL36 compound is based on Nylon 66 resin containing 30% milled glass 15% PTFE PA66
 Heat-conducting nylon

Product Description

Product Description
RZL36 compound is based on Nylon 6/6 resin containing 30% milled glass, 15% PTFE. Added features of this grade include: Wear Resistant, Dimensional Control.
General
Form	Resin Pellets
Filler                                         15 % PTFE                          30 % Milled Glass Fiber
Feature	Low Warpage   Internally Lubricated		Good Dimensional            Abrasion Resistant
Uses                                          Consumer		Electrical			Building and Construction
Physical		Nominal Value			Test Method
Mold Shrinkage, Flow		1.2 %			Method
Density / Specific Gravity		1.51 g/cm³			ISO 1183
Mechanical		Nominal Value			Test Method
Izod Impact, Unnotched(80*10*4;23 °C)		20 kJ/m²			ISO 180/1U
Izod Impact, Notched(80*10*4;23 °C)		4 kJ/m²			ISO 180/1A
Tensile Stress, Yield(5 mm/min)		54 MPa			ISO 527
Tensile Strain, Yield(5 mm/min)		2.1 %			ISO 527
Tensile Modulus(1 mm/min)		4800 MPa			ISO 527
Flexural Stress, Yield(2 mm/min)		94 MPa			ISO 178
Flexural Modulus(2 mm/min)		4300 MPa			ISO 178
Thermal		Nominal Value			Test Method
CTE, Flow(23°C to 60°C)		5.3E-05 1/°C			ISO 11359-2
CTE, XFlow(23°C to 60°C)		7.0E-05 1/°C			ISO 11359-2
HDT/Bf(0.45)		240 °C			ISO 75/Bf
HDT/Af(1.8)		121 °C			ISO 75/Af
Processing				Nominal Value
Drying Temperature<Injection>				80 °C
Drying Time<Injection>				4 hrs
Maximum Moisture Content<Injection>				0.15 - 0.25 %
Melt Temperature<Injection>				280 - 305 °C
Front, Zone 3 Temperature<Injection>				295 - 305 °C
Middle, Zone 2 Temperature<Injection>				280 - 295 °C
Rear, Zone 1 Temperature<Injection>				265 - 275 °C
Mold Temperature<Injection>				95 - 110 °C
Back Pressure<Injection>				0.2 - 0.3 MPa
Screw Speed <Injection>				30 - 60 rpm

                                                                                                                  Forever Co.,Ltd

 

With almost 20 years in the modified engineering plastics,Forever Plastics is a high-tech manufacture integrating R&D, production and sales of high-performance resin or polymer ,including PC,PP,PA6,PA66, PBT,PET, PC/ABS, PC/PBT, PC/PET alloy compounds,TPE,TPU, PE for rotomolding with the property of the flame retardant, glass fiber reinforced, high glossy, UV resistance.....with the annual output value of USD 65 million in 2021. 