Polycarbonate (PC) Copolymer Resin Is a UV Stabilized Opaque Grade

• Feature: Plastics
• CAS No.: 25766-59-0
• Formula: C6h4c(CH3)2c6h4oco2-]N
• Shipping Cost: Estimated freight per unit.: about shipping cost and estimated delivery time.
• Currency: US$
• Return&refunds: You can apply for a refund up to 30 days after receipt of the products.
• Model NO.: PC-XD2322
• EINECS: 618-371-8
• Material: Polycarbonates/PC
• Usage: General Plastics, Engineering Plastics, Specialty Plastics
• Plastic Properties After Heated: Thermoplastic Plastics
• Plastic Forming Method: Injection
• Color: Black
• Form: Resin Pellets
• Chemical Substances: Polycarbonate
• Processing Mode: Injection Molding/Extrusion
• UV: Fr
• Use: Electrical Appliances, Auto Parts, Office Supplies
• Certificates: ISO9001:2008.SGS.RoHS
• Filler: 10%-50% Glass Fiber
• Transport Package: Bag
• Specification: 25KG
• Trademark: Forever
• Origin: China
• HS Code: 390740000
• Production Capacity: 50000t/Year
• Package Size: 75.00cm * 55.00cm * 15.00cm
• Package Gross Weight: 25.010kg

Product Description

polycarbonate (PC) copolymer resin is a UV stabilized opaque grade

Product Description

 

 

Product Description
ELCRES XD2322 polycarbonate (PC) copolymer resin is a UV stabilized opaque grade. This resin offers UL94 [email protected] flame retardancy based on non-bromine, non-chlorine FR system, excellent low temperature ductility characteristics and processability. ELCRES XD2322 resin is an excellent candidate for a wide range of applications  such as electronic vehicles (EV) and 5G devices.
General
Form	Resin Pellets
Feature	High Impact   Non-Chlorinated	Outdoor		Non-Brominated & Non- Chlorinated Flame   Retardant
Uses	Consumer   Energy Storage	Healthcare                         Electrical
Physical		Nominal Value		Test Method
Density / Specific Gravity		1.19 1.19 g/cm³		ASTM D792 ISO 1183
Mold Shrinkage, Flow(3.2 mm)		0.4 - 0.8 %		Method
Mold Shrinkage, XFlow(3.2 mm)		0.4 - 0.8 %		Method
Melt Flow Rate[MFR](300 °C;1.2 kgf)		16 g/10min		ASTM D1238
Water Absorption(23 °C;saturated)		0.4 %		ISO 62-1
Moisture Absorption(23 °C;50% RH/Equilibrium)		0.15 %		ISO 62-4
Melt Volume Rate, MVR(1.2 kg;MVR at 300 °C)		15 cm³/10 min		ISO 1133
UV light, water exposure/immersion		f1		UL 746C
Mechanical		Nominal Value		Test Method
Izod Impact, Notched				ASTM D256
23 °C		780 J/m
-30 °C		652 J/m
-40 °C		360 J/m
Instrumented Dart Impact, Total Energy(23 °C)		66 J		ASTM D3763
Unnotched Izod Impact Strength				ISO 180/1U
unnotched;80*10*3;23 °C 0		NB kJ/m²
unnotched;80*10*3;-30 °C 0		NB kJ/m²
Notched Izod Impact Strength notched;80*10*3;23 °C 0 notched;80*10*3;-30 °C 0		63 kJ/m² 29 kJ/m²		ISO 180/1A
Tensile Stress, Yield
50 mm/min;Type I		58 MPa		ASTM D638
50 mm/min		56 MPa		ISO 527
Tensile Stress, Break
50 mm/min;Type I		59 MPa		ASTM D638
50 mm/min		57 MPa		ISO 527
Tensile Strain, Yield
50 mm/min;Type I		6 %		ASTM D638
50 mm/min		6 %		ISO 527
Tensile Strain, Break
50 mm/min;Type I		112 %		ASTM D638
50 mm/min		108 %		ISO 527
Tensile Modulus
5 mm/min		2100 MPa		ASTM D638
1 mm/min		2000 MPa		ISO 527
Flexural Strength
1.3 mm/min;50 mm;span		92 MPa		ASTM D790
2 mm/min		87 MPa		ISO 178
Flexural Modulus
1.3 mm/min;50 mm;span		2400 MPa		ASTM D790
2 mm/min		2100 MPa		ISO 178
Thermal		Nominal Value		Test Method
Glow Wire Flammability Index(1.5 mm)		960 °C		IEC 60695-2-12
Glow Wire Ignition Temperature [GWIT](1.5 mm)		825 °C		IEC 60695-2-13
UL Recognized ≥ 3 mm ≥ 1.5 mm		5VA V-0		UL 94
Relative Temp Index, Elec		125 °C		UL 746B
Relative Temp Index, Mechanical with Impact		115 °C		UL 746B
Relative Temp Index, Mechanical without Impact		125 °C		UL 746B
Vicat Softening Temperature(Rate B/50)		140 °C		ASTM D1525
Heat Deflection Temperature[HDT], Unannealed(3.2 mm;1.82 MPa)		123 °C		ASTM D648
HDT/Af(1.8)		118 °C		ISO 75/Af
CTE, Flow(-40 - 40 °C)		6.1e-05 1/°C		ASTM E831
CTE, XFlow(-40 - 40 °C)		6.2e-05 1/°C		ASTM E831
Electrical		Nominal Value		Test Method
Comparative tracking index M		150 V		IEC 60112
Comparative Tracking Index, CTI		PLC 3		UL 746A
High Amp Arc Ignition, HAI 3 mm 1.5 mm		PLC 0 PLC 1		UL 746A
Hot-wire Ignition, HWI 3 mm 1.5 mm		PLC 2 PLC 3		UL 746A
Processing			Nominal Value
Drying Temperature<Injection>			120 °C
Drying Time<Injection>			3 - 4 hrs
Drying Time, Cumulative<Injection>			48 hrs
Maximum Moisture Content<Injection>			0.02 %
Melt Temperature<Injection>			295 - 315 °C
Nozzle Temperature<Injection>			290 - 310 °C
Front, Zone 3 Temperature<Injection>			295 - 315 °C
Middle, Zone 2 Temperature<Injection>			280 - 305 °C
Rear, Zone 1 Temperature<Injection>			270 - 295 °C
Mold Temperature<Injection>			70 - 95 °C
Back Pressure<Injection>			0.3 - 0.7 MPa
Screw Speed <Injection>			40 - 70 rpm
Shot To Cylinder Size<Injection>			40 - 60 %
Vent Depth <Injection>			0.025 - 0.076 mm

 

                                                                                                                  Forever Co.,Ltd

 

With almost 20 years in the modified engineering plastics,Forever Plastics is a high-tech manufacture integrating R&D, production and sales of high-performance resin or polymer ,including PC,PP,PA6,PA66, PBT,PET, PC/ABS, PC/PBT, PC/PET alloy compounds,TPE,TPU, PE for rotomolding with the property of the flame retardant, glass fiber reinforced, high glossy, UV resistance.....with the annual output value of USD 65 million in 2021. 

Our customers are Osram,Cree,,Siemens,etc. for years in the electrical&electronics components, Automotive parts, House appliance,LED lights.....