MVR (300°C/1.2 kg) 6.0 cm³/10 min; 10 % glass fiber reinforced; flame retardant; UL 94V-0/1.5 mm and 5VA/3.0 mm; high viscosity; UV stabilized; easy release; injection molding - melt temperature 310 - 330°C; available in opaque colors only |
||||
General | ||||
Form | Resin Pellets | |||
Filler | 10 % Glass Fiber | |||
Feature | High Viscosity | |||
UL Yellow Card | E41613-583704 | |||
Uses | PV Convertor Box smart meter |
LED housing and base Energy Storage | ||
Physical | Nominal Value | Test Method | ||
Density / Specific Gravity(23 °C) | 1.27 g/cm³ | ISO 1183 | ||
Apparent Bulk Density, Pellets | 0.64 g/cm³ | ISO 60 | ||
Melt Mass-Flow Rate, MFR(300 °C;1.2 kg) | 7.0 g/10min | ISO 1133 | ||
Melt Volume-Flow Rate, MVR(300 °C;1.2 kg) | 6.00 cm³/10 min | ISO 1133 | ||
Molding Shrinkage, Across Flow | ||||
0.40 - 0.60 % | ISO 2577 | |||
2 mm;500 bar;60x60x2mm;280 °C | 0.45 % | ISO 294-4 | ||
Molding Shrinkage, Flow | ||||
0.40 - 0.60 % | ISO 2577 | |||
2 mm;500 bar;60x60x2mm | 0.60 % | ISO 294-4 | ||
Water Absorption, Saturation(23 °C) | 0.26 % | ISO 62 | ||
Water Absorption, Equilibrium(50% RH;23 °C) | 0.10 % | ISO 62 | ||
Ball Indentation Hardness | 128 MPa | ISO 2039-1 | ||
Mechanical | Nominal Value | Test Method | ||
Tensile Modulus(23 °C) | 3800 MPa | ISO 527-2/1 | ||
Tensile Stress, Yield(23 °C) | 64.0 MPa | ISO 527-2/5 | ||
Tensile Stress, Break(23 °C) | 45.0 MPa | ISO 527-2/5 | ||
Tensile Strain, Yield(23 °C) | 4.6 % | ISO 527-2/5 | ||
Tensile Strain, Break(23 °C) | 15 % | ISO 527-2/5 | ||
Tensile creep modulus 1 hr 1.0e+3 hr |
3600 MPa 2900 MPa |
ISO 899-1 | ||
Flexural Modulus(2 mm/min;23 °C) | 3600 MPa | ISO 178 | ||
Flexural Stress 2 mm/min;23 °C 2 mm/min;3.5% Strain;23 °C |
105 MPa 95.0 MPa |
ISO 178 | ||
Flexural Strain at Flexural Strength(2 mm/min;23 °C) | 5.8 % | ISO 178 | ||
C harpy Notched Impact Strength, Complete Break(23 °C;3 mm) | 10 kJ/m² | ISO 179 1eA | ||
C harpy Unnotched Impact Strength, Complete Break -60 °C -30 °C 23 °C |
100 kJ/m² 120 kJ/m² 150 kJ/m² |
ISO 179 1eU | ||
Notched Izod Impact Strength, Complete Break(23 °C;3 mm) | 10 kJ/m² | ISO 180/1A | ||
Multi-Axial Instrumented Impact Energy -30 °C 23 °C |
15.0 J 25.0 J |
ISO 6603-2 | ||
Multi-Axial Instrumented Impact, Peak Force -30 °C 23 °C |
3700 N 4000 N |
ISO 6603-2 | ||
Thermal | Nominal Value | Test Method | ||
Heat Deflection Temperature, Unannealed 0.45 MPa 1.8 MPa |
141 °C 135 °C |
ISO 75-2/B ISO 75-2/A |
||
Vicat Softening Temperature | 143 °C 144 °C |
ISO 306/B50 ISO 306/B120 |
||
Ball Pressure Test(136 °C) | Pass | IEC 60695-10-2 | ||
CLTE, Flow(23 - 55 °C) | 4.0E-5 cm/cm/°C | ISO 11359-2 | ||
CLTE, Transverse(23 - 55 °C) | 6.5E-5 cm/cm/°C | ISO 11359-2 | ||
Thermal Conductivity, Across Flow(23 °C) | 0.22 W/m-K | ISO 8302 | ||
RTI Elec(1.5 mm) | 125 °C | UL 746 | ||
RTI Imp(1.5 mm) | 115 °C | UL 746 | ||
RTI Str(1.5 mm) | 125 °C | UL 746 | ||
Flame Rating 1.5 mm 6 mm |
V-0 5VA |
UL 94 | ||
Flame Rating, NC, BK, GY(3 mm) | 5VA | UL 94 | ||
Glow Wire Flammability Index 0.75 mm 1.5 mm 3 mm |
960 °C 960 °C 960 °C |
IEC 60695-2-12 | ||
Glow Wire Ignition Temperature [GWIT] 1 mm 1.5 mm 3 mm |
825 °C 900 °C 900 °C |
IEC 60695-2-13 | ||
Oxygen Index, Procedure A | 35 % | ISO 4589-2 | ||
Application of Flame from Small Burner, Method K and | FK1 - F1 | DIN 53438-1 | ||
Burning Rate, US-FMVSS( > 1 mm) | passed | ISO 3795 | ||
Flash Ignition Temperature | 470 °C | ASTM D1929 | ||
Self Ignition Temperature | 550 °C | ASTM D1929 | ||
Electrical | Nominal Value | Test Method | ||
Surface Resistivity | 1.0E+16 ohms | IEC 60093 | ||
Volume Resistivity(23 °C) | 1.0E+16 ohms ·cm | IEC 60093 | ||
Electric Strength(23 °C;1 mm) | 36 kV/mm | IEC 60243-1 | ||
Relative Permittivity 100 Hz;23 °C 23 °C;1.0e+6 Hz |
3.20 3.20 |
IEC 60250 | ||
Dissipation Factor 100 Hz;23 °C 23 °C;1.0e+6 Hz |
1.0E-3 9.0E-3 |
IEC 60250 | ||
Comparative Tracking Index, Solution A | 175 V | IEC 60112 | ||
Comparative Tracking Index, Solution B | 125 V | IEC 60112 | ||
Chemical | Nominal Value | Test Method | ||
Electrolytical Corrosion(23 °C) | A1 | IEC 60426 | ||
Processing | Nominal Value | |||
Drying Temperature - Dry Air Dryer<Injection> | 120 °C | |||
Drying Time - Dry Air Dryer<Injection> | 4.0 hr | |||
Suggested Max Moisture<Injection> | < 0.020 % | |||
Suggested Shot Size<Injection> | 30 - 70 % | |||
Rear Temperature<Injection> | 250 - 270 °C | |||
Middle Temperature<injection> | 270 - 290 °C | |||
Front Temperature<Injection> | 285 - 305 °C | |||
Nozzle Temperature<Injection> | 270 - 305 °C | |||
Processing Temp, Melt<Injection> | 280 - 320 °C | |||
Mold Temperature<Injection> | 70 - 110 °C | |||
Back Pressure<Injection> | 10.0 - 20.0 MPa | |||
Vent Depth <Injection> | 0.025 - 0.075 mm | |||
Standard Melt Temperature<Injection> | 300 °C | |||
Hold Pressure<Injection> | 50 - 75 % | |||
Peripheral Screw Speed <Injection> | 0.05 - 0.2 m/s |