Product Description | ||||
Formolene® 6535N is an engineered, medium impact copolymer polypropylene. It was specifically developed to meet the OEM demands for automotive interior trim applications, with proven injection molding economy. The optimal stiffness and impact balance also provides for utility in industrial applications including bins and crates, and small appliances. Material has been approved under automotive specifications - FCA MS-DB-500 CPN 3560 and CPN 4732, Ford WSS-M4D638-B, GM16208-T1, Renault Nissan AS5, and Toyota TSM 5514G Class 2. This material is free of animal-derived content. | ||||
General | ||||
Form | Resin Pellets | |||
Ductile Feature |
Enhanced Stiffness No Animal Derived Components |
High Impact | ||
Industrial Applications White Goods & Small Appliances |
Crates | Automotive Interior | ||
Physical | Nominal Value | Test Method | ||
Density | 0.900 g/cm³ | ASTM D1505;ISO 1183 |
||
Melt Mass-Flow Rate, MFR(230 °C;2.16 kg) | 35 g/10min | ASTM D1238;ISO 1133 |
||
Durometer Hardness, Shore D, Injection Molded | 63 | ASTM D2240 |
Mechanical | Nominal Value | Test Method |
Tensile Modulus, injection molded | 1200 MPa | ISO 527-2/50 |
Tensile Strength, Yield, Injection molded | ||
50 mm/min | 24.0 MPa 23.9 MPa |
ASTM D638 ISO 527-2/50 |
Tensile Strain, Yield, Injection molded | 6.0 % | ISO 527-2/50 |
Tensile Strain, Break, Injection molded | ||
50 mm/min | 100 % 80 % |
ASTM D638 ISO 527-2/50 |
Flexural Modulus, Injection Molded(1.3 mm/min;1% Secant) | 1140 MPa | ASTM D790 |
Flexural Modulus, Chord(2 mm/min) | 1150 MPa | ISO 178 |
Notched Izod Impact, Injection Molded | ||
-18 °C | 64 J/m | ASTM D256A |
0 °C | 80 J/m | ASTM D256A |
23 °C | 130 J/m | ASTM D256A |
-40 °C | 4.0 kJ/m² | ISO 180 |
-18 °C | 6.0 kJ/m² | ISO 180 |
23 °C | 13 kJ/m² | ISO 180 |
Thermal | Nominal Value | Test Method |
Deflection Temperature Under Load, Unannealed, Injection Molded 0.45 MPa 1.8 MPa |
97.0 °C 52.0 °C |
ASTM D648 |
Deflection Temperature Under Load, Unannealed 0.45 MPa 1.8 MPa |
95.0 °C 52.0 °C |
ISO 75-2/Be ISO 75-2/Ae |