Feature: | Resin Pellets |
---|---|
CAS No.: | 25037-45-0 |
Formula: | 25037-45-0 |
Samples: |
25kg/bag
|
---|
Customization: |
---|
Shipping Cost:
Estimated freight per unit. |
about shipping cost and estimated delivery time. |
---|
Payment Method: | |
---|---|
Initial Payment Full Payment |
Currency: | US$ |
---|
Return&refunds: | You can apply for a refund up to 30 days after receipt of the products. |
---|
Suppliers with verified business licenses
Product Description | ||||
Ultraform S 2320 003 UNC Q600 is an easy flowing and rapidly freezing injection molding POM grade. Contains a mold release agent. Applications Typical applications include difficult, thin-walled parts. | ||||
General | ||||
Form | Resin Pellets | |||
Feature | Excellent Processability Ec 1907/2006 (Reach) | |||
UL Yellow Card E36632-531689 | ||||
Uses | Thin-walled Parts | |||
Physical | Nominal Value | Test Method | ||
Density / Specific Gravity | 1.40 g/cm³ | ASTM D792;ISO 1183 |
||
Melt Volume-Flow Rate, MVR(190 °C;2.16 kg) | 11 cm³/10 min | ISO 1133 | ||
Molding Shrinkage, Flow | ||||
3.18 mm | 2.0 % 2.1 % |
No Standard ISO 294-4 |
||
Molding Shrinkage, Across Flow | 2.1 % | ISO 294-4 | ||
Water Absorption, Saturation 23 °C |
0.80 % 0.80 % |
ASTM D570 ISO 62 |
||
Water Absorption, Equilibrium 50% RH 50% RH;23 °C |
0.20 % 0.20 % |
ASTM D570 ISO 62 |
Mechanical | Nominal Value | Test Method |
Tensile Modulus(23 °C) | 2700 MPa | ISO 527-2 |
Tensile Strength, Yield | ||
23 °C | 65.0 MPa | ASTM D638;ISO 527-2 |
-40 °C | 93.0 MPa | ISO 527-2 |
80 °C | 33.0 MPa | ISO 527-2 |
Tensile Elongation, Yield(23 °C) | 9.0 % | ASTM D638;ISO 527-2 |
Nominal Tensile Strain at Break(23 °C) | 28 % | ISO 527-2 |
Tensile creep modulus 1 hr 1000 hr |
1900 MPa 1300 MPa |
ISO 899-1 |
Flexural Modulus(23 °C) | 2620 MPa | ASTM D790 |
Charpy Notched Impact Strength -30 °C 23 °C |
5.0 kJ/m² 5.5 kJ/m² |
ISO 179 |
Charpy Unnotched Impact Strength -30 °C 23 °C |
170 kJ/m² 180 kJ/m² |
ISO 179 |
Notched Izod Impact -40 °C 23 °C |
50 J/m 60 J/m |
ASTM D256 |
Thermal | Nominal Value | Test Method |
Deflection Temperature Under Load, Unannealed | ||
0.45 MPa | 160 °C | ASTM D648 |
1.8 MPa | 110 °C | ASTM D648 |
0.45 MPa | 156 °C | ISO 75-2/B |
1.8 MPa | 100 °C | ISO 75-2/A |
Peak Melting Temperature | 167 °C | ASTM D3418;ISO 3146 |
CLTE, Flow | 6.0E-5 cm/cm/°C |
ASTM E831 |
1.1E-4 cm/cm/°C | No Standard |
Electrical | Nominal Value | Test Method |
Surface Resistivity 1.5 mm |
1.0E+13 ohms 1.0E+13 ohms |
ASTM D257 IEC 60093 |
Volume Resistivity 1.5 mm |
1.0e+15 ohms·cm 1.0e+15 ohms·cm |
ASTM D257 IEC 60093 |
Electric Strength | 40 kV/mm | IEC 60243-1 |
Dielectric Constant 100 Hz 1000000 Hz |
3.80 3.80 |
IEC 60250 |
Dissipation Factor 100 Hz 1000000 Hz |
1.0E-3 5.0E-3 |
IEC 60250 |
Comparative Tracking Index | 600 V | IEC 60112 |
Processing | Nominal Value | |
Drying Temperature<Injection> | 80 - 110 °C | |
Drying Time<Injection> | 2.0 - 4.0 hr | |
Suggested Max Moisture<Injection> | 0.15 % | |
Processing Temp, Melt<Injection> | 190 - 230 °C | |
Mold Temperature<Injection> | 60 - 120 °C | |
Injection Pressure<Injection> | 3.50 - 7.00 MPa |
Product Description | ||||
A semi-conductive grade of acetal copolymer for applications requiring rapid dissipation of static build- up.Information provided by Celanese Corporation. | ||||
General | ||||
Form | Resin | Pellets | ||
Physical | Nominal Value | Test Method | ||
Density / Specific Gravity | 1.40 g/cm³ | |||
Water Absorption | 0.21 % | ASTM D570 | ||
Moisture Absorption at Equilibrium | 0.80 % | ASTM D570 | ||
Linear Mold Shrinkage | 2.2 % | |||
Linear Mold Shrinkage, Transverse | 1.8 % | |||
Hardness, Rockwell R | 111 | ASTM D785 | ||
Mechanical | Nominal Value | Test Method | ||
Tensile Strength, Yield | 37.0 MPa | ASTM D638 | ||
Elongation at Break | 30 % | ASTM D638 | ||
Flexural Strength | 52.0 MPa | ASTM D790 | ||
Flexural Modulus | 2100 MPa | ASTM D790 | ||
Compressive Strength | 66.0 MPa | ASTM D695 | ||
Shear Strength | 40.0 MPa | ASTM D732 | ||
Izod Impact, Notched Temperature; 23 °C Temperature; -29 °C |
50 J/m 30 J/m |
ASTM D256 | ||
Thermal | Nominal Value | Test Method | ||
Deflection Temperature Pressure; 0.46 MPa Pressure; 1.8 MPa |
152 °C 106 °C |
ASTM D648 | ||
Flammability, UL94 | HB | UL 94 |