| Feature: | Oxidative Degradable |
|---|---|
| CAS No.: | 32131-17-2 |
| Formula: | (C12h22n2o2)N |
| Samples: |
BAG
|
|---|
| Customization: |
|---|
|
Shipping Cost:
Estimated freight per unit. |
about shipping cost and estimated delivery time. |
|---|
| Payment Method: |
|
|---|---|
| Initial Payment Full Payment |
| Currency: | US$ |
|---|
| Return&refunds: | You can apply for a refund up to 30 days after receipt of the products. |
|---|
Suppliers with verified business licenses
Audited Supplier PPA 33% glass reinforced heat stabilized lubricated high performance polyamide resin
https://forever-plastics.en.made-in-china.com/product/rJwRvlcdZpWD/China-Nylon-PA6-GF33-PA66-Granules-PA6-with-30GF-Polyamide-PA66-30-GF-PA6-Material.html Heat-conducting nylon
| General |
| Form Resin Pellets |
| Filler 33 % Glass Fiber |
| Feature Contain Slip |
| Uses Automotive Components Valve Parts Socket |
| Physical Nominal Value Test Method |
| Density / Specific Gravity 1.41 g/cm³ ISO 1183 |
| Mold Shrinkage, MD 0.3 % ISO 294-4 |
| Mold Shrinkage, TD 0.7 % ISO 294-4 |
| Water Absorption 0.2 % |
| Mechanical Nominal Value Test Method |
| Tensile Strength(20 mm/min) 195 MPa ISO 527-2 |
| Elongation at Break(20 mm/min) 3 % ISO 527-2 |
| Flexural Strength(2 mm/min) 245 MPa ISO 178 |
| Flexural Modulus(2 mm/min) 9000 MPa ISO 178 |
| Notched Izod Impact Strength 11.5 kJ/m² ISO 180 |
| Thermal Nominal Value Test Method |
| Heat Deflection Temperature(0.45 MPa) 310 °C ISO 75-2/B |
| Flammability(1.6 mm) HB UL94 |
| Processing Nominal Value |
| Drying Temperature 120 - 150 °C |
| Drying Time 3 - 5 h |
| Mold Temperature 120 - 150 °C |
| Melt Temperature 315 - 335 °C |