Audited Supplier | Product Description | |||||
| 1000P Resin is an unreinforced amorphous polyetherimide (PEI) powder. This powder is available with an average particle size (D50) of 350 micron. It may offer a high glass transition temperature (Tg) of 217°C. Features are excellent mechanical, electrical and dimensional properties up to high temperatures. The material may offer very good chemical resistance for an amorphous material and is inherently flame retarded. The material is RoHS Compliant. The base material is transparent amber colored. | |||||
| General | |||||
| Form | Resin Pellets | ||||
| Feature | Chemical Resistant Hydrolysis Resistance |
Good Dimensional Good Thermal Excellent Epoxy Adhesion |
|||
| Uses Industria | |||||
| Physical | Nominal Value | Test Method | |||
| Melt Volume Rate, MVR(5 kg;MVR at 360 °C) | 13 cm³/10 min | ISO 1133 | |||
| Density / Specific Gravity | |||||
| 1.27 g/cm³ | ISO 1183 | ||||
| 1.27 | ASTM D792 | ||||
| Water Absorption | |||||
| 24 hrs;23 °C | 0.25 % | ISO 62-1 | |||
| 23 °C;saturated | 1.25 % | ISO 62-1 | |||
| 24 hrs;23 °C | 0.25 % | ASTM D570 | |||
| 23°C/Saturated | 1.25 % | ASTM D570 | |||
| Moisture Absorption 23 °C;50% RH/24hrs 23 °C;50% RH/Equilibrium |
0.2 % 0.7 % |
ISO 62-4 | |||
| Melt Flow Rate[MFR](337 °C;6.6 kgf) | 9 g/10min | ASTM D1238 | |||
| Poisson's Ratio | 0.36 | ASTM E132 | |||
| Hardness, Rockwell M | |||||
| 106 | ISO 2039-2 | ||||
| 109 | ASTM D785 | ||||
| Mechanical | Nominal Value | Test Method | |||
| Izod Impact, Notched | |||||
| 80*10*4;23 °C | 6 kJ/m² | ISO 180/1A | |||
| 80*10*4;-30 °C | 6 kJ/m² | ISO 180/1A | |||
| 23 °C | 53 J/m | ASTM D256 | |||
| -30 °C | 50 J/m | ASTM D256 | |||
| C harpy Impact, V-Notched 80*10*4;23 °C;edgew;sp =62 mm 80*10*4;-30 °C;edgew;sp =62 mm |
4 kJ/m² 4 kJ/m² |
ISO 179 1eA | |||
| Izod Impact, Reverse Notched(3.2 mm) | 1335 J/m | ASTM D256 | |||
| Gardner(23 °C) | 36 J | ASTM D3029 | |||
| Flexural Modulus | |||||
| 2 mm/min | 3300 MPa | ISO 178 | |||
| 1.3 mm/min;50 mm;span | 3200 MPa | ASTM D790 | |||
| 2.6 mm/min;span;100 mm | 3400 MPa | ASTM D790 | |||
| Flexural Stress, Yield | |||||
| 2 mm/min | 160 MPa | ISO 178 | |||
| 1.3 mm/min;50 mm;span | 165 MPa | ASTM D790 | |||
| 2.6 mm/min;span;100 mm | 160 MPa | ASTM D790 | |||
| Ball Indentation Hardness(H358/30) | 140 MPa | ISO 2039-1 | |||
| Tensile Modulus | |||||
| 1 mm/min | 3200 MPa | ISO 527 | |||
| 5 mm/min | 3350 MPa | ASTM D638 | |||
| Tensile Strain, Break | |||||
| 50 mm/min | 50 % | ISO 527 | |||
| 50 mm/min;Type I | 60 % | ASTM D638 | |||
| 5 mm/min;Type I | 60 % | ASTM D638 | |||
| Tensile Strain, Yield | |||||
| 50 mm/min | 6 % | ISO 527 | |||
| 50 mm/min;Type I | 7 % | ASTM D638 | |||
| 5 mm/min;Type I | 7 % | ASTM D638 | |||
| Tensile Stress, Yield | |||||
| 50 mm/min | 110 MPa | ISO 527 | |||
| 50 mm/min;Type I | 115 MPa | ASTM D638 | |||
| 5 mm/min;Type I | 110 MPa | ASTM D638 | |||
| Taber Abrasion(CS-17;1 kg;1000cy) | 10 mg | ASTM D1044 | |||
| Thermal | Nominal Value | Test Method | |||
| Oxygen Index | 47 % 47 % |
ASTM D2863 ISO 4589 |
|||
| HDT/Bf(0.45 MPa;Flatw 80*10*4;sp =64mm) | 209 °C | ISO 75/Bf | |||
| HDT/Af(1.8 MPa;Flatw 80*10*4;sp =64mm) | 192 °C | ISO 75/Af | |||
| Vicat Softening Temperature | |||||
| Rate A/50 | 215 °C | ISO 306 | |||
| Rate B/50 | 211 °C | ISO 306 | |||
| Rate B/120 | 212 °C | ISO 306 | |||
| Rate B/50 | 211 °C | ASTM D1525 | |||
| CTE, Flow | |||||
| -20°C to 150°C | 5.2E-05 1/°C | ISO 11359-2 | |||
| -20°C to 150°C | 5.6E-05 1/°C | ASTM E831 | |||
| CTE, XFlow | |||||
| -20°C to 150°C | 5.2E-05 1/°C | ISO 11359-2 | |||
| -20°C to 150°C | 5.4E-05 1/°C | ASTM E831 | |||
| Ball Pressure Test(125°C +/- 2°C) | Pass | IEC 60695-10-2 | |||
| Thermal Conductivity | 0.22 W/m-K | ISO 8302 | |||
| 0.22 W/m-K | ASTM C177 | ||||
| Heat Deflection Temperature[HDT], Unannealed 0.45 MPa;6.4 mm 1.82 MPa;6.4 mm 0.45 MPa;3.2 mm 3.2 mm;1.82 MPa |
210 °C 201 °C 207 °C 190 °C |
ASTM D648 | |||
| Electrical | Nominal Value | Test Method | |||
| Volume Resistivity | |||||
| 1.0e+15 ohms ·cm | IEC 60093 | ||||
| 1.0e+17 ohms ·cm | ASTM D257 | ||||
| Surface Resistivity, ROA | > 1.E+15 Ohms | IEC 60093 | |||
| Dielectric Strength, in Oil | |||||
| 0.8 mm | 33 kV/mm | IEC 60243-1 | |||
| 1.6 mm | 25 kV/mm | IEC 60243-1 | |||
| 3.2 mm | 16 kV/mm | IEC 60243-1 | |||
| 1.6 mm | 28 kV/mm | ASTM D149 | |||
| 3.2 mm | 19.7 kV/mm | ASTM D149 | |||
| Relative Permittivity | |||||
| 1.0e+6 Hz | 2.9 | IEC 60250 | |||
| 50/60 Hz | 2.9 | IEC 60250 | |||
| 100 Hz | 3.15 | ASTM D150 | |||
| 1.0e+3 Hz | 3.15 | ASTM D150 | |||
| Dissipation Factor | |||||
| 1.0e+6 Hz | 6.0E-03 | IEC 60250 | |||
| 50/60 Hz | 5.0E-04 | IEC 60250 | |||
| 1.1e+9 Hz | 1.2E-03 | ||||
| 5.0e+9 Hz | 2.4E-03 | ||||
| 1.0e+10 Hz | 2.7E-03 | ||||
| 100 Hz | 1.5E-03 | ASTM D150 | |||
| 1.0e+3 Hz | 1.2E-03 | ASTM D150 | |||
| Dielectric Constant | |||||
| 1.1e+9 Hz | 3.01 | ||||
| 5.0e+9 Hz | 3.02 | ||||
| 1.0e+10 Hz | 3.02 | ||||
| Comparative Tracking Index | 150 V | IEC 60112 | |||
| Comparative tracking index M | 100 V | IEC 60112 | |||
| Dielectric Strength, in Air(1.6 mm) | 32.7 kV/mm | ASTM D149 | |||
| Processing | Nominal Value | ||||
| Drying Temperature | 150 ºC | ||||
| Drying Time | 4 - 6 hr | ||||
| Drying Time, Cumulative | 24 hr | ||||
| Maximum Moisture Content | 0.02 % | ||||
| Melt Temperature | 350 - 400 ºC | ||||
| Nozzle Temperature | 345 - 400 ºC | ||||
| Front - Zone 3 Temperature | 345 - 400 ºC | ||||
| Middle - Zone 2 Temperature | 340 - 400 ºC | ||||
| Rear - Zone 1 Temperature | 330 - 400 ºC | ||||
| Mold Temperature | 135 - 165 ºC | ||||
| Back Pressure | 0.3 - 0.7 MPa | ||||
| Screw Speed | 40 -70 rpm | ||||
| Shot to Cylinder Size | 40 - 60 % | ||||
| Vent Depth | 0.025 - 0.076 mm | ||||
Dongguan FOREVER Co., Ltd. Was founded in 2005 and is a national high-tech enterprise and national-level specialized giant enterprise dedicated to the research and production of polymer composite modified materials. With an annual capacity of 100, 000 tons of modified engineering plastics. Since its establishment, the company has been committed to the research of high-performance composite materials such as modified PC, PC/ABS, PBT, PA6, etc. Its products have been widely used in industries such as LED lighting, consumer electronics, new energy, security equipment, and small household appliances, providing customers with efficient delivery experience, ultimate price advantages, and strict quality assurance, contributing to the creation of a green and environmentally friendly world.
Dongguan FOREVER Co., Ltd's main products has obtained UL certification for RTI authorized temperature, outdoor weather resistance F1 and 5VA flame retardancy grades, as well as recycled-certified post-consumer low-carbon circulation products. Dongguan FOREVER Co., Ltd's products are highly recognized by customers worldwide for their reliable quality, excellent performance, and superior cost-effectiveness.
With a strong focus on research and development, Dongguan FOREVER Co., Ltd. Has established an advanced technology research and development center, equipped with state-of-the-art testing and analysis equipment and a professional R&D team that has accumulated rich experience in the field of polymer composite modified materials. Dongguan FOREVER Co., Ltd also maintains close partnerships with renowned universities and research institutions to stay at the forefront of technology and drive innovation in the industry
Suppliers with verified business licenses
Audited Supplier 
){kind=link}
){kind=link}