The Material Is Available in a Wide Range of Dark and Light Colors

• Feature: Plastics
• CAS No.: 25766-59-0
• Formula: C6h4c(CH3)2c6h4oco2-]N
• Shipping Cost: Estimated freight per unit.: about shipping cost and estimated delivery time.
• Currency: US$
• Return&refunds: You can apply for a refund up to 30 days after receipt of the products.
• Model NO.: PC-D3000IEU6
• EINECS: 618-371-8
• Material: Polycarbonates/PC
• Usage: General Plastics, Engineering Plastics, Specialty Plastics
• Plastic Properties After Heated: Thermoplastic Plastics
• Plastic Forming Method: Injection
• Color: Natural Color
• Place of Origin: Guangdong, China
• Use: Radiator Front Cover.Automotive Parts
• Features: Lubricated, Good Wear Resistance, Low Friction and
• Application: Zippers Irish Flutes, Bagpipes, Practice Chanters
• Form: Resin Pellets
• Delivery Time: in 7 Days
• Applications: Appliance Handles, Spotlights, Electric Motors.
• Glass Fiber: 0%-50%
• Gr: 0%
• Transport Package: Bag
• Specification: 25KG
• Trademark: Forever
• Origin: China
• HS Code: 390740000
• Production Capacity: 50000t/Year
• Package Size: 75.00cm * 55.00cm * 15.00cm
• Package Gross Weight: 25.010kg

Product Description

The material is available in a wide range of dark and light colors
 
 

Uses	Automotive   Electrical	Consumer                         Industria   Hydrocarbon and Energy
Physical		Nominal Value		Test Method
Density / Specific Gravity		1.16 g/cm³ 1.16		ISO 1183 ASTM D792
Moisture Absorption				ISO 62-4
23 °C;50% RH/24hrs		0.15 %
23 °C;50% RH/Equilibrium		0.3 %
Water Absorption
24 hrs;23 °C		0.7 %		ISO 62-1
23 °C;saturated		3.5 %		ISO 62-1
24 hrs;23 °C		0.7 %		ASTM D570
23°C/Saturated		3.5 %		ASTM D570
Melt Volume Rate, MVR				ISO 1133
2.16 kg;MVR at 250 °C		5 cm³/10 min
5 kg;MVR at 250 °C		15 cm³/10 min
5 kg;MVR at 260 °C		23 cm³/10 min
Melt Flow Rate[MFR](250 °C;5 kgf)		15 g/10min		ASTM D1238
Mold Shrinkage, Flow		0.5 - 0.7 %		Method
Mold Shrinkage, XFlow		0.6 - 0.8 %		Method
Mechanical			Nominal Value	Test Method
Izod Impact, Notched 80*10*4;23 °C 80*10*4;-30 °C 23 °C -30 °C			60 kJ/m² 60 kJ/m² 850 J/m 750 J/m	ISO 180/1A ISO 180/1A ASTM D256 ASTM D256
Notched Izod Impact Strength notched;80*10*3;23 °C 0 notched;80*10*3;-30 °C 0			65 kJ/m² 65 kJ/m²	ISO 180/1A
Unnotched Izod Impact Strength unnotched;80*10*3;23 °C 0 unnotched;80*10*3;-30 °C 0			NB kJ/m² NB kJ/m²	ISO 180/1U
Izod Impact, Unnotched 80*10*4;23 °C 80*10*4;-30 °C 23 °C -30 °C			NB kJ/m² NB kJ/m² NB J/m NB J/m	ISO 180/1U ISO 180/1U ASTM D4812 ASTM D4812
C harpy Impact, V-Notched 23 °C;Edgew;80*10*4;sp =62 mm 0 -30 °C;Edgew;80*10*4;sp =62 mm 0			60 kJ/m² 60 kJ/m²	ISO 179 1eA
C harpy Impact, Unnotched 23 °C;Edgew;80*10*4;sp =62 mm 0 -30 °C;Edgew;80*10*4;sp =62 mm 0			NB kJ/m² NB kJ/m²	ISO 179 1eU
Multi-Axial Instrumented Impact, Total Energy 23 °C -30 °C			65 J 65 J	ISO 6603-2
Multi-Axial Instrumented Impact, Peak Energy 23 °C -30 °C			55 J 55 J	ISO 6603-2
Instrumented Dart Impact, Total Energy 23 °C -30 °C			40 J 40 J	ASTM D3763
Instrumented Dart Impact, Energy at Peak 23 °C -30 °C			35 J 35 J	ASTM D3763
Instrumented Dart Impact, Peak force 23 °C -30 °C			4000 N 4800 N	ASTM D3763
Tensile Modulus
1 mm/min			1750 MPa	ISO 527
50 mm/min			1750 MPa	ASTM D638
Tensile Stress, Yield
50 mm/min			45 MPa	ISO 527
50 mm/min;Type I			45 MPa	ASTM D638
Tensile Strain, Yield
50 mm/min			5.5 %	ISO 527
50 mm/min;Type I			5.5 %	ASTM D638
Tensile Strain, Break
50 mm/min			> 60 %	ISO 527
50 mm/min;Type I			> 60 %	ASTM D638
Tensile Nominal Strain, Break
50 mm/min			> 60 %	ISO 527
50 mm/min;Type I			> 60 %	ASTM D638
Flexural Modulus
2 mm/min			1825 MPa	ISO 178
1.3 mm/min;50 mm;span			1900 MPa	ASTM D790
Flexural Strength
2 mm/min			70 MPa	ISO 178
1.3 mm/min;50 mm;span			70 MPa	ASTM D790
Ball Indentation Hardness(H358/30)			78 MPa	ISO 2039-1
Thermal			Nominal Value	Test Method
HDT/Af(1.8)			105 °C	ISO 75/Af
HDT/Bf(0.45)			123 °C	ISO 75/Bf
Vicat Softening Temperature
Rate B/50			123 °C	ISO 306
Rate B/120			123 °C	ISO 306
Rate A/50			137 °C	ISO 306
Rate A/120			138 °C	ISO 306
Rate B/50			123 °C	ASTM D1525
Rate B/120			123 °C	ASTM D1525
CTE, Flow
23°C to 50°C			8.5E-05 1/°C	ISO 11359-2
23°C to 50°C			8.5E-05 1/°C	ASTM E831
CTE, XFlow
23°C to 50°C			1.1E-04 1/°C	ISO 11359-2
23°C to 50°C			1.1E-04 1/°C	ASTM E831
Heat Deflection Temperature[HDT], Unannealed 3.2 mm;1.82 MPa 0.45 MPa;3.2 mm			105 °C 123 °C	ASTM D648
Ball Pressure Test(125°C +/- 2°C)			Pass	IEC 60695-10-2
Electrical			Nominal Value	Test Method
Comparative Tracking Index			175 V	IEC 60112
Surface Resistivity, ROA			1.0E+09 - 1.0E+11 ohms	IEC 60093
Static Decay(5000V to <50V)			< 0.01 Seconds	FTMS101B
Dielectric Constant(6.0e+10 - 9.0e+10 Hz)			2.73
Dissipation Factor(6.0e+10 - 9.0e+10 Hz)			0.022
Surface Resistivity			1.0E+09 - 1.0E+11 ohms	ASTM D257

        

 

Company Profile

Product Parameters

Our Customers

Our Certificates

 

Our Production

Our Package/Shipping

Our Advantages

 

Our Samples

 

Dongguan FOREVER Co., Ltd. Was founded in 2005 and is a national high-tech enterprise and national-level specialized giant enterprise dedicated to the research and production of polymer composite modified materials. With an annual capacity of 100, 000 tons of modified engineering plastics. Since its establishment, the company has been committed to the research of high-performance composite materials such as modified PC, PC/ABS, PBT, PA6, etc. Its products have been widely used in industries such as LED lighting, consumer electronics, new energy, security equipment, and small household appliances, providing customers with efficient delivery experience, ultimate price advantages, and strict quality assurance, contributing to the creation of a green and environmentally friendly world.

Dongguan FOREVER Co., Ltd's main products has obtained UL certification for RTI authorized temperature, outdoor weather resistance F1 and 5VA flame retardancy grades, as well as recycled-certified post-consumer low-carbon circulation products. Dongguan FOREVER Co., Ltd's products are highly recognized by customers worldwide for their reliable quality, excellent performance, and superior cost-effectiveness.

With a strong focus on research and development, Dongguan FOREVER Co., Ltd. Has established an advanced technology research and development center, equipped with state-of-the-art testing and analysis equipment and a professional R&D team that has accumulated rich experience in the field of polymer composite modified materials. Dongguan FOREVER Co., Ltd also maintains close partnerships with renowned universities and research institutions to stay at the forefront of technology and drive innovation in the industry