Product Description | |||||
33 % glass reinforced, impact modified. Connectors, etc. | |||||
General | |||||
Form | Resin | Pellets | |||
Filler | 33 % | Glass Fiber | |||
UL Yellow Card E207780-100140794 | |||||
Appliances Automotive Under The Electronic Displays | |||||
Uses | oo | Automotive Exterior | |||
Connector | Electrical | Medical | |||
Physical | Nominal Value | Test Method | |||
Density / Specific Gravity | 1.52 g/cm³ | ASTM D792 | |||
Specific Volume | 0.650 cm³/g | ASTM D792 | |||
Melt Mass-Flow Rate, MFR(250 °C;2.16 kg) | 12 g/10min | ASTM D1238 | |||
Molding Shrinkage, Across Flow | Internal Method | ||||
1.5 - 3.2 mm | 0.40 - 0.60 % | ||||
3.2 - 4.6 mm | 0.60 - 0.90 % | ||||
Molding Shrinkage, Flow | |||||
1.5 - 3.2 mm | 0.30 - 0.50 % | Internal Method | |||
3.2 mm | 0.50 % | Internal Method | |||
3.2 - 4.6 mm | 0.50 - 0.80 % | ASTM D792;ISO | |||
1183 | |||||
Water Absorption(24 hr) | 0.050 % | ASTM D570 | |||
Rockwell Hardness, R-Scale | 125 | ASTM D785 | |||
Mechanical | Nominal Value | Test Method | |||
Tensile Modulus(5 mm/min) | 8660 MPa | ASTM D638 | |||
Tensile Strength, Break(5 mm/min;Type I) | 106 MPa | ASTM D638 | |||
Tensile Elongation, Break(5 mm/min;Type I) | 3.1 % | ASTM D638 | |||
Flexural Modulus(1.3 mm/min;50 mm;Span) | 7810 MPa | ASTM D790 | |||
Flexural Strength, Break(1.3 mm/min;50 mm;Span) | 174 MPa | ASTM D790 | |||
Notched Izod Impact(23 °C) | 130 J/m | ASTM D256 | |||
Unnotched Izod Impact(23 °C) | 860 J/m | ASTM D4812 |
Thermal | Nominal Value | Test Method |
Deflection Temperature Under Load, Unannealed 0.45 MPa;6.4 mm 1.8 MPa;6.4 mm |
223 °C 208 °C |
ASTM D648 |
RTI Elec | 130 °C | UL 746 |
RTI Imp | 130 °C | UL 746 |
RTI Str | 140 °C | UL 746 |
Flame Rating(1.5 mm) | HB | UL 94 |
Electrical | Nominal Value | Test Method |
Arc Resistance, Tungsten Electrode | PLC5 | ASTM D495 |
Comparative Tracking Index, CTI | PLC 1 | UL 746 |
High Amp Arc Ignition, HAI, Surface | PLC 2 | UL 746 |
High Voltage Arc Tracking Rate, HVTR | PLC 0 | UL 746 |
Hot-wire Ignition, HWI | PLC 0 | UL 746 |
Processing | Nominal Value | |
Drying Temperature<Injection> | 120 °C | |
Drying Time<Injection> | 3.0 - 4.0 hr | |
Suggested Max Moisture<Injection> | 0.020 % | |
Suggested Shot Size<Injection> | 40 - 80 % | |
Rear Temperature<Injection> | 240 - 255 °C | |
Middle Temperature<injection> | 245 - 260 °C | |
Front Temperature<Injection> | 250 - 265 °C | |
Nozzle Temperature<Injection> | 245 - 260 °C | |
Processing Temp, Melt<Injection> | 250 - 265 °C | |
Mold Temperature<Injection> | 65 - 90 °C | |
Back Pressure<Injection> | 0.300 - 0.700 MPa | |
Screw Speed <Injection> | 50 - 80 rpm | |
Vent Depth <Injection> | 0.025 - 0.038 mm | |
Injection, Drying Time, Cumulative<Injection> | 12 hrs |