Engineering Compounding PA66 GF30 GF15 Resin PA6 GF30 Plastic Granules Price$2.00-$2.50

• Feature: Oxidative Degradable
• Material: Polyamide(Nylon 6.66)/PA
• Usage: General Plastics, Engineering Plastics, Specialty Plastics
• Shipping Cost: Estimated freight per unit.: about shipping cost and estimated delivery time.
• Currency: US$
• Return&refunds: You can apply for a refund up to 30 days after receipt of the products.
• Model NO.: P10323V
• Plastic Properties After Heated: Thermoplastic Plastics
• Plastic Forming Method: Injection
• Color: White
• Form: Resin Pellets
• Chemical Substances: Nylon
• Processing Mode: Injection Molding/Extrusion
• UV: Fr
• Use: Electrical Appliances, Auto Parts, Office Supplies
• Certificates: ISO9001:2008.SGS.RoHS
• Filler: 30% Glass Fiber
• Transport Package: Bag
• Specification: 25KG
• Trademark: Forever
• Origin: China
• HS Code: 390740000
• Production Capacity: 50000t/Year

Product Description

engineered glass filled nylon pa gf 10 pa66 gf pa6 30% 25% 40%manufacturerreinforced glassfiber reinforced grade 

LNP KONDUIT PX10323 compound is based on Nylon 6 resin containing glass fiber and proprietary thermal filler. Added features of this grade include: Thermally Conductive.

 

Product Description
LNP KONDUIT PX10323 compound is based on Nylon 6 resin containing glass fiber and proprietary thermal filler. Added features of this grade include: Thermally Conductive.
General
Form	Resin Pellets
Filler	Glass Fiber
Feature                                     Electrically Conductive     Thermally Conductive
Consumer                         Industria   Building and Construction			Electrical
Physical	Nominal Value		Test Method
Density	1.61 g/cm³		ASTM D792
Mold Shrinkage, Flow(24 hrs)		0.2 %	ASTM D955
Mold Shrinkage, XFlow(24 hrs)		0.22 %	ASTM D955
Moisture Absorption(50% RH;23 °C)		0.04 %	ISO 62

Mechanical	Nominal Value	Test Method
Izod Impact, Unnotched 23 °C 80*10*4;23 °C	73 J/m 6 kJ/m²	ASTM D4812 ISO 180/1U
Izod Impact, Notched 23 °C 80*10*4;23 °C	30 J/m 3 kJ/m²	ASTM D256 ISO 180/1A
Tensile Stress, Break 5 mm/min;Type I 5 mm/min	70 MPa 73 MPa	ASTM D638 ISO 527
Tensile Strain, Break 5 mm/min;Type I 5 mm/min	0.9 % 0.8 %	ASTM D638 ISO 527
Tensile Modulus 5 mm/min 1 mm/min	1.4E+04 MPa 1.4E+04 MPa	ASTM D638 ISO 527
Flexural Stress, Yield(1.3 mm/min;50 mm;span)	96 MPa	ASTM D790
Flexural Stress, break 1.3 mm/min;50 mm;span 2 mm/min	95 MPa 96 MPa	ASTM D790 ISO 178
Flexural Modulus 1.3 mm/min;50 mm;span 2 mm/min	1.4E+04 MPa 1.4E+04 MPa	ASTM D790 ISO 178
Impact Strength	3.7 - 6.8 kJ/m²	ISO R179

.

Thermal	Nominal Value	Test Method
Glow Wire Flammability Index 1 mm 1.6 mm	850 °C 960 °C	IEC 60695-2-12
Glow Wire Ignition Temperature [GWIT](1 mm)	825 °C	IEC 60695-2-13
Heat Deflection Temperature[HDT], Unannealed(1.82 MPa;6.4 mm)	204 °C	ASTM D648
CTE, Flow(40°C to 120°C)	1.2E-05 1/°C	ASTM E831
CTE, XFlow(40°C to 120°C)	7.3e-05 1/°C	ASTM E831
Thermal conductivity through plane 60*60*3mm plaque 10*10*3mm sample	1.5 W/m-K 3.5 W/m-K	ISO 22007-2 ASTM E1461-07
Thermal conductivity in plane 60*60*3mm plaque 25*0.4mm disc	18 W/m-K 15 W/m-K	ISO 22007-2 ASTM E1461-07
HDT/Bf(0.45)	217 °C	ISO 75/Bf
HDT/Af(1.8)	201 °C	ISO 75/Af
Electrical	Nominal Value	Test Method
Surface Resistivity	1.0E+06 ohms	ASTM D257
Processing		Nominal Value
Drying Temperature<Injection>		80 °C
Drying Time<Injection>		4 hrs
Maximum Moisture Content<Injection>		0.15 - 0.25 %
Melt Temperature<Injection>		270 - 295 °C
Front, Zone 3 Temperature<Injection>		270 - 290 °C
Middle, Zone 2 Temperature<Injection>		270 - 290 °C
Rear, Zone 1 Temperature<Injection>		260 - 275 °C
Mold Temperature<Injection>		85 - 100 °C
Back Pressure<Injection>		0.2 - 0.3 MPa
Screw Speed<Injection>		20 - 60 rpm

 

 

 
    

                                                                                                                  Forever Co.,Ltd

With almost 20 years in the modified engineering plastics,Forever Plastics is a high-tech manufacture integrating R&D, production and sales of high-performance resin or polymer ,including PC,PP,PA6,PA66, PBT,PET, PC/ABS, PC/PBT, PC/PET alloy compounds,TPE,TPU, PE for rotomolding with the property of the flame retardant, glass fiber reinforced, high glossy, UV resistance.....with the annual output value of USD 65 million in 2021. 

Our customers are Osram,Cree,,Siemens,etc. for years in the electrical&electronics components, Automotive parts, House appliance,LED lights.....