Polyphthalamide (PPA) Resin Designed to Possess 15% Glass-Fiber Reinforced Grades

• Feature: Oxidative Degradable
• CAS No.: 32131-17-2
• Formula: (C12h22n2o2)N
• Shipping Cost: Estimated freight per unit.: about shipping cost and estimated delivery time.
• Currency: US$
• Return&refunds: You can apply for a refund up to 30 days after receipt of the products.
• Model NO.: PPA-AT-6115 HS
• EINECS: 211-024-8
• Material: Polyamide(Nylon 6.66)/PA
• Usage: General Plastics, Engineering Plastics, Specialty Plastics
• Plastic Properties After Heated: Thermoplastic Plastics
• Plastic Forming Method: Injection
• Color: Black
• Form: Resin Pellets
• Chemical Substances: Nylon
• Processing Mode: Injection Molding/Extrusion
• UV: Fr
• Use: Electrical Appliances, Auto Parts, Office Supplies
• Certificates: ISO9001:2008.SGS.RoHS
• Filler: 10%-60% Glass Fiber
• Transport Package: Bag
• Specification: 25KG
• Trademark: Forever
• Origin: China
• HS Code: 390740000
• Production Capacity: 50000t/Year
• Package Size: 75.00cm * 55.00cm * 15.00cm
• Package Gross Weight: 25.010kg

Product Description

polyphthalamide (PPA) resin designed to possess  15% glass-fiber reinforced grades 
 Heat-conducting nylon

Product Description

AT-6115 HS is a 15% glass-fiber reinforced, toughened grade of polyphthalamide (PPA) resin designed to possess more elongation than other 15% glass-fiber reinforced grades of Amodel resin. This grade was developed for automotive snap-fit electronic connectors. It offers high flow and short molding cycles. Black: AT- 6115 HS BK 324 Natural: AT-6115 HS NT
General
Form	Resin Pellets
Filler		15 % Glass Fiber
Feature		Excellent Processability    Good Thermal    Internally Lubricated         High Elongation		High Impact
UL Yellow Card	E95746-458902
Uses   Metal Replacement			Hood   Automotive	Industrial Parts   Connector
Housing			Valves/Valve Parts	Mechanical Parts
Physical			Nominal Value	Test Method
Density, dry			1.22 g/cm³	ISO 1183/A
Dry: Molding Shrinkage, Flow			1.0 %	ASTM D955
Dry: Molding Shrinkage, Across Flow			1.1 %	ASTM D955
Dry: Water Absorption(24 hr)			0.20 %	ASTM D570
Mechanical			Nominal Value	Test Method
Dry: Tensile Modulus
			5380 MPa	ASTM D638
23 °C			5200 MPa	ISO 527-2
100 °C			3100 MPa	ISO 527-2
Condition: Tensile Modulus			4200 MPa	ASTM D638
Dry: Tensile Stress, Break				ISO 527-2
23 °C			126 MPa
100 °C			68.3 MPa
Dry: Tensile Stress			122 MPa	ASTM D638
Condition: Tensile Stress			95.8 MPa	ASTM D638
Dry: Tensile Elongation, Break			3.4 %	ASTM D638
23 °C			4.1 %	ISO 527-2
100 °C			7.7 %	ISO 527-2
Condition: Tensile Elongation, Break			5.3 %	ASTM D638
Dry: Flexural Modulus			4410 MPa	ASTM D790
23 °C			4270 MPa	ISO 178
100 °C			2340 MPa	ISO 178
Condition: Flexural Modulus			3450 MPa	ASTM D790
Dry: Flexural Strength			165 MPa	ASTM D790
23 °C			170 MPa	ISO 178
100 °C			66.9 MPa	ISO 178
Condition: Flexural Strength			115 MPa	ASTM D790
Dry: Compressive Strength			100 MPa	ASTM D695
Dry: Shear Strength			56.5 MPa	ASTM D732
Condition: Shear Strength			44.1 MPa	ASTM D732
Dry: Charpy Notched Impact Strength(23 °C)			11 kJ/m²	ISO 179 1eA
Dry: Charpy Unnotched Impact Strength(23 °C)			76 kJ/m²	ISO 179 1eU
Dry: Notched Izod Impact			91 J/m	ASTM D256
23 °C			12 kJ/m²	ISO 180/1A
Izod Notched Impact: condition			80 J/m	ASTM D256
Dry: Unnotched Izod Impact			850 J/m	ASTM D256
23 °C			55 kJ/m²	ISO 180/1U
Thermal			Nominal Value	Test Method
Dry: Heat Deflection Temperature, Unannealed 0.45 MPa 1.8 MPa			298 °C 251 °C	ISO 75-2/B ISO 75-2/A
Dry: Heat Deflection Temperature, Annealed(1.8 MPa)			260 °C	ASTM D648
Dry: Melting Temperature			305 °C	ASTM D3418;  ISO 11357-3
Dry: CLTE, Flow 0 - 100 °C 100 - 200 °C			2.2E-5 cm/cm/°C 3.0E-5 cm/cm/°C	ASTM E831
Dry: CLTE, Transverse 0 - 100 °C 100 - 200 °C			9.0E-5 cm/cm/°C 1.2E-4 cm/cm/°C	ASTM E831
Processing				Nominal Value
Drying Temperature<Injection>				110 °C
Drying Time<Injection>				4.0 hr
Suggested Max Moisture<Injection>				0.030 - 0.060 %
Rear Temperature<Injection>				316 - 324 °C
Front Temperature<Injection>				327 - 332 °C
Processing Temp, Melt<Injection>				321 - 335 °C
Mold Temperature<Injection>				66 - 93 °C
Injection Rate<Injection>				2 - 4 in/sec
Holding Pressure<Injection>				50 of injection pressure %

 

                                                                                                                  Forever Co.,Ltd

 

With almost 20 years in the modified engineering plastics,Forever Plastics is a high-tech manufacture integrating R&D, production and sales of high-performance resin or polymer ,including PC,PP,PA6,PA66, PBT,PET, PC/ABS, PC/PBT, PC/PET alloy compounds,TPE,TPU, PE for rotomolding with the property of the flame retardant, glass fiber reinforced, high glossy, UV resistance.....with the annual output value of USD 65 million in 2021. 

Our customers are Osram,Cree,,Siemens,etc. for years in the electrical&electronics components, Automotive parts, House appliance,LED lights.....