nylon resin PA6 carbon fibre Reinforced Pellets Polyamide Black PA6/ PA66 Nylon Granuleshttps://forever-plastics.en.made-in-china.com/product/rJwRvlcdZpWD/China-Nylon-PA6-GF33-PA66-Granules-PA6-with-30GF-Polyamide-PA66-30-GF-PA6-Material.html
30% Glass Reinforced, Heat Stabilized, Flame Retardant
Product Description | |||
30% Glass Reinforced, Food Contact Grade | |||
General | |||
Form | Resin Pellets | ||
Filler | 30 % Glass Fiber | ||
Feature | Fda | ||
Physical | Nominal Value | Test Method | |
Dry: Density | 1.35 g/cm³ | ISO 1183 | |
Dry: Molding Shrinkage, Across Flow | 0.90 % | ISO 294-4 | |
Dry: Molding Shrinkage, Flow | 0.30 % | ISO 294-4 | |
Dry: Water Absorption, Saturation(23 °C) | 6.3 % | ISO 62 | |
Dry: Water Absorption, Equilibrium(50% RH;23 °C) | 1.9 % | ISO 62 | |
Mechanical | Nominal Value | Test Method | |
Dry: Tensile Modulus | 9500 MPa | ISO 527-2 | |
Condition: Tensile Modulus | 6000 MPa | ISO 527-2 | |
Dry: Tensile Stress, Break | 180 MPa | ISO 527-2 | |
Condition: Tensile Stress, Break | 110 MPa | ISO 527-2 | |
Dry: Tensile Strain, Break | 3.5 % | ISO 527-2 | |
Condition: Tensile Strain, Break | 7.0 % | ISO 527-2 | |
Dry: Flexural Modulus | 8600 MPa | ISO 178 | |
Dry: Flexural Stress | 235 MPa | ISO 178 | |
Dry: Charpy Notched Impact Strength | ISO 179 1eA | ||
-30 °C | 11 kJ/m² | ||
23 °C | 12 kJ/m² | ||
Condition: Charpy Notched Impact Strength | ISO 179 1eA | ||
-30 °C | 11 kJ/m² | ||
23 °C | 25 kJ/m² | ||
Dry: Charpy Unnotched Impact Strength | ISO 179 1eU | ||
-30 °C | 75 kJ/m² | ||
23 °C | 90 kJ/m² | ||
Condition: Charpy Unnotched Impact Strength | ISO 179 1eU | ||
-30 °C | 75 kJ/m² | ||
23 °C | 110 kJ/m² |
Thermal | Nominal Value | Test Method |
Dry: Heat Deflection Temperature, Unannealed 0.45 MPa 1.8 MPa |
220 °C 200 °C |
ISO 75-2/B ISO 75-2/A |
Dry: Melting Temperature(10 °C/min) | 220 °C | ISO 11357-3 |
Dry: CLTE, Flow | 2.0E-5 cm/cm/°C | ISO 11359-2 |
Dry: CLTE, Transverse | 7.0E-5 cm/cm/°C | ISO 11359-2 |
Electrical | Nominal Value | Test Method |
Condition: Surface resistivity | 1.0E+14 ohms | IEC 60093 |
Dry: Volume Resistivity | 1.0e+15 ohms·cm | IEC 60093 |
Condition: Volume resistivity | 1.0E+13 ohms·cm | IEC 60093 |
Dry: Electric Strength | 30 kV/mm | IEC 60243-1 |
Condition: Electric Strength | 25 kV/mm | IEC 60243-1 |
Dry: Relative permittivity 100 Hz 1000000 Hz |
3.50 3.30 |
IEC 60250 |
Condition: Relative Permittivity 100 Hz 1000000 Hz |
20.0 5.00 |
IEC 60250 |
Dry: Dissipation Factor 100 Hz 1000000 Hz |
5.0E-3 0.015 |
IEC 60250 |
Condition: Dissipation factor 100 Hz 1000000 Hz |
0.30 0.12 |
IEC 60250 |
Condition: Comparative Tracking Index | 600 V | IEC 60112 |