Audited Supplier PA6 combined with enhanced processing behavior suitable for thinwall parts
https://forever-plastics.en.made-in-china.com/product/rJwRvlcdZpWD/China-Nylon-PA6-GF33-PA66-Granules-PA6-with-30GF-Polyamide-PA66-30-GF-PA6-Material.html Heat-conducting nylon
| Product Description | |||||
| TECHNYL PROTECT C 52G4 MZ25 GY R7035 is a polyamide 6 based on a non-phosphorous and Non- halogenated flame retardant system, reinforced with 25% of mineral filler, heat stabilized, for injection moulding. This grade offers a robust glow wire resistance, combined with enhanced processing behavior suitable for thin wall parts. |
|||||
| General | |||||
| Form | Resin Pellets | ||||
| Filler | 25 % Mineral | ||||
Feature |
Arc Resistant Laser Markable |
Ec 1907/2006 (Reach) En 45545 |
Non-Brominated & Non- Chlorinated Flame Retardant |
||
| Uses | Electrical | ||||
| Physical | Nominal Value | Test Method | |||
| Density / Specific | Gravity | 1.37 g/cm³ | ISO 1183 | ||
| Water Absorption | (24 hr;23 °C) | 1 % | ISO 62 | ||
| Water Absorption | at Saturation(24 hr;23 °C) | 6 % | ISO 62 | ||
| Mechanical | Nominal Value | Test Method | |||
| Dry: Tensile Modulus(1 mm/min) | 6900 MPa | ISO 527-1/-2 | |||
| Condition: Tensile Modulus(1 mm/min) | 2400 MPa | ISO 527-1/-2 | |||
| Dry: Stress at break | 75 MPa | ISO 527-1/-2 | |||
| Condition: Stress at break | 35 MPa | ISO 527-1/-2 | |||
| Strain at break | 3 % | ISO 527-1/-2 | |||
| Dry: Flexural Modulus(2 mm/min) | 6300 MPa | ISO 178 | |||
| Condition: Flexural Modulus(2 mm/min) | 2500 MPa | ISO 178 | |||
| Flexural Modulus(2 mm/min) | 6000 MPa | ASTM D790 | |||
| Dry: Flexural Strength(2 mm/min) | 125 MPa | ISO 178 | |||
| Condition: Flexural Strength(2 mm/min) | 50 MPa | ISO 178 | |||
| Flexural Strength(2 mm/min) | 120 MPa | ASTM D790 | |||
| Dry: Charpy Impact Strength(23 °C) | 35 kJ/m² | ISO 179/1eU | |||
| Condition: Charpy Impact Strength(23 °C) | 80 kJ/m² | ISO 179/1eU | |||
| C harpy Impact Strength, Unnotched(- 30 °C) | 45 kJ/m² | ISO 179/1eU | |||
| Dry: Charpy Notched Impact Strength(23 °C) | 3 kJ/m² | ISO 179/1eA | |||
| Condition: Charpy Notched Impact Strength(23 °C) | 4.5 kJ/m² | ISO 179/1eA | |||
| C harpy Notched Impact Strength(- 30 °C) | 2.5 kJ/m² | ISO 179/1eA | |||
| Notched Izod Impact Strength(23 °C) | 2 kJ/m² | ISO 180/1A | |||
| Thermal | Nominal Value | Test Method | |||
| Melting Temperature(10 °C/min) | 222 °C | ISO 11357-1 | |||
| Temp. of deflection under load 0.45 MPa 1.8 MPa |
200 °C 130 °C |
ISO 75 | |||
| Flammability 0.75 mm 1.5 mm 3 mm |
V-2 V-2 V-2 |
UL 94 | |||
| Electrical | Nominal Value | Test Method | |||
| Comparative Tracking Index(Solution A) | 525 V | IEC 60112 | |||
| Dielectric Strength(1 mm) | 35 kV/mm | IEC 60243-1 | |||
| Processing | Nominal Value | ||||
| Drying Temperature | 80 °C | ||||
| Dry Time(with a dehumidified air drying equipment, dew point mini -20°C) |
2 - 4 h | ||||
| Suggested Max Moisture | 0.002 | ||||
| Rear Temperature | 230 - 235 °C | ||||
| Middle Temperature | 235 - 240 °C | ||||
| Front Temperature | 240 - 250 °C | ||||
| Mold Temperature | 60 - 90 °C | ||||