Product Description | |||||||||
LUX9136C Polycarbonate (PC) resin is a non-filled, injection moldable grade. This non-chlorinated, non- brominated flame retardant PC has an UL-94 V0 rating at 1.5 mm, high flow capability and is UV stabilized providing additional weathering capability. LUX9136C is available in diffusion colors. |
|||||||||
General | |||||||||
Form | Resin Pellets | ||||||||
Feature |
F1 | Excellent Processability Diffusive |
Non-Brominated & Non- Chlorinated Flame Retardant |
||||||
UL Yellow Card | E207780-101088463 | ||||||||
Uses Lighting Diffusers | Electrical | ||||||||
Physical | Nominal Value | Test Method | |||||||
Density / Specific Gravity | 1.19 1.2 g/cm³ |
ASTM D792 ISO 1183 |
|||||||
Mold Shrinkage, Flow(3.2 mm) | 0.55 - 0.75 % | SABIC Method | |||||||
Mold Shrinkage, XFlow(3.2 mm) | 0.6 - 0.8 % | SABIC Method | |||||||
Melt Flow Rate[MFR](300 °C;1.2 kgf) | 18 g/10min | ASTM D1238 | |||||||
Water Absorption(23 °C;saturated) | 0.13 % | ISO 62-1 | |||||||
Moisture Absorption(50% RH;23 °C) | 0.11 % | ISO 62 | |||||||
Melt Volume Rate, MVR(1.2 kg;MVR at 300 °C) | 17 cm³/10 min | ISO 1133 | |||||||
UV light, water exposure/immersion | f1 | UL 746C | |||||||
Mechanical | Nominal Value | Test Method | |||||||
Izod Impact, Unnotched 23 °C -30 °C |
NB J/m NB J/m |
ASTM D4812 | |||||||
Izod Impact, Notched 23 °C -30 °C |
100 J/m 85 J/m |
ASTM D256 | |||||||
Instrumented Dart Impact, Total Energy(23 °C) | 65 J | ASTM D3763 | |||||||
Unnotched Izod Impact Strength unnotched;80*10*3;23 °C 0 unnotched;80*10*3;-30 °C 0 |
NB kJ/m² NB kJ/m² |
ISO 180/1U | |||||||
Notched Izod Impact Strength notched;80*10*3;23 °C 0 notched;80*10*3;-30 °C 0 |
10 kJ/m² 9 kJ/m² |
ISO 180/1A | |||||||
C harpy Impact, V-Notched 23 °C;Edgew;80*10*3;sp =62mm 0 -30 °C;Edgew;80*10*3;sp =62mm 0 |
10 kJ/m² 9 kJ/m² |
ISO 179 1eA | |||||||
C harpy Impact, Unnotched 23 °C;Edgew;80*10*3;sp =62mm 0 -30 °C;Edgew;80*10*3;sp =62mm 0 |
NB kJ/m² NB kJ/m² |
ISO 179 1eU | |||||||
Tensile Stress, Yield | |||||||||
50 mm/min;Type I | 67 MPa | ASTM D638 | |||||||
50 mm/min | 63 MPa | ISO 527 | |||||||
Tensile Stress, Break | |||||||||
50 mm/min;Type I | 54 MPa | ASTM D638 | |||||||
50 mm/min | 57 MPa | ISO 527 | |||||||
Tensile Strain, Yield | |||||||||
50 mm/min;Type I | 6 % | ASTM D638 | |||||||
50 mm/min | 6 % | ISO 527 | |||||||
Tensile Strain, Break | |||||||||
50 mm/min;Type I | 80 % | ASTM D638 | |||||||
50 mm/min | 73 % | ISO 527 | |||||||
Tensile Modulus | |||||||||
50 mm/min | 2400 MPa | ASTM D638 | |||||||
1 mm/min | 2300 MPa | ISO 527 | |||||||
Flexural Stress, Yield | |||||||||
1.3 mm/min;50 mm;span | 103 MPa | ASTM D790 | |||||||
2 mm/min | 96 MPa | ISO 178 | |||||||
Flexural Modulus | |||||||||
1.3 mm/min;50 mm;span | 2400 MPa | ASTM D790 | |||||||
2 mm/min | 2400 MPa | ISO 178 | |||||||
Thermal | Nominal Value | Test Method | |||||||
UL Recognized ≥ 1.5 mm ≥ 0.4 mm |
V-0 V-2 |
UL 94 | |||||||
Glow Wire Ignition Temperature [GWIT] 3 mm 1.5 mm |
850 °C 850 °C |
IEC 60695-2-13 | |||||||
Glow Wire Flammability Index 3 mm 1.5 mm |
960 °C 960 °C |
IEC 60695-2-12 | |||||||
Vicat Softening Temperature Rate B/50 Rate B/50 Rate B/120 |
136 °C 139 °C 140 °C |
ASTM D1525 ISO 306 ISO 306 |
|||||||
Heat Deflection Temperature[HDT], Unannealed 0.45 MPa;3.2 mm 3.2 mm;1.82 MPa |
130 °C 120 °C |
ASTM D648 | |||||||
CTE, Flow -40 - 40 °C 23°C to 80°C |
6.8E-05 1/°C 7.7e-05 1/°C |
ASTM E831 ISO 11359-2 |
|||||||
CTE, XFlow -40 - 40 °C 23°C to 80°C |
7.0E-05 1/°C 8.0e-05 1/°C |
ASTM E831 ISO 11359-2 |
|||||||
Ball Pressure Test(125°C +/- 2°C) | Pass | IEC 60695-10-2 | |||||||
HDT/Be(Edgew;120*10*4;sp =100mm; 0.45 Mpa) | 131 °C | ISO 75/Be | |||||||
Hdt/Ae(1.8 MPa;Edgew;120*10*4;sp =100mm) | 121 °C | ISO 75/Ae | |||||||
Relative Temp Index, Elec | 130 °C | UL 746B | |||||||
Relative Temp Index, Mechanical with Impact | 120 °C | UL 746B | |||||||
Relative Temp Index, Mechanical without Impact | 130 °C | UL 746B | |||||||
Electrical | Nominal Value | Test Method | |||||||
Dielectric Constant, Dk(1.1e+9 Hz) | 2.78 | ASTM ES 7-83 | |||||||
Dissipation Factor, Df(1.1e+9 Hz) | 5.6E-03 | ASTM ES 7-83 | |||||||
Comparative Tracking Index, CTI | PLC 3 | UL 746A | |||||||
Hot-wire Ignition, HWI ≥ 1.5 mm ≥ 0.4 mm |
PLC 0 PLC 3 |
UL 746A | |||||||
High Amp Arc Ignition, HAI( ≥ 0.4 mm) | PLC 1 | UL 746A | |||||||
Processing | Nominal Value | ||||||||
Drying Temperature<Injection> | 120 °C | ||||||||
Drying Time<Injection> | 3 - 4 hrs | ||||||||
Drying Time, Cumulative<Injection> | 48 hrs | ||||||||
Maximum Moisture Content<Injection> | 0.02 % | ||||||||
Melt Temperature<Injection> | 280 - 305 °C | ||||||||
Nozzle Temperature<Injection> | 275 - 300 °C | ||||||||
Front, Zone 3 Temperature<Injection> | 280 - 305 °C | ||||||||
Middle, Zone 2 Temperature<Injection> | 270 - 295 °C | ||||||||
Rear, Zone 1 Temperature<Injection> | 260 - 280 °C | ||||||||
Mold Temperature<Injection> | 70 - 95 °C | ||||||||
Back Pressure<Injection> | 0.3 - 0.7 MPa | ||||||||
Screw Speed <Injection> | 40 - 70 rpm | ||||||||
Shot To Cylinder Size<Injection> | 40 - 60 % | ||||||||
Vent Depth <Injection> | 0.025 - 0.076 mm |