Product Description | |||||
XHT4143 is a high flow, UV stabilized, high heat polycarbonate copolymer blend with an HDT/Af of 162C. It is available in a range of opaque and limited transparent colors. | |||||
General | |||||
Form | Resin Pellets | ||||
Feature | Good Thermal | Outdoor | |||
UL Yellow Card | E207780-100321031 | ||||
Uses | Automotive Electrical |
Consumer | Healthcare | ||
Physical | Nominal Value | Test Method | |||
Density / Specific Gravity | 1.2 1.21 g/cm³ |
ASTM D792 ISO 1183 |
|||
Mold Shrinkage, Flow(3.2 mm) | 0.6 - 0.95 % | Method | |||
Melt Flow Rate[MFR](330 °C;2.16 kgf) | 25 g/10min | ASTM D1238 | |||
Water Absorption(23 °C;saturated) | 0.33 % | ISO 62-1 | |||
Moisture Absorption(50% RH;23 °C) | 0.25 % | ISO 62 | |||
Melt Volume Rate, MVR(2.16 kg;330 °C) | 24 cm³/10 min | ISO 1133 | |||
Mechanical | Nominal Value | Test Method | |||
Izod Impact, Notched 23 °C -30 °C |
93 J/m 76 J/m |
ASTM D256 | |||
Instrumented Dart Impact, Total Energy(23 °C) | 72 J | ASTM D3763 | |||
Unnotched Izod Impact Strength unnotched;80*10*3;23 °C 0 unnotched;80*10*3;-30 °C 0 |
NB kJ/m² NB kJ/m² |
ISO 180/1U | |||
Notched Izod Impact Strength notched;80*10*3;23 °C 0 notched;80*10*3;-30 °C 0 |
10 kJ/m² 8 kJ/m² |
ISO 180/1A | |||
C harpy Impact, V-Notched 23 °C;Edgew;80*10*3;sp =62mm 0 -30 °C;Edgew;80*10*3;sp =62mm 0 |
11 kJ/m² 9 kJ/m² |
ISO 179 1eA | |||
C harpy Impact, Unnotched 23 °C;Edgew;80*10*3;sp =62mm 0 -30 °C;Edgew;80*10*3;sp =62mm 0 |
NB kJ/m² NB kJ/m² |
ISO 179 1eU | |||
Tensile Stress, Yield | |||||
50 mm/min;Type I | 77 MPa | ASTM D638 | |||
50 mm/min | 78 MPa | ISO 527 | |||
Tensile Stress, Break | |||||
50 mm/min;Type I | 69 MPa | ASTM D638 | |||
50 mm/min | 67 MPa | ISO 527 | |||
Tensile Strain, Yield | |||||
50 mm/min;Type I | 7 % | ASTM D638 | |||
50 mm/min | 7 % | ISO 527 | |||
Tensile Strain, Break | |||||
50 mm/min;Type I | 50 % | ASTM D638 | |||
50 mm/min | 50 % | ISO 527 | |||
Tensile Modulus | |||||
5 mm/min | 2730 MPa | ASTM D638 | |||
1 mm/min | 2750 MPa | ISO 527 | |||
Flexural Stress, Yield | |||||
1.3 mm/min;50 mm;span | 120 MPa | ASTM D790 | |||
2 mm/min | 80 MPa | ISO 178 | |||
Flexural Modulus | |||||
1.3 mm/min;50 mm;span | 2600 MPa | ASTM D790 | |||
2 mm/min | 2600 MPa | ISO 178 | |||
Thermal | Nominal Value | Test Method | |||
UL Recognized(≥ 1.5 mm) | HB | UL 94 | |||
Glow Wire Ignition Temperature [GWIT](3 mm) | 875 °C | IEC 60695-2-13 | |||
Glow Wire Flammability Index(3 mm) | 960 °C | IEC 60695-2-12 | |||
Vicat Softening Temperature | |||||
Rate B/50 | 183 °C | ASTM D1525 | |||
Rate B/50 | 183 °C | ISO 306 | |||
Rate B/120 | 181 °C | ISO 306 | |||
Heat Deflection Temperature[HDT], Unannealed 0.45 MPa;3.2 mm 3.2 mm;1.82 MPa |
174 °C 165 °C |
ASTM D648 | |||
CTE, Flow | |||||
-40 - 40 °C | 6.0E-05 1/°C | ASTM E831 | |||
-40 - 40 °C | 6.0E-05 1/°C | ISO 11359-2 | |||
CTE, XFlow | |||||
-40 - 40 °C | 6.0E-05 1/°C | ASTM E831 | |||
-40 - 40 °C | 6.0E-05 1/°C | ISO 11359-2 | |||
Ball Pressure Test(165°C +/- 2°C) | PASSES | IEC 60695-10-2 | |||
HDT/Bf(0.45) | 173 °C | ISO 75/Bf | |||
HDT/Af(1.8) | 162 °C | ISO 75/Af | |||
Relative Temp Index, Elec | 150 °C | UL 746B | |||
Relative Temp Index, Mechanical with Impact | 130 °C | UL 746B | |||
Relative Temp Index, Mechanical without Impact | 150 °C | UL 746B | |||
Electrical | Nominal Value | Test Method | |||
Comparative Tracking Index, CTI | PLC 3 | UL 746A | |||
Hot-wire Ignition, HWI(1.5 mm) | PLC 3 | UL 746A | |||
High Amp Arc Ignition, HAI(1.5 mm) | PLC 0 | UL 746A | |||
Processing | Nominal Value | ||||
Drying Temperature<Injection> | 135 °C | ||||
Drying Time<Injection> | 4 - 6 hrs | ||||
Maximum Moisture Content<Injection> | 0.02 % | ||||
Melt Temperature<Injection> | 300 - 315 °C | ||||
Nozzle Temperature<Injection> | 295 - 310 °C | ||||
Front, Zone 3 Temperature<Injection> | 300 - 315 °C | ||||
Middle, Zone 2 Temperature<Injection> | 290 - 305 °C | ||||
Rear, Zone 1 Temperature<Injection> | 280 - 295 °C | ||||
Mold Temperature<Injection> | 95 - 130 °C | ||||
Back Pressure<Injection> | 0.3 - 0.7 MPa | ||||
Screw Speed <Injection> | 40 - 90 rpm | ||||
Shot To Cylinder Size<Injection> | 40 - 60 % | ||||
Vent Depth <Injection> | 0.025 - 0.08 mm |