Opaque EXL, UV-Stabilized & light shielding capability (Wall thickness >0.8mm), for portable electronics device enclosure application. Only available in white, grey and limited pastel colors. Consult CIC or PM for color availability & limitation. |
||||
General | ||||
Form | Resin Pellets | |||
Feature | Low Temperature Impact Outdoor Li ht Shi ldi | High Impact | ||
UL Yellow Card E207780-642296 | ||||
Uses Automotive | Industria | Electrical | ||
Physical | Nominal Value | Test Method | ||
Density / Specific Gravity | 1.28 1.28 g/cm³ |
ASTM D792 ISO 1183 |
||
Mold Shrinkage, Flow(3.2 mm) | 0.4 - 0.8 % | Method | ||
Melt Flow Rate[MFR](300 °C;1.2 kgf) | 11 g/10min | ASTM D1238 | ||
Water Absorption(23 °C;saturated) | 0.17 % | ISO 62-1 | ||
Moisture Absorption(50% RH;23 °C) | 0.07 % | ISO 62 | ||
Melt Volume Rate, MVR(1.2 kg;MVR at 300 °C) | 10 cm³/10 min | ISO 1133 | ||
Mechanical | Nominal Value | Test Method | ||
Izod Impact, Notched | ||||
23 °C | 766 J/m | ASTM D256 | ||
-30 °C | 640 J/m | ASTM D256 | ||
80*10*4;23 °C | 56 kJ/m² | ISO 180/1A | ||
80*10*4;-30 °C | 46 KJ/m² | ISO 180/1A | ||
Instrumented Dart Impact, Total Energy(23 °C) | 68 J | ASTM D3763 | ||
C harpy Impact, V-Notched(23 °C;Edgew;80*10*4;sp =62 mm 0) | 55 kJ/m² | ISO 179 1eA | ||
Tensile Stress, Yield | ||||
50 mm/min;Type I | 52 MPa | ASTM D638 | ||
50 mm/min | 52 MPa | ISO 527 | ||
Tensile Stress, Break | ||||
50 mm/min;Type I | 54 MPa | ASTM D638 | ||
50 mm/min | 47 MPa | ISO 527 | ||
Tensile Strain, Yield | ||||
50 mm/min;Type I | 5 % | ASTM D638 | ||
50 mm/min | 5 % | ISO 527 | ||
Tensile Strain, Break | ||||
50 mm/min;Type I | 84 % | ASTM D638 | ||
50 mm/min | 75 % | ISO 527 | ||
Tensile Modulus | ||||
50 mm/min | 2030 MPa | ASTM D638 | ||
1 mm/min | 2000 MPa | ISO 527 | ||
Flexural Stress, Yield | ||||
1.3 mm/min;50 mm;span | 86 MPa | ASTM D790 | ||
2 mm/min | 83 MPa | ISO 178 | ||
Flexural Modulus | ||||
1.3 mm/min;50 mm;span | 2050 MPa | ASTM D790 | ||
2 mm/min | 2110 MPa | ISO 178 | ||
Thermal | Nominal Value | Test Method | ||
UL Recognized(0.4 mm) | HB | UL 94 | ||
Vicat Softening Temperature | ||||
Rate B/50 | 138 °C | ASTM D1525 | ||
Rate B/50 | 138 °C | ISO 306 | ||
Rate B/120 | 146 °C | ISO 306 | ||
Heat Deflection Temperature[HDT], Unannealed(3.2 mm;1.82 MPa) | 121 °C | ASTM D648 | ||
CTE, Flow | ||||
-40 - 40 °C | 7.0E-05 1/°C | ASTM E831 | ||
-40 - 40 °C | 7.0E-05 1/°C | ISO 11359-2 | ||
CTE, XFlow | ||||
-40 - 40 °C | 6.7e-05 1/°C | ASTM E831 | ||
-40 - 40 °C | 8.2E-05 1/°C | ISO 11359-2 | ||
HDT/Af(1.8) | 118 °C | ISO 75/Af | ||
Relative Temp Index, Elec | 80 °C | UL 746B | ||
Relative Temp Index, Mechanical with Impact | 80 °C | UL 746B | ||
Relative Temp Index, Mechanical without Impact | 80 °C | UL 746B | ||
Processing | Nominal Value | |||
Drying Temperature<Injection> | 120 °C | |||
Drying Time<Injection> | 3 - 4 hrs | |||
Maximum Moisture Content<Injection> | 0.02 % | |||
Melt Temperature<Injection> | 295 - 315 °C | |||
Nozzle Temperature<Injection> | 290 - 310 °C | |||
Front, Zone 3 Temperature<Injection> | 295 - 315 °C | |||
Middle, Zone 2 Temperature<Injection> | 280 - 305 °C | |||
Rear, Zone 1 Temperature<Injection> | 260 - 280 °C | |||
Hopper Temperature<Injection> | 60 - 80 °C | |||
Mold Temperature<Injection> | 70 - 95 °C |