Product Description | ||||
PC 8000-05 polycarbonate(PC) siloxane copolymer resin is designed for extrusion and injection molding products. It exhibits an excellent low temperature ductility and good physical property balance of heat resistance, transparency and impact strength. Main Characteristics Low Temperature ductility No UV absorbers No Mold release agent Applications Compounds Small appliances Packaging applications |
||||
General | ||||
Form | Resin Pellets | |||
Feature Ductile | Clean/High Purity | Good Thermal | ||
Uses Appliances | Compounding | Packaging | ||
Physical | Nominal Value | Test Method | ||
Density / Specific Gravity | 1.20 g/cm³ | ASTM D792;ISO 1183 | ||
Melt Mass-Flow Rate, MFR(300 °C;1.2 kg) | 3.5 g/10min | ASTM D1238 | ||
Molding Shrinkage, Flow | 0.50 - 0.70 % | ASTM D955 | ||
Water Absorption(24 hr;23 °C) | 0.12 % | ASTM D570;ISO 62 | ||
Water Absorption, Equilibrium(50% RH;23 °C) | 0.20 % | ASTM D570;ISO 62 | ||
Rockwell Hardness, M-Scale | 50 | ASTM D785;ISO 2039-2 | ||
Rockwell Hardness, R-Scale | 120 | ASTM D785;ISO 2039-2 | ||
Mechanical | Nominal Value | Test Method | ||
Tensile Modulus | ||||
2180 MPa | ASTM D638 | |||
2390 MPa | ISO 527-2 | |||
Tensile Strength, Yield | ||||
50 mm/min;23 °C | 58.0 MPa | ASTM D638 | ||
23 °C | 57.0 MPa | ISO 527-2/50 | ||
Tensile Strength, Break | ||||
68.0 MPa | ASTM D638 | |||
64.0 MPa | ISO 527-2 | |||
Tensile Elongation, Yield | 6.0 % | ASTM D638;ISO 527-2 | ||
Tensile Elongation, Break | ||||
120 % | ASTM D638 | |||
110 % | ISO 527-2 | |||
Flexural Modulus | ||||
2030 MPa | ASTM D790 | |||
1940 MPa | ISO 178 | |||
Flexural Strength | ||||
86.0 MPa | ASTM D790 | |||
82.0 MPa | ISO 178 | |||
Notched Izod Impact | ||||
-30 °C;3.18 mm;0.25 mm;Notch Depth | 760 J/m | ASTM D256 | ||
23 °C;3.18 mm;0.25 mm;Notch Depth | 890 J/m | ASTM D256 | ||
-30 °C | 60 kJ/m² | ISO 180 | ||
23 °C | 70 kJ/m² | ISO 180 | ||
Unnotched Izod Impact(23 °C) | No Break | ISO 180;ASTM D256 | ||
Thermal | Nominal Value | Test Method | ||
Deflection Temperature Under Load, Annealed 0.45 MPa;4 mm 1.8 MPa;4 mm |
132 °C 130 °C |
ASTM D648 | ||
Deflection Temperature Under Load, Unannealed | ||||
1.8 MPa;4 mm | 118 °C | ASTM D648 | ||
1.8 MPa | 115 °C | ISO 75-2/A | ||
Vicat Softening Temperature(50 °C/h;50 N;Rate A;Loading 2) | 138 °C | ASTM D1525;ISO 306/B120 | ||
CLTE, Flow(-40 - 82 °C) | 7.0E-5 cm/cm/°C | ASTM D696 | ||
Electrical | Nominal Value | Test Method | ||
Volume Resistivity(23 °C) | 1.0e+15 ohms ·cm | ASTM D257 | ||
Optical | Nominal Value | Test Method | ||
Transmittance | ||||
3.0e+3 µm | > 88.0 % | ASTM D1003 | ||
3.0e+3 µm | > 88.0 % | ISO 13468-1 | ||
Haze | ||||
3.0e+3 µm | < 1.00 % | ASTM D1003 | ||
3.0e+3 µm | < 1.00 % | ISO 14782 |