Halogen Free and Red Phosphorous Free Flame Retardant Mineral Reinforced Polyamide
https://forever-plastics.en.made-in-china.com/product/rJwRvlcdZpWD/China-Nylon-PA6-GF33-PA66-Granules-PA6-with-30GF-Polyamide-PA66-30-GF-PA6-Material.html Heat-conducting nylon
Product Description | |||
PROTECT C 52G4 MZ25 WT R9003 is a polyamide 6 based on a non-phosphorous and Non-halogenated flame retardant system, reinforced with 25% of mineral filler, heat stabilized, for injection moulding. This grade offers a robust glow wire resistance, combined with enhanced processing behavior suitable for thin wall parts. | |||
General | |||
Form Resin Pellets | |||
Filler 25 % Mineral | |||
Chlorinated Flame R t d t |
|||
Uses Connector Electrical | |||
Physical Nominal Value Test Method | |||
Density / Specific Gravity 1.37 g/cm³ ISO 1183 | |||
Water Absorption(24 hr, 23°C) 1 % ISO 62 | |||
Water Absorption at Saturation(24 hr, 23°C) 6 % ISO 62 | |||
Molding shrinkage, parallel(72 hr, 23°C, 50% RH) 0.6 % | |||
Molding shrinkage, normal(72 hr, 23°C, 50% RH) 0.8 % | |||
Mechanical | Nominal Value | Test Method | |
Tensile Modulus 1 mm/min/dry 1 mm/min/conditioned |
6900 MPa 2400 MPa |
ISO 527-1/-2 | |
Stress at break dry conditioned |
75 MPa 35 MPa |
ISO 527-1/-2 | |
Strain at break | 3 % | ISO 527-1/-2 | |
Flexural Modulus 2 mm/min/dry 2 mm/min/conditioned 2 mm/min |
6300 MPa 2500 MPa 6000 MPa |
ISO 178 ISO 178 ASTM D790 |
|
Flexural Strength 2 mm/min/dry 2 mm/min/conditioned 2 mm/min |
125 MPa 50 MPa 120 MPa |
ISO 178 ISO 178 ASTM D790 |
|
C harpy Impact Strength, Unnotched dry; 23 ºC conditioned; 23 -30 °C |
35 kJ/m² 80 kJ/m² 45 kJ/m² |
ISO 179 1eU | |
C harpy Notched Impact Strength dry; 23 ºC conditioned; 23 -30 °C |
3 kJ/m² 4.5 kJ/m² 2.5 kJ/m² |
ISO 179 1eA | |
Notched Izod Impact Strength(23 ºC) | 2 kJ/m² | ISO 180/1A | |
Thermal | Nominal Value | Test Method | |
Melting Temperature(10°C/min) | 222 °C | ISO 11357-1 | |
Temp. of deflection under load 0.45 MPa 1.8 MPa |
200 °C 130 °C |
ISO 75 | |
Flammability 0.75 mm 1.5 mm 3 mm |
V-2 V-2 V-2 |
UL 94 | |
Electrical | Nominal Value | Test Method | |
Comparative Tracking Index(Solution A) | 525 V | IEC 60112 | |
Dielectric Strength(1 mm) | 35 kV/mm | IEC 60243-1 | |
Processing | Nominal Value | ||
Drying Temperature | 80 °C | ||
Drying Time | 2 - 4 h | ||
Suggested Max Moisture | 0.2 % | ||
Rear Temperature | 230 - 235 °C | ||
Middle Temperature | 235 - 240 °C | ||
Front Temperature | 240 - 250 °C | ||
Mould Temperature<Injection> | 60 - 90 °C |