PA6 Compound Is Based on Nylon 6 Resin Containing Proprietary Thermal Filler

• Feature: Oxidative Degradable
• CAS No.: 32131-17-2
• Formula: (C12h22n2o2)N
• Shipping Cost: Estimated freight per unit.: about shipping cost and estimated delivery time.
• Currency: US$
• Return&refunds: You can apply for a refund up to 30 days after receipt of the products.
• Model NO.: PA-PX13012
• EINECS: 211-024-8
• Material: Polyamide(Nylon 6.66)/PA
• Usage: General Plastics, Engineering Plastics, Specialty Plastics
• Plastic Properties After Heated: Thermoplastic Plastics
• Plastic Forming Method: Injection
• Color: Black
• Form: Resin Pellets
• Chemical Substances: Nylon
• Processing Mode: Injection Molding/Extrusion
• UV: Fr
• Use: Electrical Appliances, Auto Parts, Office Supplies
• Certificates: ISO9001:2008.SGS.RoHS
• Filler: 10%-50% Glass Fiber
• Transport Package: Bag
• Specification: 25KG
• Trademark: Forever
• Origin: China
• HS Code: 390740000
• Production Capacity: 50000t/Year
• Package Size: 75.00cm * 55.00cm * 15.00cm
• Package Gross Weight: 25.010kg

Product Description

PA6 compound is based on Nylon 6 resin containing proprietary thermal filler
 Heat-conducting nylon

Product Description

Product Description
PX13012 compound is based on Nylon 6 resin containing proprietary thermal filler. Added features of this grade include: Thermally Conductive, Electrically Insulative and Non-Brominated, Non-Chlorinated Flame   Retardant.
General
Form	Resin Pellets
Feature		Thermally Conductive	Non-Brominated & Non- Chlorinated Flame   Retardant		Non-Chlorinated Electrically Isolative
UL Yellow Card                         E45329-101769086
Uses	Consumer                         Industria   Building and Construction			Electrical
Physical			Nominal Value		Test Method
Molding Shrinkage, Flow, Tensile Bar			0.7 %		Method
Mold Shrinkage, Flow
24 hrs			0.55 %		ASTM D955
24 hrs			0.55 %		ISO 294
Mold Shrinkage, XFlow
24 hrs			0.65 %		ASTM D955
24 hrs			0.65 %		ISO 294
Density / Specific Gravity			1.68 g/cm³		ISO 1183
Water Absorption(24 hrs;23 °C)			0.23 %		ISO 62-1

 

Mechanical	Nominal Value	Test Method
Izod Impact, Unnotched
23 °C	152 J/m	ASTM D4812
80*10*4;23 °C	9 kJ/m²	ISO 180/1U
Izod Impact, Notched
23 °C	15 J/m	ASTM D256
80*10*4;23 °C	3 kJ/m²	ISO 180/1A
Tensile Stress, Yield(5 mm/min;Type I)	68 MPa	ASTM D638
Tensile Strain, Break
5 mm/min;Type I	1.2 %	ASTM D638
5 mm/min	1.1 %	ISO 527
Tensile Modulus
5 mm/min	1.0E+04 MPa	ASTM D638
1 mm/min	1.3E+04 MPa	ISO 527
Flexural Stress, break(1.3 mm/min;50 mm;span)	119 MPa	ASTM D790
Flexural Modulus
1.3 mm/min;50 mm;span	1.2E+04 MPa	ASTM D790
2 mm/min	1.2E+04 MPa	ISO 178
Tensile Stress, Break(5 mm/min)	75 MPa	ISO 527
Flexural Stress, Yield(2 mm/min)	105 MPa	ISO 178

Thermal                                                                                Nominal Value					Test Method
UL Recognized(≥ 0.8 mm)                                                   V-0					UL 94
Glow Wire Ignition Temperature [GWIT] 0.8 mm 1.6 mm 3 mm	750 °C 775 °C 800 °C				IEC 60695-2-13
Glow Wire Flammability Index 0.8 mm 1.6 mm 3 mm	960 °C 960 °C 960 °C				IEC 60695-2-12
Heat Deflection Temperature[HDT](0.45 MPa;3.2 mm)     203 °C					ASTM D648
Heat Deflection Temperature[HDT], Unannealed(3.2 mm;1.82 MPa)			137 °C		ASTM D648
CTE, Flow -40 - 40 °C -30°C to 80°C	3.3E-05 3.9E-05			1/°C 1/°C	ASTM E831 ISO 11359-2
CTE, XFlow -40 - 40 °C -30°C to 80°C	4.4E-05 1/°C 5.5e-05 1/°C				ASTM E831 ISO 11359-2
Thermal conductivity through plane(60*60*3mm plaque) 1.2 W/m-K					ISO 22007-2
Thermal conductivity in plane(60*60*3mm plaque)          5.5 W/m-K					ISO 22007-2
Ball Pressure Test(165°C +/- 2°C)                                        PASSES					IEC 60695-10-2
HDT/Bf(0.45)                                                                        203 °C					ISO 75/Bf
HDT/Af(1.8)                                                                           160 °C					ISO 75/Af
Relative Temp Index, Elec                                                    130 °C					UL 746B
Relative Temp Index, Mechanical with Impact                   100 °C					UL 746B
Relative Temp Index, Mechanical without Impact              130 °C					UL 746B
Electrical		Nominal Value			Test Method
Surface Resistivity		4.0E+14 ohms			ASTM D257
Dielectric Strength, in Oil(1.6 mm)		7.2 kV/mm			ASTM D149
Dielectric Strength(1.6 mm)		6.1 kV/mm			IEC 60243-1
Comparative Tracking Index, CTI		PLC 0			UL 746A
Comparative Tracking Index		600 V			IEC 60112
Hot-wire Ignition, HWI( ≥ 0.8 mm)		PLC 0			UL 746A
High Amp Arc Ignition, HAI( ≥ 0.8 mm)		PLC 0			UL 746A
Processing					Nominal Value
Drying Temperature<Injection>					80 °C
Drying Time<Injection>					4 hrs
Maximum Moisture Content<Injection>					0.25 %
Minimum Moisture Content<Injection>					0.15 %
Melt Temperature<Injection>					270 - 295 °C
Front, Zone 3 Temperature<Injection>					270 - 290 °C
Middle, Zone 2 Temperature<Injection>					270 - 290 °C
Rear, Zone 1 Temperature<Injection>					260 - 275 °C
Mold Temperature<Injection>					85 - 100 °C
Back Pressure<Injection>					0.2 - 0.3 MPa
Screw Speed <Injection>					20 - 60 rpm

 

                                                                                                                  Forever Co.,Ltd

 

With almost 20 years in the modified engineering plastics,Forever Plastics is a high-tech manufacture integrating R&D, production and sales of high-performance resin or polymer ,including PC,PP,PA6,PA66, PBT,PET, PC/ABS, PC/PBT, PC/PET alloy compounds,TPE,TPU, PE for rotomolding with the property of the flame retardant, glass fiber reinforced, high glossy, UV resistance.....with the annual output value of USD 65 million in 2021. 

Our customers are Osram,Cree,,Siemens,etc. for years in the electrical&electronics components, Automotive parts, House appliance,LED lights.....