| Feature: | Oxidative Degradable |
|---|---|
| CAS No.: | 32131-17-2 |
| Formula: | (C12h22n2o2)N |
| Samples: |
|---|
| Customization: |
|---|
|
Shipping Cost:
Estimated freight per unit. |
about shipping cost and estimated delivery time. |
|---|
| Payment Method: |
|
|---|---|
| Initial Payment Full Payment |
| Currency: | US$ |
|---|
| Return&refunds: | You can apply for a refund up to 30 days after receipt of the products. |
|---|
Suppliers with verified business licenses
Audited Supplier Nylon 6 resin containing glass fiber and proprietary thermal filler of this grade include
https://forever-plastics.en.made-in-china.com/product/rJwRvlcdZpWD/China-Nylon-PA6-GF33-PA66-Granules-PA6-with-30GF-Polyamide-PA66-30-GF-PA6-Material.html Heat-conducting nylon
| Product Description | ||||
| PX10323 compound is based on Nylon 6 resin containing glass fiber and proprietary thermal filler. Added features of this grade include: Thermally Conductive. | ||||
| General | ||||
| Form Resin Pellets | ||||
| Filler Glass Fiber | ||||
| Feature Electrically Conductive Thermally Conductive | ||||
| Uses | Consumer Industria Building and Construction |
Electrical | ||
| Physical Nominal Value Test Method | ||||
| Density / Specific Gravity 1.61 g/cm³ ASTM D792 | ||||
| Mold Shrinkage, Flow(24 hrs) 0.2 % ASTM D955 | ||||
| Mold Shrinkage, XFlow(24 hrs) 0.22 % ASTM D955 | ||||
| Moisture Absorption(50% RH;23 °C) 0.04 % ISO 62 | ||||
| Mechanical | Nominal Value | Test Method | ||
| Izod Impact, Unnotched | ||||
| 23 °C | 73 J/m | ASTM D4812 | ||
| 80*10*4;23 °C | 6 kJ/m² | ISO 180/1U | ||
| Izod Impact, Notched | ||||
| 23 °C | 30 J/m | ASTM D256 | ||
| 80*10*4;23 °C | 3 kJ/m² | ISO 180/1A | ||
| Tensile Stress, Break | ||||
| 5 mm/min;Type I | 70 MPa | ASTM D638 | ||
| 5 mm/min | 73 MPa | ISO 527 | ||
| Tensile Strain, Break | ||||
| 5 mm/min;Type I | 0.9 % | ASTM D638 | ||
| 5 mm/min | 0.8 % | ISO 527 | ||
| Tensile Modulus | ||||
| 5 mm/min | 1.4E+04 MPa | ASTM D638 | ||
| 1 mm/min | 1.4E+04 MPa | ISO 527 | ||
| Flexural Stress, Yield(1.3 mm/min;50 mm;span) | 96 MPa | ASTM D790 | ||
| Flexural Stress, break | ||||
| 1.3 mm/min;50 mm;span | 95 MPa | ASTM D790 | ||
| 2 mm/min | 96 MPa | ISO 178 | ||
| Flexural Modulus | ||||
| 1.3 mm/min;50 mm;span | 1.4E+04 MPa | ASTM D790 | ||
| 2 mm/min | 1.4E+04 MPa | ISO 178 | ||
| Impact Strength | 3.7 - 6.8 kJ/m² | ISO R179 | ||
| Thermal | Nominal Value | Test Method | ||
| Glow Wire Flammability Index 1 mm 1.6 mm |
850 °C 960 °C |
IEC 60695-2-12 | ||
| Glow Wire Ignition Temperature [GWIT](1 mm) | 825 °C | IEC 60695-2-13 | ||
| Heat Deflection Temperature[HDT], Unannealed(1.82 MPa;6.4 mm) | 204 °C | ASTM D648 | ||
| CTE, Flow(40°C to 120°C) | 1.2E-05 1/°C | ASTM E831 | ||
| CTE, XFlow(40°C to 120°C) | 7.3e-05 1/°C | ASTM E831 | ||
| Thermal conductivity through plane | ||||
| 60*60*3mm plaque | 1.5 W/m-K | ISO 22007-2 | ||
| 10*10*3mm sample | 3.5 W/m-K | ASTM E1461-07 | ||
| Thermal conductivity in plane | ||||
| 60*60*3mm plaque | 18 W/m-K | ISO 22007-2 | ||
| 25*0.4mm disc | 15 W/m-K | ASTM E1461-07 | ||
| HDT/Bf(0.45) | 217 °C | ISO 75/Bf | ||
| HDT/Af(1.8) | 201 °C | ISO 75/Af | ||
| Electrical | Nominal Value | Test Method | ||
| Surface Resistivity | 1.0E+06 ohms | ASTM D257 | ||
| Processing | Nominal Value | |||
| Drying Temperature<Injection> | 80 °C | |||
| Drying Time<Injection> | 4 hrs | |||
| Maximum Moisture Content<Injection> | 0.15 - 0.25 % | |||
| Melt Temperature<Injection> | 270 - 295 °C | |||
| Front, Zone 3 Temperature<Injection> | 270 - 290 °C | |||
| Middle, Zone 2 Temperature<Injection> | 270 - 290 °C | |||
| Rear, Zone 1 Temperature<Injection> | 260 - 275 °C | |||
| Mold Temperature<Injection> | 85 - 100 °C | |||
| Back Pressure<Injection> | 0.2 - 0.3 MPa | |||
| Screw Speed <Injection> | 20 - 60 rpm | |||