Feature: | Plastics |
---|---|
CAS No.: | 25766-59-0 |
Formula: | C6h4c(CH3)2c6h4oco2-]N |
Samples: |
25kg/bag
|
---|
Customization: |
---|
Shipping Cost:
Estimated freight per unit. |
about shipping cost and estimated delivery time. |
---|
Payment Method: | |
---|---|
Initial Payment Full Payment |
Currency: | US$ |
---|
Return&refunds: | You can apply for a refund up to 30 days after receipt of the products. |
---|
Suppliers with verified business licenses
Product Description | |||
polycarbonate; flame retardant; high thermal conductivity; light components; LED heat sinks (metal replacement); components for heat dissipation | |||
General | |||
Form Resin Pellets | |||
Feature | Thermally Conductive(Isolation) |
||
Uses Lighting Applications Electrical | |||
Physical Nominal Value Test Method | |||
Density / Specific Gravity(23 °C) 1.42 g/cm³ ISO 1183 | |||
Molding Shrinkage, Across Flow(2 mm) 0.050 - 0.15 % ISO 294-4 | |||
Molding Shrinkage, Flow(2 mm) 0.050 - 0.15 % ISO 294-4 | |||
Melt Viscosity ISO 11443-A | |||
1000s-1;280 °C 200 Pa · s | |||
300 °C;1000s-1 120 Pa · s | |||
Mechanical Nominal Value Test Method | |||
Tensile Modulus(23 °C) 8500 MPa ISO 527-1/1 | |||
Tensile Stress, Break(23 °C) 40.0 MPa ISO 527-2/5 | |||
Tensile Strain, Break(23 °C) 1.0 % ISO 527-2/5 | |||
Flexural Modulus(2 mm/min;23 °C) 9000 MPa ISO 178 | |||
Flexural Stress(2 mm/min;23 °C) 62.0 MPa ISO 178 | |||
Flexural Strain at Flexural Strength(2 mm/min;23 °C) 1.0 % ISO 178 | |||
C harpy Unnotched Impact Strength(23 °C) 4.0 kJ/m² ISO 179/1eU | |||
Thermal | Nominal Value | Test Method | |
Deflection Temperature Under Load, Unannealed 0.45 MPa 1.8 MPa |
130 °C 125 °C |
ISO 75-2/B ISO 75-2/A |
|
Vicat Softening Temperature | 130 °C | ISO 306/B50 | |
CLTE, Flow(23 - 55 °C) | 2.5E-5 cm/cm/°C | ISO 11359-2 | |
CLTE, Transverse(23 - 55 °C) | 4.0E-5 cm/cm/°C | ISO 11359-2 | |
Thermal Conductivity, in-plane(23 °C) | 1.3 W/m/K | ASTM E1461 | |
Thermal Conductivity, through-plane(23 °C) | 16 W/m/K | ASTM E1461 | |
Flame Rating(2 mm) | V-0 | UL 94 | |
Glow Wire Flammability Index 1.5 mm 3 mm |
960 °C 960 °C |
IEC 60695-2-12 | |
Glow Wire Ignition Temperature [GWIT] 1.5 mm 3 mm |
875 °C 930 °C |
IEC 60695-2-13 | |
Electrical | Nominal Value | Test Method | |
Volume Resistivity(23 °C) | 1.0E+2 ohms ·cm | IEC 60093 | |
Processing | Nominal Value | ||
Drying Temperature - Dry Air Dryer<Injection> | 110 °C | ||
Drying Time - Dry Air Dryer<Injection> | 4.0 hr | ||
Suggested Max Moisture<Injection> | < 0.20 % | ||
Rear Temperature<Injection> | 270 - 290 °C | ||
Middle Temperature<injection> | 280 - 300 °C | ||
Front Temperature<Injection> | 290 - 310 °C | ||
Nozzle Temperature<Injection> | 300 - 320 °C | ||
Processing Temp, Melt<Injection> | 300 - 320 °C | ||
Mold Temperature<Injection> | 80 - 90 °C | ||
Back Pressure<Injection> | 5.00 - 15.0 MPa | ||
Vent Depth <Injection> | 0.025 - 0.075 mm |