Polyphthalamide (PPA) Is a 35% Glass Reinforced Resin That Is Heat Stabilized

• Feature: Oxidative Degradable
• CAS No.: 32131-17-2
• Formula: (C12h22n2o2)N
• Shipping Cost: Estimated freight per unit.: about shipping cost and estimated delivery time.
• Currency: US$
• Return&refunds: You can apply for a refund up to 30 days after receipt of the products.
• Model NO.: PPA-A-6135HN
• EINECS: 211-024-8
• Material: Polyamide(Nylon 6.66)/PA
• Usage: General Plastics, Engineering Plastics, Specialty Plastics
• Plastic Properties After Heated: Thermoplastic Plastics
• Plastic Forming Method: Injection
• Color: Black
• Form: Resin Pellets
• Chemical Substances: Nylon
• Processing Mode: Injection Molding/Extrusion
• UV: Fr
• Use: Electrical Appliances, Auto Parts, Office Supplies
• Certificates: ISO9001:2008.SGS.RoHS
• Filler: 10%-60% Glass Fiber
• Transport Package: Bag
• Specification: 25KG
• Trademark: Forever
• Origin: China
• HS Code: 390740000
• Production Capacity: 50000t/Year
• Package Size: 75.00cm * 55.00cm * 15.00cm
• Package Gross Weight: 25.010kg

Product Description

polyphthalamide (PPA) is a 35% glass reinforced resin that is heat stabilized
 Heat-conducting nylon

Product Description

Product Description
A-6135 HN polyphthalamide (PPA) is a 35% glass reinforced resin that is heat stabilized, non-lubricated and hot-water moldable. Key properties of the resin are high heat resistance, high strength and stiffness over a broad temperature range. It also exhibits low moisture absorption excellent chemical resistance and excellent electrical properties.  A-6135 HN resin is ideal for automotive electrical and electronic applications,   including connectors, sockets, switches and sensors. It is also a good choice for under-hood enclosures that    protect critical control systems such as anti lock brakes, traction control, steering, electronic engine control,    transmission and chassis control units. Black: A-6135 HN BK 324
General
Form                                        Resin Pellets
Filler                                         35 % Glass Fiber
Chemical Resistant		Creep Resistance		Excellent Processability
Feature                                     Enhanced Stiffness		Good Thermal		Good Hardness
Hot Water Moldability		Low Moisture
Automotive Electronics		Automotive Under The   Hood		Industrial Applications Industrial Parts
Uses	Lawn And Garden Equipment	Metal Replacement		Automotive
		Connector		Electrical Engineering
Valves/Valve Parts		Mechanical Parts
Physical		Nominal Value		Test Method
Density, dry		1.45 g/cm³		ISO 1183/A
Dry: Molding Shrinkage, Flow
		0.60 %		ASTM D955
		0.50 %		ISO 294-4
Dry: Molding Shrinkage, Across Flow
		0.90 %		ASTM D955
		1.0 %		ISO 294-4
Dry: Water Absorption
24 hr		0.30 %		ASTM D570
24 hr;23 °C		0.29 %		ISO 62
Dry: Rockwell Hardness, R-Scale		125		ASTM D785
Mechanical		Nominal Value		Test Method
Dry: Tensile Modulus				ASTM D638
23 °C		13800 MPa		ISO 527-2
100 °C		11500 MPa		ISO 527-2
150 °C		7310 MPa		ISO 527-2
175 °C		6270 MPa		ISO 527-2
		5310 MPa

 

Condition: Tensile Modulus	12200 MPa			ASTM D638
Dry: Tensile Stress, Break 23 °C 100 °C 150 °C 175 °C	211 MPa 121 MPa 92.4 MPa 82.0 MPa			ISO 527-2
Dry: Tensile Stress	203 MPa			ASTM D638
Condition: Tensile Stress	176 MPa			ASTM D638
Dry: Tensile Elongation, Break	1.9 %			ASTM D638
23 °C	2.0 %			ISO 527-2
100 °C	4.3 %			ISO 527-2
150 °C	4.9 %			ISO 527-2
175 °C	4.7 %			ISO 527-2
Condition: Tensile Elongation, Break	2.1 %			ASTM D638
Dry: Flexural Modulus	11400 MPa			ASTM D790
23 °C	11400 MPa			ISO 178
100 °C	6600 MPa			ISO 178
150 °C	4900 MPa			ISO 178
175 °C	4600 MPa			ISO 178
Condition: Flexural Modulus	11000 MPa			ASTM D790
Dry: Flexural Strength	310 MPa			ASTM D790
3.5% Strain;23 °C	300 MPa			ISO 178
3.5% Strain;100 °C	170 MPa			ISO 178
3.5% Strain;150 °C	123 MPa			ISO 178
3.5% Strain;175 °C	112 MPa			ISO 178
Condition: Flexural Strength		249 MPa		ASTM D790
Dry: Compressive Strength		148 MPa		ASTM D695
Dry: Shear Strength		87.6 MPa		ASTM D732
Condition: Shear Strength		73.8 MPa		ASTM D732
Dry: Poisson's Ratio		0.39		ASTM E132
Dry: Charpy Notched Impact Strength(23 °C)		9.2 kJ/m²		ISO 179 1eA
Dry: Charpy Unnotched Impact Strength(23 °C)		60 kJ/m²		ISO 179 1eU
Dry: Notched Izod Impact		85 J/m		ASTM D256
23 °C		9.1 kJ/m²		ISO 180
Izod Notched Impact: condition		69 J/m		ASTM D256
Dry: Unnotched Izod Impact		800 J/m		ASTM D256
23 °C		62 kJ/m²		ISO 180
Thermal		Nominal Value		Test Method
Dry: Heat Deflection Temperature, Unannealed
0.45 MPa		303 °C		ISO 75-2/B
1.8 MPa		288 °C		ISO 75-2/A
Dry: Heat Deflection Temperature, Annealed(1.8 MPa;3.2 mm)		291 °C		ASTM D648
Dry: Melting Temperature		310 °C		ASTM D570;ISO 11357-3
Dry: CLTE, Flow 0 - 100 °C 100 - 200 °C		2.2E-5 cm/cm/°C 1.6E-5 cm/cm/°C		ASTM E831
Dry: CLTE, Transverse 0 - 100 °C 100 - 200 °C	6.1E-5 cm/cm/°C 1.0E-4 cm/cm/°C			ASTM E831
Processing			Nominal Value
Drying Temperature<Injection>			120 °C
Drying Time<Injection>			4.0 hr
Suggested Max Moisture<Injection>			0.030 - 0.060 %
Rear Temperature<Injection>			316 - 321 °C
Front Temperature<Injection>			327 - 332 °C
Processing Temp, Melt<Injection>			321 - 335 °C
Mold Temperature<Injection>			66 - 93 °C
Injection Rate<Injection>			3 - 6 in/sec
Holding Pressure<Injection>			50 of injection pressure %

 

                                                                                                                  Forever Co.,Ltd

 

With almost 20 years in the modified engineering plastics,Forever Plastics is a high-tech manufacture integrating R&D, production and sales of high-performance resin or polymer ,including PC,PP,PA6,PA66, PBT,PET, PC/ABS, PC/PBT, PC/PET alloy compounds,TPE,TPU, PE for rotomolding with the property of the flame retardant, glass fiber reinforced, high glossy, UV resistance.....with the annual output value of USD 65 million in 2021. 