| Feature: | Oxidative Degradable |
|---|---|
| CAS No.: | 32131-17-2 |
| Formula: | (C12h22n2o2)N |
| Samples: |
|---|
| Customization: |
|---|
|
Shipping Cost:
Estimated freight per unit. |
about shipping cost and estimated delivery time. |
|---|
| Payment Method: |
|
|---|---|
| Initial Payment Full Payment |
| Currency: | US$ |
|---|
| Return&refunds: | You can apply for a refund up to 30 days after receipt of the products. |
|---|
Suppliers with verified business licenses
Audited Supplier Nylon 6 plastics and can be used in a wide range of thermal management applications
https://forever-plastics.en.made-in-china.com/product/rJwRvlcdZpWD/China-Nylon-PA6-GF33-PA66-Granules-PA6-with-30GF-Polyamide-PA66-30-GF-PA6-Material.html Heat-conducting nylon
| Product Description | |||
| Thermal Management Compounds have been engineered to combine the heat transfer and cooling capabilities of metals with the design freedom, weight reduction and cost advantages of thermoplastics. These materials provide the benefits of proprietary conductive additive technologies and the performance of select engineering thermoplastic resins. Therma Tech compounds have been shown to improve thermal conductivity up to 100-times that of conventional plastics and can be used in a wide range of thermal management applications. |
|||
| General | |||
| Form Resin Pellets | |||
| Feature Electrically Conductive Thermally Conductive | |||
| Automotive Under The H d | |||
| Uses oo | Consumer | Housing | |
| Electrical | |||
| Physical | Nominal Value | Test Method | |
| Density / Specific Gravity | 1.64 g/cm³ | ISO 1183 | |
| Molding Shrinkage, Flow | 0.20 - 0.40 % | ISO 294-4 | |
| Mechanical | Nominal Value | Test Method | |
| Tensile Modulus(1 mm/min;23 °C) | 14700 MPa | ISO 527 | |
| Tensile Strength, Break(50 mm/min;23 °C) | 65.0 MPa | ISO 527 | |
| Tensile Elongation, Break(50 mm/min;23 °C) | 0.50 - 0.80 % | ISO 527 | |
| Flexural Modulus(10 mm/min;23 °C) | 13000 MPa | ISO 178 | |
| Flexural Strength(10 mm/min;23 °C) | 90.0 MPa | ISO 178 | |
| C harpy Notched Impact Strength | 3.0 kJ/m² | ISO 179/1eA | |
| C harpy Impact Strength, Unnotched | 7.0 kJ/m² | ISO 179/1eU | |
| Thermal | Nominal Value | Test Method |
| Deflection Temperature Under Load, Unannealed 0.45 MPa 1.8 MPa |
260 °C 245 °C |
ISO 75-2/B ISO 75-2/A |
| Thermal Conductivity, Through Plane 23 °C;Modified Transient Plane Source, C-Therm TCi™ |
2.3 - 2.7 W/m-K 4.5 - 5.5 W/m-K |
ASTM E1461 |
| Thermal conductivity in plane | 19 - 21 W/m-K | ASTM E1461 |
| Flame Rating 0.75 mm 1 mm 1.5 mm 3 mm |
HB HB HB V-0 |
UL 94 |
| Glow Wire Flammability Index 1 mm 1.5 mm 3 mm |
960 °C 960 °C 960 °C |
IEC 60695-2-12 |
| Glow Wire Ignition Temperature [GWIT] 1 mm 1.5 mm 3 mm |
850 °C 925 °C 925 °C |
IEC 60695-2-13 |
| Electrical | Nominal Value | Test Method |
| Surface Resistivity | < 1.0E+5 ohms | IEC 60093 |
| Processing | Nominal Value | |
| Drying Temperature | 80 °C | |
| Drying Time | 4.0 hr | |
| Suggested Max Moisture | 0.20 % | |
| Melt Temperature | 275 - 300 °C | |
| Mold Temperature | 80 - 105 °C |