Polycarbonate (PC) Is a Non-Filled Resin, Suitable for Injection Molding and Extrusion

• Feature: Plastics
• CAS No.: 25766-59-0
• Formula: C6h4c(CH3)2c6h4oco2-]N
• Shipping Cost: Estimated freight per unit.: about shipping cost and estimated delivery time.
• Currency: US$
• Return&refunds: You can apply for a refund up to 30 days after receipt of the products.
• Model NO.: PC-CFR5630
• EINECS: 618-371-8
• Material: Polycarbonates/PC
• Usage: General Plastics, Engineering Plastics, Specialty Plastics
• Plastic Properties After Heated: Thermoplastic Plastics
• Plastic Forming Method: Injection
• Color: Natural Color
• Place of Origin: Guangdong, China
• Use: Radiator Front Cover.Automotive Parts
• Features: Lubricated, Good Wear Resistance, Low Friction and
• Application: Zippers Irish Flutes, Bagpipes, Practice Chanters
• Form: Resin Pellets
• Delivery Time: in 7 Days
• Applications: Appliance Handles, Spotlights, Electric Motors.
• Glass Fiber: 0%
• Transport Package: Bag
• Specification: 25KG
• Trademark: Forever
• Origin: China
• HS Code: 390740000
• Production Capacity: 50000t/Year
• Package Size: 75.00cm * 55.00cm * 15.00cm
• Package Gross Weight: 25.010kg

Product Description

Polycarbonate (PC) is a non-filled resin, suitable for injection molding and extrusion
  
  

Product Description
CFR5630 Polycarbonate (PC) is a non-filled resin, suitable for injection molding and extrusion. This non- chlorinated, non-brominated flame retardant PC resin meets FAR25.853 smoke density and 60 second vertical    burn and OEM toxicity requirements. CFR5630 resin is available in transparent and opaque colors.
General
Form	Resin Pellets
Feature		Clear/Transparent		Aeroplane Application   Low Smoke	Non-Brominated & Non- Chlorinated Flame   Retardant
UL Yellow Card	E207780-101088462
Uses                                         Automotive				Aeroplane Application
Physical				Nominal Value	Test Method
Density / Specific Gravity				1.19 1.2 g/cm³	ASTM D792 ISO 1183
Mold Shrinkage, Flow(3.2 mm)				0.55 - 0.75 %	SABIC Method
Mold Shrinkage, XFlow(3.2 mm)				0.6 - 0.8 %	SABIC Method
Melt Flow Rate[MFR](300 °C;1.2 kgf)				5 g/10min	ASTM D1238
Water Absorption(23 °C;saturated)				0.14 %	ISO 62-1
Moisture Absorption(50% RH;23 °C)				0.11 %	ISO 62
Melt Volume Rate, MVR(1.2 kg;MVR at 300 °C)				5 cm³/10 min	ISO 1133
UV light, water exposure/immersion				f1	UL 746C
Mechanical				Nominal Value	Test Method
Izod Impact, Unnotched 23 °C -30 °C				2150 J/m 2000 J/m	ASTM D4812
Izod Impact, Notched 23 °C -30 °C				100 J/m 85 J/m	ASTM D256
Instrumented Dart Impact, Total Energy(23 °C)				66 J	ASTM D3763
Unnotched Izod Impact Strength unnotched;80*10*3;23 °C 0 unnotched;80*10*3;-30 °C 0				NB kJ/m² NB kJ/m²	ISO 180/1U
Notched Izod Impact Strength notched;80*10*3;23 °C 0 notched;80*10*3;-30 °C 0			10 kJ/m² 9 kJ/m²			ISO 180/1A
C harpy Impact, V-Notched 23 °C;Edgew;80*10*3;sp =62mm 0 -30 °C;Edgew;80*10*3;sp =62mm 0			10 kJ/m² 9 kJ/m²			ISO 179 1eA
C harpy Impact, Unnotched 23 °C;Edgew;80*10*3;sp =62mm 0 -30 °C;Edgew;80*10*3;sp =62mm 0			132 kJ/m² 129 kJ/m²			ISO 179 1eU
Tensile Stress, Yield
50 mm/min;Type I			68 MPa			ASTM D638
50 mm/min			67 MPa			ISO 527
Tensile Stress, Break
50 mm/min;Type I			52 MPa			ASTM D638
50 mm/min			52 MPa			ISO 527
Tensile Strain, Yield
50 mm/min;Type I			6 %			ASTM D638
50 mm/min			6 %			ISO 527
Tensile Strain, Break
50 mm/min;Type I			51 %			ASTM D638
50 mm/min			23 %			ISO 527
Tensile Modulus
50 mm/min			2500 MPa			ASTM D638
1 mm/min			2400 MPa			ISO 527
Flexural Stress, Yield
1.3 mm/min;50 mm;span			106 MPa			ASTM D790
2 mm/min			103 MPa			ISO 178
Flexural Modulus
1.3 mm/min;50 mm;span			2400 MPa			ASTM D790
2 mm/min			2500 MPa			ISO 178
Thermal			Nominal Value			Test Method

CFR5630
PC

 

UL Recognized
≥ 3 mm
≥ 1 mm
≥ 0.4 mm


5VA
V-0
V-2

UL 94

FAA Flammability(FAR 25.853 A/B)		Pass	FAR 25.853
Vertical Burn, A(60s passes at)		5 Seconds	FAR 25.853
Vertical Burn, B(12s passes at)		5 Seconds	FAR 25.853
NBS Smoke Density, Flaming, Dmax		< 100	ASTM E662
Glow Wire Ignition Temperature [GWIT] 3 mm 1 mm		850 °C 875 °C	IEC 60695-2-13
Glow Wire Flammability Index 3 mm 1 mm		960 °C 960 °C	IEC 60695-2-12
Oxygen Index		45 %	ISO 4589
Vicat Softening Temperature Rate B/50 Rate B/50 Rate B/120		136 °C 137 °C 139 °C	ASTM D1525 ISO 306 ISO 306
Heat Deflection Temperature[HDT], Unannealed 0.45 MPa;3.2 mm 3.2 mm;1.82 MPa		131 °C 120 °C	ASTM D648
CTE, Flow -40 - 40 °C 23°C to 80°C		6.6E-05 1/°C 7.2e-05 1/°C	ASTM E831 ISO 11359-2
CTE, XFlow -40 - 40 °C 23°C to 80°C		7.0E-05 1/°C 7.6E-05 1/°C	ASTM E831 ISO 11359-2
Ball Pressure Test(125°C +/- 2°C)		Pass	IEC 60695-10-2
HDT/Be(Edgew;120*10*4;sp =100mm; 0.45 Mpa)		131 °C	ISO 75/Be
Hdt/Ae(1.8 MPa;Edgew;120*10*4;sp =100mm)		120 °C	ISO 75/Ae
Relative Temp Index, Elec		125 °C	UL 746B
Relative Temp Index, Mechanical with Impact		120 °C	UL 746B
Relative Temp Index, Mechanical without Impact		125 °C	UL 746B
Electrical	Nominal Value			Test Method
Dielectric Constant, Dk(1.1e+9 Hz)	2.79			ASTM ES 7-83
Dissipation Factor, Df(1.1e+9 Hz)	5.8E-03			ASTM ES 7-83
Comparative Tracking Index, CTI	PLC 3			UL 746A
Hot-wire Ignition, HWI ≥ 3 mm ≥ 1 mm	PLC 2 PLC 3			UL 746A
High Amp Arc Ignition, HAI( ≥ 1 mm)	PLC 0			UL 746A
Processing				Nominal Value
Drying Temperature<Injection>				120 °C
Drying Time<Injection>				3 - 4 hrs
Drying Time, Cumulative<Injection>				48 hrs
Maximum Moisture Content<Injection>				0.02 %
Melt Temperature<Injection>				290 - 310 °C
Nozzle Temperature<Injection>				280 - 305 °C
Front, Zone 3 Temperature<Injection>				290 - 310 °C
Middle, Zone 2 Temperature<Injection>				275 - 300 °C
Rear, Zone 1 Temperature<Injection>				265 - 290 °C
Mold Temperature<Injection>				70 - 95 °C
Back Pressure<Injection>				0.3 - 0.7 MPa
Screw Speed <Injection>				40 - 70 rpm
Shot To Cylinder Size<Injection>				40 - 60 %
Vent Depth <Injection>				0.025 - 0.076 mm

 

Company Profile

Product Parameters

Our Customers

Our Certificates

 

Our Production

Our Package/Shipping

Our Advantages

 

Our Samples

 

Dongguan FOREVER Co., Ltd. Was founded in 2005 and is a national high-tech enterprise and national-level specialized giant enterprise dedicated to the research and production of polymer composite modified materials. With an annual capacity of 100, 000 tons of modified engineering plastics. Since its establishment, the company has been committed to the research of high-performance composite materials such as modified PC, PC/ABS, PBT, PA6, etc. Its products have been widely used in industries such as LED lighting, consumer electronics, new energy, security equipment, and small household appliances, providing customers with efficient delivery experience, ultimate price advantages, and strict quality assurance, contributing to the creation of a green and environmentally friendly world.

Dongguan FOREVER Co., Ltd's main products has obtained UL certification for RTI authorized temperature, outdoor weather resistance F1 and 5VA flame retardancy grades, as well as recycled-certified post-consumer low-carbon circulation products. Dongguan FOREVER Co., Ltd's products are highly recognized by customers worldwide for their reliable quality, excellent performance, and superior cost-effectiveness.

With a strong focus on research and development, Dongguan FOREVER Co., Ltd. Has established an advanced technology research and development center, equipped with state-of-the-art testing and analysis equipment and a professional R&D team that has accumulated rich experience in the field of polymer composite modified materials. Dongguan FOREVER Co., Ltd also maintains close partnerships with renowned universities and research institutions to stay at the forefront of technology and drive innovation in the industry