Improved Stiffness Fatigue Resistance Electrically Conductive Emirfi Shielding PC

• CAS No.: 942626-09-7
• Formula: C18h18bno4
• EINECS: 323.15100
• Shipping Cost: Estimated freight per unit.: about shipping cost and estimated delivery time.
• Currency: US$
• Return&refunds: You can apply for a refund up to 30 days after receipt of the products.
• Model NO.: PC 122-XH
• Material: Polycarbonates/PC
• Usage: Engineering Plastics
• Plastic Properties After Heated: Thermoplastic Plastics
• Plastic Forming Method: Injection
• Color: White
• Form: Resin Pellets
• Chemical Substances: Polycarbonate
• Processing Mode: Injection Molding/Extrusion
• UV: Fr
• Use: Electrical Appliances, Auto Parts, Office Supplies
• Certificates: ISO9001:2008.SGS.RoHS
• Transport Package: Bag
• Specification: 25KG
• Trademark: Forever
• Origin: China
• HS Code: 39081011
• Production Capacity: 50000t/Year
• Package Size: 75.00cm * 55.00cm * 15.00cm
• Package Gross Weight: 25.010kg

Product Description

Improved Stiffness Fatigue Resistance Electrically Conductive Emirfi Shielding PC 
 

Product Description

XHT2171 is a 55 MVR high flow, high heat polycarbonate copolymer enabling high aesthetics, thin wall and complex designs. It is available in a range of opaque colors.

Product Description
XHT2171 is a 55 MVR high flow, high heat polycarbonate copolymer enabling high aesthetics, thin wall and complex designs. It is available in a range of opaque colors.
General
Form                                        Resin Pellets
Feature                                     Good Thermal
Uses                                         Automotive                       Healthcare                         Electrical
Physical                                                                                 Nominal Value                                       Test Method
Density / Specific Gravity 1.2                                                         ASTM D792 1.2 g/cm³                                              ISO 1183
Mold Shrinkage, Flow(3.2 mm)                                           0.6 - 0.9 %                                               Method
Melt Flow Rate[MFR]                                                                                                                           ASTM D1238
300 °C;2.16 kgf                                                                   22 g/10min
330 °C;2.16 kgf                                                                   60 g/10min
Water Absorption(23 °C;saturated)                                    0.3 %                                                      ISO 62-1
Moisture Absorption(50% RH;23 °C)                                  0.3 %                                                       ISO 62
Melt Volume Rate, MVR                                                                                                                      ISO 1133
2.16 kg;MVR at 300 °C                                                        19 cm³/10 min
2.16 kg;330 °C                                                                     55 cm³/10 min
Hardness, Rockwell R                                                           125                                                         ISO 2039-2
Mechanical                                                                            Nominal Value                                      Test Method
Izod Impact, Unnotched                                                                                                                    ASTM D4812
23 °C                                                                                     NB J/m
-30 °C                                                                                    NB J/m
Izod Impact, Notched                                                                                                                        ASTM D256
23 °C                                                                                    80 J/m
-30 °C                                                                                   75 J/m
Unnotched Izod Impact Strength                                                                                                      ISO 180/1U
unnotched;80*10*3;23 °C 0                                                NB kJ/m²
unnotched;80*10*3;-30 °C 0                                              NB kJ/m²
Notched Izod Impact Strength notched;80*10*3;23 °C 0 notched;80*10*3;-30 °C 0	9 kJ/m² 9 kJ/m²		ISO 180/1A
C harpy Impact, V-Notched 23 °C;Edgew;80*10*3;sp =62mm 0 -30 °C;Edgew;80*10*3;sp =62mm 0	10 kJ/m² 10 kJ/m²		ISO 179 1eA
C harpy Impact, Unnotched 23 °C;Edgew;80*10*3;sp =62mm 0 -30 °C;Edgew;80*10*3;sp =62mm 0	NB kJ/m² NB kJ/m²		ISO 179 1eU
Tensile Stress, Yield
50 mm/min;Type I	73 MPa		ASTM D638
50 mm/min	74 MPa		ISO 527
Tensile Stress, Break
50 mm/min;Type I	60 MPa		ASTM D638
50 mm/min	60 MPa		ISO 527
Tensile Strain, Yield
50 mm/min;Type I	7 %		ASTM D638
50 mm/min	7 %		ISO 527
Tensile Strain, Break
50 mm/min;Type I	> 30 %		ASTM D638
50 mm/min	> 50 %		ISO 527
Tensile Modulus
5 mm/min	2450 MPa		ASTM D638
1 mm/min	2450 MPa		ISO 527
Flexural Stress, Yield
1.3 mm/min;50 mm;span	115 MPa		ASTM D790
2 mm/min	107 MPa		ISO 178
Flexural Modulus
1.3 mm/min;50 mm;span	2600 MPa		ASTM D790
2 mm/min	2400 MPa		ISO 178
Ball Indentation Hardness(H358/30)	147 MPa		ISO 2039-1
Thermal		Nominal Value		Test Method
Vicat Softening Temperature
Rate B/50		164 °C		ASTM D1525
Rate B/120		165 °C		ASTM D1525
Rate B/50		165 °C		ISO 306
Rate B/120		167 °C		ISO 306
Heat Deflection Temperature[HDT], Unannealed 0.45 MPa;3.2 mm 3.2 mm;1.82 MPa		160 °C 147 °C		ASTM D648
CTE, Flow
-40 - 40 °C		6.0E-05 1/°C		ASTM E831
-40 - 40 °C		6.0E-05 1/°C		ISO 11359-2
CTE, XFlow
-40 - 40 °C		6.0E-05 1/°C		ASTM E831
-40 - 40 °C		6.0E-05 1/°C		ISO 11359-2
Thermal Conductivity @ 25 °C		0.2 W/m-K		ASTM C177
Ball Pressure Test(125°C +/- 2°C)		PASSES		IEC 60695-10-2
HDT/Bf(0.45)		159 °C		ISO 75/Bf
HDT/Af(1.8)		146 °C		ISO 75/Af
Metallized Haze Pass At 1.5Mm		155 °C		Method
Processing				Nominal Value
Drying Temperature<Injection>				130 °C
Drying Time<Injection>				4 - 6 hrs
Maximum Moisture Content<Injection>				0.02 %
Melt Temperature<Injection>				290 - 350 °C
Nozzle Temperature<Injection>				285 - 345 °C
Front, Zone 3 Temperature<Injection>				290 - 350 °C
Middle, Zone 2 Temperature<Injection>				280 - 340 °C
Rear, Zone 1 Temperature<Injection>				270 - 330 °C
Mold Temperature<Injection>				85 - 130 °C
Back Pressure<Injection>				0.3 - 0.7 MPa
Screw Speed <Injection>				40 - 90 rpm
Shot To Cylinder Size<Injection>				40 - 60 %
Vent Depth <Injection>				0.025 - 0.08 mm

 

good quality UV-stabilized UL746 F1 F2 PC blend alloy equal to Covestro Makroblend TEIJIN Panlite Mitsubishi

With almost 20 years in the modified engineering plastics,Forever Plastics is a high-tech manufacture integrating R&D, production and sales of high-performance resin or polymer ,including PC,PP,PA6,PA66, PBT,PET, PC/ABS, PC/PBT, PC/PET alloy compounds,TPE,TPU, PE for rotomolding with the property of the flame retardant, glass fiber reinforced, high glossy, UV resistance.....with the annual output value of USD 65 million in 2021Our customers are Philips,Osram,Cree,Schneider,Siemens,etc. for years in the electrical&electronics components, Automotive parts, House appliance,LED lights.....