Audited Supplier ABS FOR projectors large MFPs coffee makers TV front and rear frames and car audio consoles
https://forever-plastics.en.made-in-china.com/product-list-1.html
| Product Description | |||||
| Features: High Flow; 1.0mm V-1; 1.5mm V-0; 1.5mm 5VB; 2.5mm 5VA (TBBA series) Applications: Displays; Chassis; Modems; Power Panels; Power Outlets; Car Batteries; Cash Register Housings; Printer enclosures; remote controls; light boxes; fax machines; projectors; large MFPs; coffee makers; TV front and rear frames and car audio consoles | |||||
| General | |||||
| Form | Resin Pellets | ||||
| Feature | Excellent Processability | ||||
| UL Yellow Card E56070-565073 | |||||
| Light Covers Printer Parts Panel | |||||
| Uses Facsimile machine parts Projector Housing Socket | |||||
Remote Controls Coffee Machine |
|||||
Physical Nominal Value Test Method |
|||||
Density / Specific Gravity(23 °C) 1. 19 g/cm³ ISO 1183 |
|||||
Melt Volume-Flow Rate, MVR(220 °C;10 kg) 58 cm³/ 10 min ISO 1133 |
|||||
Molding Shrinkage 0.30 - 0.60 % ISO 294 -4 |
|||||
Mechanical Nominal Value Test Method |
|||||
Tensile Strength, Yield(50 mm/min) 38. 0 MPa ISO 527 -2/50 |
|||||
| Tensile Strength, Break(50 mm/min) 29. 0 MPa ISO 527 -2/50 | |||||
| Tensile Elongation, Break(50 mm/min) 10 % ISO 527 -2/50 | |||||
| Flexural Modulus(2 mm/min) 1800 MPa ISO 178 | |||||
| Flexural Strength(2 mm/min) 55.0 MPa ISO 178 | |||||
| C harpy Notched Impact Strength ISO 179 | |||||
| -30 °C 10 kJ/m² | |||||
| 23 °C 22 kJ/m² | |||||
| Notched Izod Impact ISO 180/1A | |||||
| -30 °C 9.0 kJ/m² | |||||
| 23 °C 21 kJ/m² | |||||
| Thermal Nominal Value | Test Method | ||||
| Deflection Temperature Under Load, Unannealed(1.8 MPa) | 74.0 °C | ISO 75-2/A | |||
| Deflection Temperature Under Load, Annealed(1.8 MPa) | 83.0 °C | ISO 75-2/A | |||
| Vicat Softening Temperature | |||||
| 50 ºC/hr;1 kg | 78.0 °C | ISO 306/B50 | |||
| 5 kg;50 ºC/hr | 91.0 °C | ISO 306/A50 | |||
| CLTE, Flow | 8.4E-5 | ISO 11359-2 | |||
| Flame Rating 1 mm 1.5 mm 1.5 mm 2.5 mm |
V-1 V-0 5VB 5VA |
UL 94 | |||
| Processing | Nominal Value | ||||
| Drying Temperature<Injection> | 80 - 85 °C | ||||
| Drying Time<Injection> | 2.0 - 4.0 hr | ||||
| Rear Temperature<Injection> | 180 - 210 °C | ||||
| Middle Temperature<injection> | 190 - 220 °C | ||||
| Front Temperature<Injection> | 190 - 220 °C | ||||
| Mold Temperature<Injection> | 40 - 70 °C | ||||
| Injection Pressure<Injection> | 4.90 - 7.85 MPa | ||||
| Injection Rate<Injection> | Slow-Moderate | ||||
| Holding Pressure<Injection> | 1.96 - 4.90 MPa | ||||
| Back Pressure<Injection> | 0.490 - 0.981 MPa | ||||
| Cushion<Injection> | 3.18 mm | ||||