Product Description | ||||
A high-viscosity grade for general injection molding It has a high stiffness compared to general POM copolymer. | ||||
General | ||||
Form | ||||
Feature | ||||
UL Yellow Card E120354-220440 | ||||
Physical | Nominal Value | Test Method | ||
Density / Specific Gravity | 1.41 g/cm³ | ISO 1183 | ||
Melt Mass-Flow Rate, MFR(190 °C;2.16 kg) | 3.0 g/10min | ISO 1133 | ||
Molding Shrinkage, Flow(2 mm) | 2.0 % | Internal Method | ||
Water Absorption, Equilibrium(50% RH;23 °C) | 0.20 % | ISO 62 | ||
Mechanical | Nominal Value | Test Method | ||
Tensile Modulus | 2800 MPa | ISO 527-1 | ||
Tensile Stress | 67.0 MPa | ISO 527-2 | ||
Tensile Strain, Yield | 12 % | ISO 527-2 | ||
Nominal Tensile Strain at Break | 35 % | ISO 527-2 | ||
Flexural Modulus | 2600 MPa | ISO 178 | ||
Flexural Stress | 90.0 MPa | ISO 178 | ||
Charpy Notched Impact Strength -30 °C 23 °C |
6.5 kJ/m² 8.5 kJ/m² |
ISO 179/1eA | ||
Thermal | Nominal Value | Test Method | ||
Deflection Temperature Under Load, Unannealed(1.8 MPa) | 100 °C | ISO 75-2/A | ||
Melting Temperature | 170 °C | ISO 11357-3 | ||
CLTE, Flow | 1.2E-4 cm/cm/°C | ISO 11359-2 | ||
Flame Rating | HB | UL 94 | ||
Electrical | Nominal Value | Test Method | ||
Surface Resistivity | 1.0E+16 ohms | IEC 60093 | ||
Volume Resistivity | 1.0e+14 ohms·cm | IEC 60093 | ||
Electric Strength | 19 kV/mm | IEC 60243-1 |
Product Description | ||||
A semi-conductive grade of acetal copolymer for applications requiring rapid dissipation of static build- up.Information provided by Celanese Corporation. | ||||
General | ||||
Form | Resin | Pellets | ||
Physical | Nominal Value | Test Method | ||
Density / Specific Gravity | 1.40 g/cm³ | |||
Water Absorption | 0.21 % | ASTM D570 | ||
Moisture Absorption at Equilibrium | 0.80 % | ASTM D570 | ||
Linear Mold Shrinkage | 2.2 % | |||
Linear Mold Shrinkage, Transverse | 1.8 % | |||
Hardness, Rockwell R | 111 | ASTM D785 | ||
Mechanical | Nominal Value | Test Method | ||
Tensile Strength, Yield | 37.0 MPa | ASTM D638 | ||
Elongation at Break | 30 % | ASTM D638 | ||
Flexural Strength | 52.0 MPa | ASTM D790 | ||
Flexural Modulus | 2100 MPa | ASTM D790 | ||
Compressive Strength | 66.0 MPa | ASTM D695 | ||
Shear Strength | 40.0 MPa | ASTM D732 | ||
Izod Impact, Notched Temperature; 23 °C Temperature; -29 °C |
50 J/m 30 J/m |
ASTM D256 | ||
Thermal | Nominal Value | Test Method | ||
Deflection Temperature Pressure; 0.46 MPa Pressure; 1.8 MPa |
152 °C 106 °C |
ASTM D648 | ||
Flammability, UL94 | HB | UL 94 |