Plastics Raw Materials Thermal Conductive Plastics PA6 for LED Light Lamp

• Material: Plastic
• Adjustable: Adjustable
• Application: Office Chair
• Shipping Cost: Estimated freight per unit.: about shipping cost and estimated delivery time.
• Currency: US$
• Return&refunds: You can apply for a refund up to 30 days after receipt of the products.
• Model NO.: PA6-3-8097 VPXH
• Name: PA6 with 30% Glass Fiber
• Features: High Strength, Good Mechanical Property,Dimensiona
• Used: Automobiles, Machine Parts,Power Tools,Sport Equip
• Applications: Outer Casing;Auto Parts
• Material Shape: Granules
• Performance: Reinforce PA
• Transport Package: 25kg/Bag
• Specification: 500G30
• Trademark: FOREVER
• Origin: China
• HS Code: 3909101000
• Production Capacity: 80000t/Year
• Package Size: 75.00cm * 55.00cm * 15.00cm
• Package Gross Weight: 25.010kg

Product Description

Dongguan Forever Co., Ltd. is the manufacture for the plastics raw materials, like PC,PP,PA6,PA66, PBT,PC/ABS, PC/PBT alloy granules, including the flame retardant, glass fiber reinforced, high glossy, UV resistance.....especially the modified compound for LED lights diffusing polycarbonate PC and flame retardant polybutylece terephthalate PBT,light guide polycarbonate,flame retardant V0/5VA polycarbonate,pcabs alloy, PCR.

 

Our customers are Philips, Osram, Cree, GE,SIEMENS, etc. for years in the LED light bulbs, tubes, heat sinks,profiles

 

Our thermoplastics polymers are compliant with RoHS and REACH, UL94,UL726 F1/F2, ISO9001,TSCA certification (for example PC RTI 130ºC, and PBT RTI 140ºC). 

ITEM NO: 3-8097 VP-XH
 

Product Description
3-8097 VP-XH type PA6 resin can make strong, hard parts. Isotropic shrinkage properties. Inherently flame retardant. Application areas: Automotive industry, textile machinery, instruments and precision engineering. Typical parts: Electrical and electronic industry parts.
General
Form                                        Resin Pellets
Feature	Thermally   Conductive(Isolation)
Physical		Nominal Value	Test Method
Density / Specific Gravity		1.56 g/cm³	ISO 1183
Linear Mold Shrinkage		0.2 - 0.5 %
Mechanical		Nominal Value	Test Method
Tensile Strength		140 MPa
Elongation at Break		1.60 %
Modulus of Elasticity		1.6E+4 MPa
Flexural Strength(Strain 2.1 %)		215 MPa
Flexural Modulus		1.4E+4 MPa
C harpy Impact Unnotched(23 °C)		30 kJ/m²	ISO 179 1eU
Thermal		Nominal Value	Test Method
Thermal Conductivity, In Plane(Hot Disk;Parallel 60x60x3 3.50 W/m-K mm)
Maximum Service Temperature, Air
Continuous		90.0 °C
Short Term		210 °C
Deflection Temperature(Pressure; 1.8 MPa)		200 °C
Electrical		Nominal Value	Test Method
Volume Resistivity(10V)		> = 1.00e+6 ohms ·cm
Surface Resistance(10 V)		> = 1.00e+6 Ohms

Processing	Nominal Value
Nozzle Temperature	270 - 280 °C
Zone 1	250 - 270 °C
Barrel - Zone 2 Temperature	270 - 290 °C
Barrel - Zone 3 Temperature	280 - 300 °C
Melt Temperature	270 °C
Mold Temperature	70.0 - 110 °C
Drying Temperature
Time 10 - 16 hr	75.0 °C
Time 4 - 6 hr	105 °C