Ultradur B 4406 G4 is an injection molding grade with 20 % glass fibers for parts requiring enhanced fire resistance (eg relay housings, plug-and-socket connectors, switches, lighting components). Applications Typical applications include relay housings, plug-and-socket connectors, switches, and lighting components. |
|||||
General | |||||
Form | Resin Pellets | ||||
Filler | 20 % Glass Fiber | ||||
Feature | |||||
UL Yellow Card | E41871-233789 | ||||
Uses |
Lighting Applications Housing | Switches Connector | |||
Physical | Nominal Value | Test Method | |||
Density / Specific Gravity | 1.55 g/cm³ | ASTM D792;ISO 1183 | |||
Melt Volume-Flow Rate, MVR(250 °C;2.16 kg) | 11 cm³/10 min | ISO 1133 | |||
Molding Shrinkage, Flow(3.18 mm) | 0.30 % | No Standard | |||
Water Absorption, Saturation | |||||
0.40 % | ASTM D570 | ||||
23 °C | 0.40 % | ISO 62 | |||
Water Absorption, Equilibrium | |||||
50% RH | 0.20 % | ASTM D570 | |||
50% RH;23 °C | 0.20 % | ISO 62 | |||
Viscosity Number, Reduced Viscosity | 112.0 ml/g | ISO 1628 | |||
Mechanical | Nominal Value | Test Method | |||
Tensile Modulus(23 °C) | 8200 MPa | ISO 527-2 | |||
Tensile Strength, Break | |||||
23 °C | 117 MPa | ASTM D638 | |||
23 °C | 125 MPa | ISO 527-2 | |||
Tensile Elongation, Break | |||||
23 °C | 2.2 % | ASTM D638 | |||
23 °C | 2.6 % | ISO 527-2 | |||
C harpy Notched Impact Strength(23 °C) | 9.0 kJ/m² | ISO 179 | |||
C harpy Unnotched Impact Strength(23 °C) | 48 kJ/m² | ISO 179 | |||
Notched Izod Impact(23 °C) | 53 J/m | ASTM D256 | |||
Thermal | Nominal Value | Test Method | |||
Deflection Temperature Under Load, Unannealed 0.45 MPa 1.8 MPa 0.45 MPa 1.8 MPa |
215 °C 177 °C 223 °C 200 °C |
ASTM D648 ASTM D648 ISO 75-2/B ISO 75-2/A |
|||
Peak Melting Temperature | 223 °C | ASTM D3418;ISO 3146 | |||
CLTE, Flow | 3.0E-5 cm/cm/°C 5.0E-5 cm/cm/°C |
ASTM E831 No Standard |
|||
RTI Elec 0.75 mm 1.5 mm 3 mm |
140 °C 140 °C 140 °C |
UL 746 | |||
RTI Imp 0.75 mm 1.5 mm 3 mm |
120 °C 120 °C 120 °C |
UL 746 | |||
RTI Str 0.75 mm 1.5 mm 3 mm |
125 °C 130 °C 130 °C |
UL 746 | |||
Flame Rating 0.4 mm 0.75 mm 1.5 mm 3 mm |
V-0 V-0 V-0 V-0 |
UL 94 | |||
Electrical | Nominal Value | Test Method | |||
Volume Resistivity 1.5 mm |
> 1.0E+15 Ohms ·cm > 1.0E+15 Ohms ·cm |
ASTM D257 IEC 60093 |
|||
Dielectric Constant 100 Hz 1.0e+6 Hz |
3.90 3.60 |
IEC 60250 | |||
Dissipation Factor 100 Hz 1.0e+6 Hz |
7.0E-3 0.017 |
IEC 60250 | |||
Comparative Tracking Index | 200 V | IEC 60112 | |||
Processing | Nominal Value | ||||
Drying Temperature<Injection> | 100 - 120 °C | ||||
Drying Time<Injection> | 4.0 hr | ||||
Suggested Max Moisture<Injection> | 0.040 % | ||||
Processing Temp, Melt<Injection> | 250 - 270 °C | ||||
Mold Temperature<Injection> | 60 - 100 °C | ||||
Injection Pressure<Injection> | 3.50 - 12.5 MPa | ||||
Injection Rate<Injection> | Fast | ||||
Back Pressure<Injection> | < 1.00 MPa |