The C7230P-XH resin is a type of plastic made from a combination of polycarbonate (PC) and acrylonitrile butadiene styrene (ABS), and it contains minerals that enhance its properties. This resin is designed to be flame retardant. It offers a good combination of rigidity, smooth flow, and resistance to impact, which makes it suitable for a wide range of uses.
General |
||||
Form |
Resin Pellets |
|||
Filler |
Mineral |
|||
Feature |
Enhanced Stiffness |
|||
Usage Electronic Displays NoteBook Computer |
||||
Physical |
Nominal Value |
Test Method |
||
Density / Specific Gravity |
1.30 g/cm³ |
|||
Melt Mass-Flow Rate, MFR(260 °C;2.16 kg) |
13 g/10min |
ASTM D1238 |
||
Melt Volume-Flow Rate, MVR(260 °C;2.16 kg) |
9.00 cm³/10 min |
ISO 1133 |
||
Molding Shrinkage, Flow(3.2 mm) |
0.25 - 0.35 % |
Internal Method |
||
Water Absorption, Saturation(23 °C) |
0.090 % |
ISO 62 |
||
Water Absorption, Equilibrium(50% RH;23 °C) |
0.040 % |
ISO 62 |
Mechanical |
Nominal Value |
Test Method |
Tensile Modulus |
||
5 mm/min |
5200 MPa 5580 MPa |
ASTM D638 ISO 527-2/1 |
Tensile Strength, Yield |
||
50 mm/min;Type I |
58.0 MPa 55.0 MPa |
ASTM D638 ISO 527-2/50 |
Tensile Strength, Break |
||
50 mm/min;Type I |
45.0 MPa 35.0 MPa |
ASTM D638 ISO 527-2/50 |
Tensile Elongation, Yield |
||
50 mm/min;Type I |
4.0 % 3.8 % |
ASTM D638 ISO 527-2/50 |
Tensile Elongation, Break |
||
50 mm/min;Type I |
32 % 30 % |
ASTM D638 ISO 527-2/50 |
Flexural Modulus |
||
1.3 mm/min;50 mm;Span |
4530 MPa |
ASTM D790 |
2 mm/min |
4580 MPa |
ISO 178 |
Flexural Stress, at Yield(2 mm/min) |
99.0 MPa |
ISO 178 |
Flexural Stress, Yield(1.3 mm/min;50 mm;Span) |
98.0 MPa |
ASTM D790 |
C harpy Notched Impact Strength(23 °C;80*10*4;sp =62mm 0) |
5.0 kJ/m² |
ISO 179 1eA |
Notched Izod Impact |
||
-30 °C |
55 J/m |
ASTM D256 |
23 °C |
69 J/m |
ASTM D256 |
80*10*4 mm;-30 °C |
5.0 kJ/m² |
ISO 180/1A |
80*10*4 mm;23 °C |
5.0 kJ/m² |
ISO 180/1A |
Instrumented Dart Impact, Total Energy(23 °C) |
0.00 J |
ASTM D3763 |
Thermal |
Nominal Value |
Test Method |
Deflection Temperature Under Load, Unannealed |
||
1.8 MPa;3.2 mm |
88.0 °C |
ASTM D648 |
80*10*4 mm;1.8 MPa;4 mm;64 mm;Span |
89.0 °C |
ISO 75-2/Af |
Vicat Softening Temperature |
||
50 °C/h;50 N;Rate A;Loading 2 |
108 °C 107 °C 110 °C |
ASTM D1525 ISO 306/B50 ISO 306/B120 |
CLTE, Flow(-40 - 40 °C) |
4.2E-5 cm/cm/°C |
|
CLTE, Transverse |
||
-40 - 40 °C |
4.9E-5 cm/cm/°C |
ASTM E831 |
-40 °C |
5.9E-5 cm/cm/°C |
ISO 11359-2 |
Flame Rating 1.2 mm 2 mm |
V-0 5VB |
UL 94 |
Processing |
Nominal Value |
|
Drying Temperature<Injection> |
80 - 90 °C |
|
Drying Time<Injection> |
3.0 - 4.0 hr |
|
Suggested Max Moisture<Injection> |
0.040 % |
|
Suggested Shot Size<Injection> |
30 - 80 % |
|
Rear Temperature<Injection> |
220 - 255 °C |
|
Middle Temperature<injection> |
220 - 265 °C |
|
Front Temperature<Injection> |
245 - 275 °C |
|
Nozzle Temperature<Injection> |
245 - 275 °C |
|
Processing Temp, Melt<Injection> |
245 - 275 °C |
|
Mold Temperature<Injection> |
60 - 80 °C |
|
Back Pressure<Injection> |
0.300 - 0.700 MPa |
|
Screw Speed <Injection> |
40 - 70 rpm |
|
Vent Depth <Injection> |
0.038 - 0.076 mm |