Product Description | |||
XHT4143 is a high flow, UV stabilized, high heat polycarbonate copolymer blend with an HDT/Af of 162C. | |||
General | |||
Form Resin Pellets | |||
Feature Good Thermal Outdoor | |||
Uses Automotive | |||
Physical Nominal Value Test Method | |||
Density / Specific Gravity 1.2 ASTM D792 1.21 g/cm³ ISO 1183 |
|||
Mold Shrinkage, Flow(3.2 mm) 0.6 - 0.95 % Method | |||
Melt Flow Rate[MFR](330 °C;2.16 kgf) 25 g/10min ASTM D1238 | |||
Water Absorption(23 °C;saturated) 0.33 % ISO 62-1 | |||
Moisture Absorption(50% RH;23 °C) 0.25 % ISO 62 | |||
Melt Volume Rate, MVR(2.16 kg;330 °C) 24 cm³/10 min ISO 1133 | |||
Mechanical Nominal Value Test Method | |||
Izod Impact, Notched ASTM D256 | |||
23 °C 93 J/m | |||
-30 °C 76 J/m | |||
Instrumented Dart Impact, Total Energy(23 °C) 72 J ASTM D3763 | |||
Unnotched Izod Impact Strength ISO 180/1U | |||
unnotched;80*10*3;23 °C 0 NB kJ/m² | |||
unnotched;80*10*3;-30 °C 0 NB kJ/m² | |||
Notched Izod Impact Strength ISO 180/1A | |||
notched;80*10*3;23 °C 0 10 kJ/m² | |||
notched;80*10*3;-30 °C 0 8 kJ/m² | |||
C harpy Impact, V-Notched ISO 179 1eA | |||
23 °C;Edgew;80*10*3;sp =62mm 0 11 kJ/m² | |||
-30 °C;Edgew;80*10*3;sp =62mm 0 9 kJ/m² | |||
C harpy Impact, Unnotched ISO 179 1eU | |||
23 °C;Edgew;80*10*3;sp =62mm 0 NB kJ/m² | |||
-30 °C;Edgew;80*10*3;sp =62mm 0 NB kJ/m² | |||
Tensile Stress, Yield | |||
50 mm/min;Type I | 77 MPa | ASTM D638 | |
50 mm/min | 78 MPa | ISO 527 | |
Tensile Stress, Break | |||
50 mm/min;Type I | 69 MPa | ASTM D638 | |
50 mm/min | 67 MPa | ISO 527 | |
Tensile Strain, Yield | |||
50 mm/min;Type I | 7 % | ASTM D638 | |
50 mm/min | 7 % | ISO 527 | |
Tensile Strain, Break | |||
50 mm/min;Type I | 50 % | ASTM D638 | |
50 mm/min | 50 % | ISO 527 | |
Tensile Modulus | |||
5 mm/min | 2730 MPa | ASTM D638 | |
1 mm/min | 2750 MPa | ISO 527 | |
Flexural Stress, Yield | |||
1.3 mm/min;50 mm;span | 120 MPa | ASTM D790 | |
2 mm/min | 80 MPa | ISO 178 | |
Flexural Modulus | |||
1.3 mm/min;50 mm;span | 2600 MPa | ASTM D790 | |
2 mm/min | 2600 MPa | ISO 178 | |
Thermal | Nominal Value | Test Method | |
Glow Wire Flammability Index 2 mm 2.5 mm |
850 °C 960 °C |
IEC 60695-2-12 | |
Vicat Softening Temperature | |||
Rate B/50 | 183 °C | ASTM D1525 | |
Rate B/50 | 183 °C | ISO 306 | |
Rate B/120 | 181 °C | ISO 306 | |
Heat Deflection Temperature[HDT], Unannealed 0.45 MPa;3.2 mm 3.2 mm;1.82 MPa |
174 °C 165 °C |
ASTM D648 | |
CTE, Flow | |||
-40 - 40 °C | 6.0E-05 1/°C | ASTM E831 | |
-40 - 40 °C | 6.0E-05 1/°C | ISO 11359-2 | |
CTE, XFlow | |||
-40 - 40 °C | 6.0E-05 1/°C | ASTM E831 | |
-40 - 40 °C | 6.0E-05 1/°C | ISO 11359-2 | |
Ball Pressure Test(165°C +/- 2°C) | PASSES | IEC 60695-10-2 | |
HDT/Bf(0.45) | 173 °C | ISO 75/Bf | |
HDT/Af(1.8) | 162 °C | ISO 75/Af | |
Optical | Nominal Value | Test Method | |
Light Transmission(2.54 mm) | 86 % | ASTM D1003 | |
Haze(2.54 mm) | 0.5 % | ASTM D1003 | |
Refractive Index | 1.605 | ASTM D542 | |
Processing | Nominal Value | ||
Drying Temperature<Injection> | 135 °C | ||
Drying Time<Injection> | 4 - 6 hrs | ||
Maximum Moisture Content<Injection> | 0.02 % | ||
Melt Temperature<Injection> | 290 - 325 °C | ||
Nozzle Temperature<Injection> | 295 - 310 °C | ||
Front, Zone 3 Temperature<Injection> | 300 - 315 °C | ||
Middle, Zone 2 Temperature<Injection> | 290 - 305 °C | ||
Rear, Zone 1 Temperature<Injection> | 280 - 295 °C | ||
Mold Temperature<Injection> | 95 - 130 °C | ||
Back Pressure<Injection> | 0.3 - 0.7 MPa | ||
Screw Speed <Injection> | 40 - 90 rpm | ||
Shot To Cylinder Size<Injection> | 40 - 60 % | ||
Vent Depth <Injection> | 0.025 - 0.08 mm |