Nylon 6 resin containing mineral and glass fiber Heat-Conducting Nylon66
https://forever-plastics.en.made-in-china.com/product/rJwRvlcdZpWD/China-Nylon-PA6-GF33-PA66-Granules-PA6-with-30GF-Polyamide-PA66-30-GF-PA6-Material.html Heat-conducting nylon
Product Description | |||||
PX13322 compound is based on Nylon 6 resin containing mineral and glass fiber. Added features of this grade include: Thermally Conductive, Electrically Insulative and Non-Brominated, Non-Chlorinated Flame Retardant. | |||||
General | |||||
Form | Resin Pellets | ||||
Filler | |||||
Feature |
Thermally Conductive | Non-Brominated & Non- | Non-Chlorinated Electrically Isolative |
||
Chlorinated Flame R t d t |
|||||
UL Yellow Card | E207780 - 101694795 | ||||
Uses |
Consumer Industria Building and Construction |
Electrical | |||
Physical | Nominal Value | Test Method | |||
Density / Specific Gravity | 1.69 g/cm³ | ASTM D792 | |||
Mold Shrinkage, Flow(24 hrs) | 0.54 % | ASTM D955 | |||
Mold Shrinkage, XFlow(24 hrs) | 0.57 % | ASTM D955 | |||
Water Absorption(24 hrs;23 °C) | 0.06 % | ISO 62-1 |
Mechanical | Nominal Value | Test Method |
Izod Impact, Unnotched | ||
23 °C | 235 J/m | ASTM D4812 |
80*10*4;23 °C | 16 kJ/m² | ISO 180/1U |
Izod Impact, Notched | ||
23 °C | 21 J/m | ASTM D256 |
80*10*4;23 °C | 3 kJ/m² | ISO 180/1A |
Tensile Stress, Break | ||
5 mm/min;Type I | 77 MPa | ASTM D638 |
5 mm/min | 78 MPa | ISO 527 |
Tensile Strain, Break | ||
5 mm/min;Type I | 0.7 % | ASTM D638 |
5 mm/min | 0.8 % | ISO 527 |
Tensile Modulus | ||
5 mm/min | 1.4E+04 MPa | ASTM D638 |
1 mm/min | 1.3E+04 MPa | ISO 527 |
Flexural Stress, break | ||
1.3 mm/min;50 mm;span | 127 MPa | ASTM D790 |
2 mm/min | 128 MPa | ISO 178 |
Flexural Modulus | ||
1.3 mm/min;50 mm;span | 1.1E+04 MPa | ASTM D790 |
2 mm/min | 1.2E+04 MPa | ISO 178 |
Thermal | Nominal Value | Test Method |
UL Recognized(≥ 0.8 mm) | V-0 | UL 94 |
Glow Wire Ignition Temperature [GWIT] 1 mm 3 mm |
800 °C 850 °C |
IEC 60695-2-13 |
Glow Wire Flammability Index 1 mm 3 mm |
960 °C 960 °C |
IEC 60695-2-12 |
Heat Deflection Temperature[HDT](0.45 MPa;3.2 mm) | 205 °C | ASTM D648 |
Heat Deflection Temperature[HDT], Unannealed(1.82 MPa;6.4 mm) | 174 °C | ASTM D648 |
CTE, Flow -40 - 40 °C 40°C to 120°C |
3.1E-05 1/°C 2.3E-05 1/°C |
ASTM E831 |
CTE, XFlow -40 - 40 °C 40°C to 120°C |
4.8E-05 1/°C 5.3E-05 1/°C |
ASTM E831 |
Thermal conductivity through plane 60*60*3mm plaque 10*10*3mm sample |
1 W/m-K 2 W/m-K |
ISO 22007-2 ASTM E1461-07 |
Thermal conductivity in plane 60*60*3mm plaque 25*0.4mm disc |
3.3 W/m-K 3.4 W/m-K |
ISO 22007-2 ASTM E1461-07 |
HDT/Bf(0.45) | 204 °C | ISO 75/Bf |
HDT/Af(1.8) | 162 °C | ISO 75/Af |
Relative Temp Index, Elec | 65 °C | UL 746B |
Relative Temp Index, Mechanical with Impact | 65 °C | UL 746B |
Relative Temp Index, Mechanical without Impact | 65 °C | UL 746B |
Electrical | Nominal Value | Test Method |
Surface Resistivity | > 1.E+15 ohms | ASTM D257 |
Dielectric Strength, in Oil(1 mm) | > 10 kV/mm | ASTM D149 |
Dielectric Constant, Dk(1.1e+9 Hz) | 4.86 | ASTM ES 7-83 |
Dissipation Factor, Df(1.1e+9 Hz) | 0.0103 | ASTM ES 7-83 |
Comparative Tracking Index | 600 V | IEC 60112 |
Hot-wire Ignition, HWI ≥ 1 mm ≥ 0.8 mm |
PLC 0 PLC 1 |
UL 746A |
High Amp Arc Ignition, HAI( ≥ 0.8 mm) | PLC 0 | UL 746A |
Processing | Nominal Value | |
Drying Temperature<Injection> | 80 °C | |
Drying Time<Injection> | 4 hrs | |
Maximum Moisture Content<Injection> | 0.15 - 0.25 % | |
Melt Temperature<Injection> | 270 - 295 °C | |
Front, Zone 3 Temperature<Injection> | 270 - 290 °C | |
Middle, Zone 2 Temperature<Injection> | 270 - 290 °C | |
Rear, Zone 1 Temperature<Injection> | 260 - 275 °C | |
Mold Temperature<Injection> | 85 - 100 °C | |
Back Pressure<Injection> | 0.2 - 0.3 MPa | |
Screw Speed <Injection> | 20 - 60 rpm |