PA6 25% Mineral Reinforced Heat Stabilized Flame Retardant (halogen free) Nylon 6

• Feature: Oxidative Degradable
• CAS No.: 32131-17-2
• Formula: (C12h22n2o2)N
• Shipping Cost: Estimated freight per unit.: about shipping cost and estimated delivery time.
• Currency: US$
• Return&refunds: You can apply for a refund up to 30 days after receipt of the products.
• Model NO.: PA6-K222-KMV5
• EINECS: 211-024-8
• Material: Polyamide(Nylon 6.66)/PA
• Usage: General Plastics, Engineering Plastics, Specialty Plastics
• Plastic Properties After Heated: Thermoplastic Plastics
• Plastic Forming Method: Injection
• Color: Black
• Form: Resin Pellets
• Chemical Substances: Nylon
• Processing Mode: Injection Molding/Extrusion
• UV: Fr
• Use: Electrical Appliances, Auto Parts, Office Supplies
• Certificates: ISO9001:2008.SGS.RoHS
• Filler: 10%-50% Glass Fiber
• Transport Package: Bag
• Specification: 25KG
• Trademark: Forever
• Origin: China
• HS Code: 390740000
• Production Capacity: 50000t/Year
• Package Size: 75.00cm * 55.00cm * 15.00cm
• Package Gross Weight: 25.010kg

Product Description

PA6 25% Mineral Reinforced Heat Stabilized Flame Retardant (halogen free) Nylon 6
 Heat-conducting nylon

Product Description

Product Description
25% Mineral Reinforced, Heat Stabilized, Flame Retardant (halogen free)
General
Form	Resin Pellets
Filler	25 % Mineral
Feature	Non-Brominated & Non- Chlorinated Flame   Retardant			Good Thermal
UL Yellow Card                         E47960-257448
Physical			Nominal Value		Test Method
Density, dry			1.38 g/cm³		ISO 1183
Dry: Molding Shrinkage, Across Flow			0.82 %		ISO 294-4
Dry: Molding Shrinkage, Flow			0.91 %		ISO 294-4
Dry: Water Absorption, Saturation(23 °C)			6.2 %		ISO 62
Dry: Water Absorption, Equilibrium(50% RH;23 °C)			1.8 %		ISO 62
Mechanical			Nominal Value		Test Method
Dry: Tensile Modulus			6000 MPa		ISO 527-2
Condition: Tensile Modulus			2500 MPa		ISO 527-2
Dry: Tensile Stress, Break			65.0 MPa		ISO 527-2
Condition: Tensile Stress, Break			35.0 MPa		ISO 527-2
Dry: Tensile Strain, Break			2.5 %		ISO 527-2
Condition: Tensile Strain, Break			30 %		ISO 527-2
Dry: Charpy Notched Impact Strength -30 °C 23 °C			2.0 kJ/m² 2.0 kJ/m²		ISO 179 1eA
Dry: Charpy Unnotched Impact Strength -30 °C 23 °C			25 kJ/m² 29 kJ/m²		ISO 179 1eU
Thermal		Nominal Value				Test Method
Dry: Heat Deflection Temperature, Unannealed 0.45 MPa 1.8 MPa		205 °C 110 °C				ISO 75-2/B ISO 75-2/A
Dry: Melting Temperature(10 °C/min)		220 °C				ISO 11357-3
Dry: CLTE, Flow		5.0E-5 cm/cm/°C				ISO 11359-2
Dry: CLTE, Transverse		5.0E-5 cm/cm/°C				ISO 11359-2
Dry: Flammability Classification 0.75 mm 1.5 mm		V-2 V-2				IEC 60695-11-10, - 20
Dry: Glow Wire Flammability Index 0.75 mm 3 mm		960 °C 960 °C				IEC 60695-2-12
Dry: Glow Wire Ignition Temperature 0.75 mm 3 mm		700 °C 725 °C				IEC 60695-2-13
Electrical		Nominal Value				Test Method
Condition: Surface resistivity		> 1.0E+15 Ohms				IEC 60093
Dry: Volume Resistivity		> 1.0E+15 Ohms ·cm				IEC 60093
Condition: Comparative Tracking Index		600 V				IEC 60112

 

                                                                                                                  Forever Co.,Ltd

 

With almost 20 years in the modified engineering plastics,Forever Plastics is a high-tech manufacture integrating R&D, production and sales of high-performance resin or polymer ,including PC,PP,PA6,PA66, PBT,PET, PC/ABS, PC/PBT, PC/PET alloy compounds,TPE,TPU, PE for rotomolding with the property of the flame retardant, glass fiber reinforced, high glossy, UV resistance.....with the annual output value of USD 65 million in 2021. 