| Customization: | Available |
|---|---|
| Feature: | Plastics |
| CAS No.: | 25766-59-0 |
|
Still deciding? Get samples of US$ 1/kg
Order Sample
|
| Shipping Cost: | Contact the supplier about freight and estimated delivery time. |
|---|
| Payment methods: |
|
|---|---|
| Support payment in USD |
| Secure payments: | Every payment you make at Made-in-china.com is protected by the platform. |
|---|
| Refund policy: | Claim a refund if your order doesn't ship, is missing, or arrives with product issues. |
|---|
Suppliers with verified business licenses
Audited Supplier Audited by an independent third-party inspection agency
high gloss high rigidity ABS good flexural strength telephone casing lamp holder toys
https://forever-plastics.en.made-in-china.com/product-list-1.html
| Product Description | |||||
| Features: high gloss; high rigidity; good flexural strength Application: telephone casing; lamp holder; toys; office supplies; clock casing; small appliances | |||||
| General | |||||
| Form | Resin Pellets | ||||
| Feature | High Mechanical Strength And Rigidity | High Reflection Ductile | |||
| Light Covers Toys | White Goods & Small A li | ||||
| Uses | pp ances | ||||
| Office supplies Telephone | |||||
| Physical Nominal Value | Test Method | ||||
| Melt Volume Rate, MVR | ISO 1133 | ||||
| 5 kg;200 ºC 2.1 cm³/10 min | |||||
| 220 ºC;10 kg 22 cm³/10 min | |||||
| Hardness, Rockwell R 105 | ASTM D785 | ||||
| Density / Specific Gravity(23 ºC) 1.04 g/cm³ | ISO 1183 | ||||
| Mechanical Nominal Value | Test Method | ||||
| Tensile Strength(50 mm/min) 48 MPa | ISO 527 | ||||
| Elongation at Break(50 mm/min) 15 % | ISO 527 | ||||
| Flexural Strength(2 mm/min) 78 MPa | ISO178 | ||||
| Flexural Modulus(2 mm/min) 2300 MPa | ISO178 | ||||
| Notched Izod Impact Strength(23 ºC;4 mm) 14 kJ/m² | ISO 180 | ||||
| C harpy impact strength(23 ºC;4 mm) 15 kJ/m² | ISO 179 | ||||
| Thermal Nominal Value | Test Method | ||||
| Vicat Softening Temperature(10 N;50 ºC/hr) 104 °C | ISO 306 | ||||
| Deflection Temperature Under Load, Annealed(1.8 MPa) 95 °C | ISO 75-2 | ||||
| Deflection Temperature Under Load, Unannealed(1.8 MPa) | 80 °C | ISO 75-2 | |||
| Flammability(1.5 mm) HB | UL-94 | ||||
| Processing | Nominal Value | ||||
| Drying Temperature<Injection> | 80 - 85 °C | ||||
| Drying Time<Injection> | 2.0 - 4.0 hr | ||||
| Rear Temperature<Injection> | 190 - 230 °C | ||||
| Middle Temperature<injection> | 190 - 230 °C | ||||
| Front Temperature<Injection> | 180 - 220 °C | ||||
| Mold Temperature<Injection> | 30 - 70 °C | ||||
| Injection Pressure<Injection> | 4.90 - 6.86 MPa | ||||
| Holding Pressure<Injection> | 3.92 - 5.88 MPa | ||||
| Back Pressure<Injection> | 0.490 - 1.47 MPa | ||||