Good Wear Resistance POM for Fire Hoses Barrels Cases Fountain Pens

• Feature: Resin Pellets
• CAS No.: 25037-45-0
• Formula: 25037-45-0
• Shipping Cost: Estimated freight per unit.: about shipping cost and estimated delivery time.
• Currency: US$
• Return&refunds: You can apply for a refund up to 30 days after receipt of the products.
• Model NO.: POM-C0304
• EINECS: 25037-45-0
• Material: Polyacetal/POM
• Usage: Engineering Plastics
• Plastic Properties After Heated: Thermoplastic Plastics
• Plastic Forming Method: Injection
• Color: White
• Place of Origin: Guangdong, China
• Use: Fully Automatic Coffee Brewers; Knife Handles
• Features: Lubricated, Good Wear Resistance, Low Friction and
• Application: Zippers Irish Flutes, Bagpipes, Practice Chanters
• Transport Package: Bag
• Specification: 25KG
• Trademark: Forever
• Origin: China
• HS Code: 390740000
• Production Capacity: 50000t/Year
• Package Size: 75.00cm * 50.00cm * 15.00cm
• Package Gross Weight: 25.000kg

Product Description

Company Profile

 

Good Wear Resistance POM  for fire hoses barrels cases for fountain pens Celanese  c0304


 

Product Parameters

 

Product Description
POM copolymerInformation provided by forever
General
Form	Resin Pellets
Physical		Nominal Value		Test Method
Density / Specific Gravity		1.40 g/cm³		ISO 1183
Water Absorption at Saturation		0.650 %		ISO 62
Linear Mold Shrinkage, Flow		1.85 %		ISO 294-4
Linear Mold Shrinkage, Transverse		1.75 %		ISO 294-4
Melt Volume-Flow Rate, MVR(2.16		kg;190 °C;cm3/10min)26.0 cm³/10 min		ISO 1133
Mechanical		Nominal Value		Test Method
Tensile Strength, Yield		56.0 MPa		ISO 527-2/1A
Elongation at Break			45.0 %
Elongation at Yield			8.00 %	ISO 527-2/1A
Tensile Modulus			2600 MPa	ISO 527-2/1A
Flexural Modulus			2350 MPa	ISO 178
Charpy Impact Unnotched Temperature; 23 °C Temperature; -30 °C			150 kJ/m² 145 kJ/m²	ISO 179 1eU
Charpy Impact, Notched Temperature; 23 °C Temperature; -30 °C			5.5 kJ/m² 5.5 kJ/m²	ISO 179 1eA
Thermal			Nominal Value	Test Method
CTE, Flow			140 µm/m-°C	ISO 11359-2
CLTE, Transverse			140 µm/m-°C	ISO 11359-2
Melting Point(10°C/min)			166 °C	ISO 11357-1/-2/-3
Deflection Temperature(Pressure; 1.8 MPa)			90.0 °C	ISO 75-1/-2

 

Processing	Nominal Value
Processing Temperature	80.0 - 120 °C 190 - 200 °C
Feed Temperature	60.0 - 80.0 °C
Middle Barrel Temperature	20.0 - 30.0 °C
Zone 1	170 - 175 °C
Barrel - Zone 2 Temperature	180 - 185 °C
Barrel - Zone 3 Temperature	180 - 195 °C
Zone 4 Temperature	180 - 200 °C
Die Temperature	190 - 200 °C
Melt Temperature	180 - 200 °C
Drying Temperature	120 - 140 °C
Dry Time	3.00 - 4.00 hour
Moisture Content	< = 0.150 %
Injection Pressure	60.0 - 120 MPa
Hold Pressure	60.0 - 120 MPa
Back Pressure	< = 4.00 MPa
Screw Speed Diameter 55 mm Diameter 40 mm Diameter 25 mm	70.0 rpm 100 rpm 150 rpm

Detailed Photos

Packaging & Shipping

Dongguan FOREVER Co., Ltd. Was founded in 2005 and is a national high-tech enterprise and national-level specialized giant enterprise dedicated to the research and production of polymer composite modified materials. With an annual capacity of 100, 000 tons of modified engineering plastics. Since its establishment, the company has been committed to the research of high-performance composite materials such as modified PC, PC/ABS, PBT, PA6, etc. Its products have been widely used in industries such as LED lighting, consumer electronics, new energy, security equipment, and small household appliances, providing customers with efficient delivery experience, ultimate price advantages, and strict quality assurance, contributing to the creation of a green and environmentally friendly world.

Dongguan FOREVER Co., Ltd's main products has obtained UL certification for RTI authorized temperature, outdoor weather resistance F1 and 5VA flame retardancy grades, as well as recycled-certified post-consumer low-carbon circulation products. Dongguan FOREVER Co., Ltd's products are highly recognized by customers worldwide for their reliable quality, excellent performance, and superior cost-effectiveness.

With a strong focus on research and development, Dongguan FOREVER Co., Ltd. Has established an advanced technology research and development center, equipped with state-of-the-art testing and analysis equipment and a professional R&D team that has accumulated rich experience in the field of polymer composite modified materials. Dongguan FOREVER Co., Ltd also maintains close partnerships with renowned universities and research institutions to stay at the forefront of technology and drive innovation in the industry.