Product Description |
Opaque EXL, UV-Stabilized & light shielding capability, for portable electronics device enclosure application. Only available in white, grey and limited pastel colors. Consult CIC or PM for color availability & limitation. |
General |
Form Resin Pellets |
Filler Mineral |
Feature |
Low Temperature Impact High Impact Light Shielding |
Outdoor |
Uses |
Tablets And Portable Devices |
Electrical |
Physical Nominal Value Test Method |
Density / Specific Gravity 1.3 g/cm³ ISO 1183 |
Melt Volume Rate, MVR(1.2 kg;MVR at 300 °C) 12 cm³/10 min ISO 1133 |
Mechanical Nominal Value Test Method |
Izod Impact, Notched(23 °C) 532 J/m ASTM D256 |
Tensile Stress, Yield(50 mm/min;Type I) 52 MPa ASTM D638 |
Tensile Stress, Break(50 mm/min;Type I) 46 MPa ASTM D638 |
Tensile Strain, Yield(50 mm/min;Type I) 5 % ASTM D638 |
Tensile Strain, Break(50 mm/min;Type I) 68 % ASTM D638 |
Tensile Modulus(50 mm/min) 2030 MPa ASTM D638 |
Flexural Stress, Yield(1.3 mm/min;50 mm;span) 80 MPa ASTM D790 |
Flexural Modulus(1.3 mm/min;50 mm;span) 1970 MPa ASTM D790 |
Thermal Nominal Value Test Method |
Heat Deflection Temperature[HDT], Unannealed(3.2 mm;1.82 MPa) |
114 °C ASTM D648 |
Processing |
Nominal Value |
Drying Temperature<Injection> |
120 °C |
Drying Time<Injection> |
3 - 4 hrs |
Maximum Moisture Content<Injection> |
0.02 % |
Melt Temperature<Injection> |
295 - 315 °C |
Nozzle Temperature<Injection> |
290 - 310 °C |
Front, Zone 3 Temperature<Injection> |
295 - 315 °C |
Middle, Zone 2 Temperature<Injection> |
280 - 305 °C |
Rear, Zone 1 Temperature<Injection> |
260 - 280 °C |
Hopper Temperature<Injection> |
60 - 80 °C |
Mold Temperature<Injection> |
70 - 95 °C |