50% Glass Reinforced PA4T Suitable for NMT Suitable for PVD Automotive applications
https://forever-plastics.en.made-in-china.com/product/rJwRvlcdZpWD/China-Nylon-PA6-GF33-PA66-Granules-PA6-with-30GF-Polyamide-PA66-30-GF-PA6-Material.html Heat-conducting nylon
Product Description | ||
PARA LGF-1050 is a 50% Long Glass Fiber reinforced, heat stabilized polyarylamide PARA with excellent surface gloss, low moisture absorption and high heat deflection temperature. It exhibits unique stiffness/toughness combination, an excellent retention of properties in a wide temperature range, as well as outstanding creep resistance. PARA LGF-1050 has a pellet length of 9mm and can be processed on most injection-molding machines. It is available in black and natural. Black: PARA LGF-1050 BK 000-9 Natural: PARA LGF-1050 NT-9 |
||
General | ||
Form Resin Pellets | ||
Filler 50 % Long Glass Fiber | ||
Creep Resistance | ||
g mpac g empera ure | ||
Industrial Applications Aerospace | ||
Physical Nominal Value Test Method | ||
Density / Specific Gravity 1.64 g/cm³ ISO 1183 | ||
Water Absorption, Equilibrium(50% RH;23 °C) 1.2 % ISO 62 | ||
Mold Shrinkage, Flow 0.10 - 0.30 % Internal Method | ||
Mechanical Nominal Value Test Method | ||
Tensile Modulus ISO 527-2 | ||
23 °C 22000 MPa | ||
70 °C 20000 MPa | ||
Tensile Stress ISO 527-2 | ||
23 °C 265 MPa | ||
70 °C 205 MPa | ||
Tensile Strain, Break 1.6 % ISO 527-2 | ||
Flexural Modulus(23 °C) 21000 MPa ISO 178 | ||
Flexural Stress(23 °C) 405 MPa ISO 178 | ||
C harpy Notched Impact Strength(23 °C) 34 kJ/m² ISO 179 | ||
C harpy Unnotched Impact Strength(23 °C) 60 kJ/m² ISO 179 | ||
Thermal | Nominal Value | Test Method |
Heat Deflection Temperature, Unannealed | ||
0.45 MPa | 260 °C | ISO 75-2/B |
1.8 MPa | 255 °C | ISO 75-2/A |
Processing | Nominal Value | |
Drying Temperature<Injection> | 120 °C | |
Drying Time<Injection> | 4.0 hr | |
Suggested Max Moisture<Injection> | 0.080 % | |
Rear Temperature<Injection> | 280 - 300 °C | |
Middle Temperature<injection> | 280 - 310 °C | |
Front Temperature<Injection> | 280 - 310 °C | |
Nozzle Temperature<Injection> | 270 - 310 °C | |
Processing Temp, Melt<Injection> | < 310 °C | |
Mold Temperature<Injection> | 120 - 140 °C |