Product Description | |||
20% Glass reinforced, chemically coupled; values are based on natural or black materials unless otherwise noted. | |||
General | |||
Form | Resin Pellets | ||
Filler | 20 % Glass Fiber | ||
Physical | Nominal Value | Test Method | |
Specific Gravity | 1.04 g/cm³ | ASTM D792 | |
Filler Content | 20.0 % | ASTM D2584 | |
Linear Mold Shrinkage | 0.1 - 0.4 % | ASTM D955 | |
Linear Mold Shrinkage, Transverse | 0.4 - 0.8 % | ASTM D955 | |
Melt Flow | 10.0 g/10min | ASTM D1238 | |
Mechanical | Nominal Value | Test Method | |
Tensile Strength, Yield | 52.0 MPa | ASTM D638 | |
Elongation at Break | 4.00 % | ASTM D638 | |
Flexural Strength | 86.0 MPa | ASTM D790 | |
Flexural Modulus | 3450 MPa | ASTM D790 | |
Izod Impact, Notched(Thickness; 3.17 mm) | 133 J/m | ASTM D256 | |
Thermal | Nominal Value | Test Method | |
Deflection Temperature | ASTM D648 | ||
Thickness; 3.17 mm;Pressure; 0.46 MPa | 146 °C | ||
Thickness; 3.17 mm;Pressure; 1.8 MPa | 132 °C | ||
Flammability, UL94 Thickness; 3 mm;All Color Recognition Thickness; 1.5 mm;All Color Recognition |
HB HB |
||
Processing | Nominal Value | ||
Rear Barrel Temperature | 204 - 249 °C | ||
Middle Barrel Temperature | 216 - 260 °C | ||
Front Barrel Temperature | 216 - 260 °C | ||
Nozzle Temperature | 216 - 260 °C | ||
Melt Temperature | 216 - 260 °C | ||
Mold Temperature | 26.7 - 60.0 °C | ||
Back Pressure | 0.345 - 0.689 MPa |