40% Glass Reinforced PA4t Heat Stabilized for Automotive Applications

• Feature: Oxidative Degradable
• CAS No.: 32131-17-2
• Formula: (C12h22n2o2)N
• Shipping Cost: Estimated freight per unit.: about shipping cost and estimated delivery time.
• Currency: US$
• Return&refunds: You can apply for a refund up to 30 days after receipt of the products.
• Model NO.: PA4T-MX2
• EINECS: 211-024-8
• Material: Polyamide(Nylon 6.66)/PA
• Usage: General Plastics, Engineering Plastics, Specialty Plastics
• Plastic Properties After Heated: Thermoplastic Plastics
• Plastic Forming Method: Injection
• Color: Black
• Form: Resin Pellets
• Chemical Substances: Nylon
• Processing Mode: Injection Molding/Extrusion
• UV: Fr
• Use: Electrical Appliances, Auto Parts, Office Supplies
• Certificates: ISO9001:2008.SGS.RoHS
• Filler: 5%-60% Glass Fiber
• Transport Package: Bag
• Specification: 25KG
• Trademark: Forever
• Origin: China
• HS Code: 390740000
• Production Capacity: 50000t/Year
• Package Size: 75.00cm * 55.00cm * 15.00cm
• Package Gross Weight: 25.010kg

Product Description

40% Glass Reinforced PA4T Heat Stabilized for Automotive applications
 Heat-conducting nylon

Product Description

Product Description
40% Glass Reinforced, PA4T, Heat Stabilized, for Automotive applications
General
Form                                        Resin Pellets
Filler                                          40 % Glass Fiber
Feature                                     Good Thermal
Uses                                         Automotive
Physical                                                                                 Nominal Value                                       Test Method
Density, dry                                                                           1.55 g/cm³                                              ISO 1183
Dry: Molding Shrinkage, Across Flow                                 1.0 %                                                       ISO 294-4
Dry: Molding Shrinkage, Flow                                             0.35 %                                                     ISO 294-4
Dry: Water Absorption, Equilibrium(50% RH;23 °C)           1.6 %                                                       ISO 62
Mechanical                                                                            Nominal Value                                      Test Method
Dry: Tensile Modulus                                                                                                                          ISO 527-2
14500 MPa
-40 °C                                                                                   14500 MPa
40 °C                                                                                    14200 MPa
80 °C                                                                                     13800 MPa
100 °C                                                                                   12500 MPa
120 °C                                                                                   9500 MPa
150 °C                                                                                   6700 MPa
160 °C                                                                                   6300 MPa
180 °C                                                                                   5500 MPa
200 °C                                                                                   5300 MPa
Condition: Tensile Modulus                                                14500 MPa                                             ISO 527-2
Dry: Tensile Stress, Break -40 °C 40 °C 80 °C 100 °C 120 °C 150 °C 160 °C 180 °C 200 °C	220 MPa 240 MPa 210 MPa 190 MPa 160 MPa 130 MPa 100 MPa 95.0 MPa 90.0 MPa 82.0 MPa		ISO 527-2
Condition: Tensile Stress, Break	210 MPa		ISO 527-2
Dry: Tensile Strain, Break -40 °C 40 °C 100 °C 120 °C 150 °C 160 °C 180 °C 200 °C 80 °C	2.1 % 2.1 % 2.2 % 3.0 % 5.1 % 6.9 % 7.0 % 7.0 % 7.0 % 2.5 %		ISO 527-2 ISO 527-2 ISO 527-2 ISO 527-2 ISO 527-2 ISO 527-2 ISO 527-2 ISO 527-2 ISO 527-2 ASTM D790;ISO 178;ISO 527-2
Condition: Tensile Strain, Break	2.0 %		ISO 527-2
Dry: Flexural Modulus 120 °C 160 °C	14200 MPa 9800 MPa 6000 MPa		ISO 178
Dry: Flexural Stress	340 MPa		ISO 178
Dry: Charpy Notched Impact Strength -30 °C 23 °C	9.0 kJ/m² 9.0 kJ/m²		ISO 179 1eA
Dry: Charpy Unnotched Impact Strength -30 °C 23 °C		55 kJ/m² 65 kJ/m²		ISO 179 1eU
Condition: Charpy Unnotched Impact Strength(23 °C)		55 kJ/m²		ISO 179 1eU
Thermal		Nominal Value		Test Method
Dry: Heat Deflection Temperature, Unannealed(1.8 MPa)		305 °C		ISO 75-2/A
Dry: Melting Temperature(10 °C/min)		325 °C		ISO 11357-3
Dry: CLTE, Flow		3.0E-5 cm/cm/°C		ASTM D696
Dry: CLTE, Transverse		3.5E-5 cm/cm/°C		ASTM D696
Electrical		Nominal Value		Test Method
Dry: Volume Resistivity		> 1.0E+15 Ohms ·cm		IEC 60093
Condition: Volume resistivity		> 1.0E+15 Ohms ·cm		IEC 60093
Dry: Relative permittivity 100 Hz 1.0e+6 Hz		4.90 4.60		IEC 60250
Condition: Relative Permittivity 100 Hz 1.0e+6 Hz		5.70 4.80		IEC 60250

 

                                                                                                                  Forever Co.,Ltd

 

With almost 20 years in the modified engineering plastics,Forever Plastics is a high-tech manufacture integrating R&D, production and sales of high-performance resin or polymer ,including PC,PP,PA6,PA66, PBT,PET, PC/ABS, PC/PBT, PC/PET alloy compounds,TPE,TPU, PE for rotomolding with the property of the flame retardant, glass fiber reinforced, high glossy, UV resistance.....with the annual output value of USD 65 million in 2021. 