KN333NW is a Polyamide 66 (Nylon 66) processed by injection molding Flame Rated
https://forever-plastics.en.made-in-china.com/product/rJwRvlcdZpWD/China-Nylon-PA6-GF33-PA66-Granules-PA6-with-30GF-Polyamide-PA66-30-GF-PA6-Material.html Heat-conducting nylon
Product Description | ||
KN333NW is a Polyamide 66 (Nylon 66) product. It can be processed by injection molding and is available in Asia Pacific, Europe, Latin America, or North America. Characteristics include: Flame Rated RoHS Compliant Good Dimensional Stability Impact Resistant |
||
General | ||
Form Resin Pellets | ||
Feature Good Dimensional Ductile | ||
Physical | Nominal Value | Test Method |
Density / Specific Gravity | 1.10 g/cm³ | ASTM D792;ISO 1183 |
Molding Shrinkage, Flow | 1.6 - 1.9 % 1.4 % |
ASTM D955 ISO 294-4 |
Molding Shrinkage, Across Flow | 1.6 % | ISO 294-4 |
Water Absorption(24 hr;23 °C) | 1.7 % | ISO 62 |
Water Absorption, Equilibrium(60% RH;23 °C) | 1.0 % | ASTM D570 |
Rockwell Hardness, R-Scale | 120 111 |
ASTM D785 ISO 2039-2 |
Mechanical | Nominal Value | Test Method |
Tensile Strength | ||
23 °C | 59.0 MPa | ASTM D638 |
23 °C | 120 MPa | ISO 527-2 |
Tensile Elongation, Break | ||
23 °C | 50 % | ASTM D638 |
23 °C | 80 % | ISO 527-2 |
Flexural Modulus | ||
23 °C | 1960 MPa | ASTM D790 |
23 °C | 2000 MPa | ISO 178 |
Flexural Strength | ||
23 °C | 98.0 MPa | ASTM D790 |
23 °C | 80.0 MPa | ISO 178 |
C harpy Notched Impact Strength(23 °C) | 60 kJ/m² | ISO 179 1eA |
Notched Izod Impact(23 °C) | 590 J/m | ASTM D256 |
Thermal | Nominal Value | Test Method |
Deflection Temperature Under Load, Unannealed 0.45 MPa 1.8 MPa |
205 °C 70.0 °C |
ASTM D648 |
Melting Point | 255 °C | ASTM D1525;ISO 11357-3 |
CLTE, Flow | 6.0E-5 cm/cm/°C | ASTM D696 |
Flame Rating(0.8 mm) | HB | UL 94 |
Electrical | Nominal Value | Test Method |
Dielectric Strength | 20 kV/mm | ASTM D149 |
Dielectric Constant(1.0e+6 Hz) | 3.10 | ASTM D150 |
Arc Resistance | 125 sec | ASTM D495 |
Processing | Nominal Value | |
Drying Temperature - Desiccant Dryer<Injection> | 80 - 100 °C | |
Drying Time - Desiccant Dryer<Injection> | 4.0 - 5.0 hr | |
Suggested Max Moisture<Injection> | < 0.050 % | |
Rear Temperature<Injection> | 260 °C | |
Middle Temperature<injection> | 265 °C | |
Front Temperature<Injection> | 270 °C | |
Nozzle Temperature<Injection> | 275 °C | |
Mold Temperature<Injection> | 60 - 80 °C |