Resistant High Strength Impact Modified Typical application of PA66
https://forever-plastics.en.made-in-china.com/product/rJwRvlcdZpWD/China-Nylon-PA6-GF33-PA66-Granules-PA6-with-30GF-Polyamide-PA66-30-GF-PA6-Material.html Heat-conducting nylon
Product Description | |||||
PA66-G10 HSBK101 is a Polyamide 66 (Nylon 66) material filled with 10% glass fiber. It is available in Asia Pacific or North America for injection molding. Important attributes of PA66-G10 HSBK101 are: Flame Rated Good Dimensional Stability Heat Resistant High Strength Impact Modified Typical application of PA66-G10 HSBK101: Automotive | |||||
General | |||||
Form | Resin Pellets | ||||
Filler | 10 % Glass Fiber | ||||
Feature | Good Dimensional Good Thermal | High Impact | |||
Uses Automotive | |||||
Physical | Nominal Value | Test Method | |||
Density / Specific Gravity | 1.20 g/cm³ | ISO 1183 | |||
Molding Shrinkage, Across Flow | 1.0 % | ISO 2577 | |||
Molding Shrinkage, Flow | 0.50 % | ISO 2577 | |||
Water Absorption, Equilibrium(50% RH;23 °C) | 2.2 % | ISO 62 | |||
Ash Content | 10 % | ISO 3451-1 | |||
Ball Indentation Hardness(23 °C) | 180 MPa | ISO 2039-1 | |||
Mechanical | Nominal Value | Test Method | |||
Tensile Modulus | 4800 MPa | ISO 527-2/1 | |||
Tensile Stress | 110 MPa | ISO 527-2/5 | |||
Tensile Strain, Break | 3.5 % | ISO 527-2/5 | |||
Flexural Modulus(2 mm/min) | 4000 MPa | ISO 178 | |||
Flexural Stress(2 mm/min) | 155 MPa | ISO 178 | |||
C harpy Notched Impact Strength(23 °C) | 6.0 kJ/m² | ISO 179 1eA | |||
Thermal | Nominal Value | Test Method | |||
Heat Deflection Temperature, Unannealed | |||||
0.45 MPa | 250 °C | ISO 75-2/B | |||
1.8 MPa | 235 °C | ISO 75-2/A | |||
Flame Rating(1.6 mm) | HB | UL 94 | |||
Electrical | Nominal Value | Test Method | |||
Volume Resistivity | 1.0e+15 ohms ·cm | IEC 60093 | |||
Processing | Nominal Value | ||||
Drying Temperature<Injection> | 100 - 130 °C | ||||
Drying Time<Injection> | 4.0 - 6.0 hr | ||||
Rear Temperature<Injection> | 270 - 285 °C | ||||
Middle Temperature<injection> | 280 - 290 °C | ||||
Front Temperature<Injection> | 290 - 300 °C | ||||
Processing Temp, Melt<Injection> | 270 - 290 °C | ||||
Mold Temperature<Injection> | 40 - 100 °C | ||||
Injection Rate<Injection> | Moderate-Fast |