Feature: | Plastics |
---|---|
CAS No.: | 63440-93-7 |
Formula: | C24h24o8 |
Samples: |
25kg/bag
|
---|
Customization: |
---|
Shipping Cost:
Estimated freight per unit. |
about shipping cost and estimated delivery time. |
---|
Payment Method: | |
---|---|
Initial Payment Full Payment |
Currency: | US$ |
---|
Return&refunds: | You can apply for a refund up to 30 days after receipt of the products. |
---|
Suppliers with verified business licenses
General | ||||||
Form Resin Pellets | ||||||
Feature | Ductile | Good Platable | ||||
Appliances Lighting Applications Automotive Lighting | ||||||
Electronic Displays | Lawn And Garden Equipment | Pharmaceuticals | ||||
Usage Aerospace | Automotive | Sporting Goods | ||||
Automotive Exterior | Automotive Interior |
Constraction |
||||
Rail |
Outdoor |
|||||
Physical | Nominal Value | Test Method | ||||
Density / Specific Gravity | 1.10 g/cm³ | ASTM D792 | ||||
Melt Mass-Flow Rate, MFR(260 °C;5 kg) | 14 g/10min | ASTM D1238 | ||||
Molding Shrinkage, Across Flow(3.2 mm) | 0.50 - 0.70 % | Internal Method | ||||
Molding Shrinkage, Flow(3.2 mm) | 0.50 - 0.80 % | Internal Method | ||||
Water Absorption(24 hr) | 0.10 % | ASTM D570 | ||||
Mechanical | Nominal Value | Test Method | ||||
Tensile Modulus(50 mm/min) | 2130 MPa | ASTM D638 | ||||
Tensile Strength, Yield(50 mm/min;Type I) | 50.0 MPa | ASTM D638 | ||||
Tensile Strength, Break(50 mm/min;Type I) | 44.0 MPa | ASTM D638 | ||||
Tensile Elongation, Yield(50 mm/min;Type I) | 8.6 % | ASTM D638 | ||||
Tensile Elongation, Break(50 mm/min;Type I) | 150 % | ASTM D638 | ||||
Flexural Modulus(1.3 mm/min;50 mm;Span) | 2060 MPa | ASTM D790 | ||||
Flexural Strength, Yield(1.3 mm/min;50 mm;Span) | 72.0 MPa | ASTM D790 | ||||
Notched Izod Impact | ASTM D256 | |||||
-30 °C | 430 J/m | |||||
23 °C | 530 J/m | |||||
Instrumented Dart Impact, Total Energy | ASTM D3763 | |||||
-30 °C | 33.0 J | |||||
23 °C | 40.0 J |
Thermal | Nominal Value | Test Method |
Deflection Temperature Under Load, Unannealed 0.45 MPa;3.2 mm 1.8 MPa;3.2 mm |
115 °C 98.0 °C |
ASTM D648 |
Vicat Softening Temperature(50 °C/h;50 N;Rate A;Loading 2) | 111 °C | ASTM D1525 |
CLTE, Flow(-40 - 40 °C) | 7.2E-5 cm/cm/°C | ASTM E831 |
CLTE, Transverse(-40 - 40 °C) | 9.0E-5 cm/cm/°C | ASTM E831 |
Thermal Conductivity | 0.20 W/m-K | ASTM C177 |
Processing | Nominal Value | |
Drying Temperature<Injection> | 100 - 105 °C | |
Drying Time<Injection> | 3.0 - 4.0 hr | |
Suggested Max Moisture<Injection> | 0.020 % | |
Suggested Shot Size<Injection> | 30 - 80 % | |
Rear Temperature<Injection> | 250 - 280 °C | |
Middle Temperature<injection> | 255 - 290 °C | |
Front Temperature<Injection> | 255 - 290 °C | |
Nozzle Temperature<Injection> | 260 - 290 °C | |
Processing Temp, Melt<Injection> | 260 - 290 °C | |
Mold Temperature<Injection> | 75 - 100 °C | |
Back Pressure<Injection> | 0.300 - 0.700 MPa | |
Screw Speed <Injection> | 40 - 70 rpm | |
Vent Depth <Injection> | 0.038 - 0.076 mm | |
Drying Time, Cumulative<Injection> | 8 hrs |