PC/ABS low gloss. |
General |
Form Resin Pellets |
Feature Low Gloss Outdoor |
UL Yellow Card E207780-523226 |
Appliances Lighting Applications Automotive Lighting |
Uses Electronic Displays Automotive Automotive Exterior |
Automotive Interior Constraction Household Applications |
Physical Nominal Value Test Method |
Density / Specific Gravity 1.13 g/cm³ ASTM D792 |
Melt Mass-Flow Rate, MFR(260 °C;5 kg) 17 g/10min ASTM D1238 |
Molding Shrinkage, Across Flow(3.2 mm) 0.50 - 0.70 % Internal Method |
Molding Shrinkage, Flow(3.2 mm) 0.50 - 0.70 % Internal Method |
Water Absorption(24 hr) 0.10 % ASTM D570 |
Water Absorption, Equilibrium(23 °C) 0.40 % ASTM D570 |
Rockwell Hardness, R-Scale 118 ASTM D785 |
Mechanical Nominal Value Test Method |
Tensile Strength, Yield(50 mm/min;Type I) 54.0 MPa ASTM D638 |
Tensile Elongation, Break(50 mm/min;Type I) 75 % ASTM D638 |
Flexural Modulus(1.3 mm/min;50 mm;Span) 2300 MPa ASTM D790 |
Flexural Strength, Yield(1.3 mm/min;50 mm;Span) 84.0 MPa ASTM D790 |
Notched Izod Impact ASTM D256 |
-30 °C 320 J/m |
23 °C 530 J/m |
Instrumented Dart Impact, Total Energy ASTM D3763 |
-30 °C 33.0 J |
23 °C 40.0 J |
Thermal | Nominal Value | Test Method |
Deflection Temperature Under Load, Unannealed 0.45 MPa;3.2 mm 0.45 MPa;6.4 mm 1.8 MPa;3.2 mm 1.8 MPa;6.4 mm |
123 °C 129 °C 107 °C 110 °C |
ASTM D648 |
Vicat Softening Temperature(50 °C/h;50 N;Rate A;Loading 2) | 129 °C | ASTM D1525 |
CLTE, Flow(-20 - 150 °C) | 7.2E-5 cm/cm/°C | ASTM E831 |
CLTE, Transverse(-20 - 150 °C) | 7.2E-5 cm/cm/°C | ASTM E831 |
Thermal Conductivity | 0.20 W/m-K | ASTM C177 |
RTI Elec | 60.0 °C | UL 746 |
RTI Imp | 60.0 °C | UL 746 |
RTI Str | 60.0 °C | UL 746 |
Flame Rating(1.5 mm) | HB | UL 94 |
Electrical | Nominal Value | Test Method |
Arc Resistance, Tungsten Electrode | PLC 6 | ASTM D495 |
Comparative Tracking Index[CTI] | PLC 2 | UL 746 |
High Amp Arc Ignition, HAI, Surface | PLC 0 | UL 746 |
Hot-wire Ignition, HWI | PLC 2 | UL 746 |
Optical | Nominal Value | Test Method |
Gardner Gloss, Untextured(60°) | 30 | ASTM D523 |
Processing | Nominal Value |
Drying Temperature<Injection> | 105 - 110 °C |
Drying Time<Injection> | 3.0 - 4.0 hr |
Suggested Max Moisture<Injection> | 0.040 % |
Suggested Shot Size<Injection> | 30 - 80 % |
Rear Temperature<Injection> | 250 - 290 °C |
Middle Temperature<injection> | 255 - 295 °C |
Front Temperature<Injection> | 260 - 300 °C |
Nozzle Temperature<Injection> | 275 - 300 °C |
Processing Temp, Melt<Injection> | 275 - 300 °C |
Mold Temperature<Injection> | 60 - 90 °C |
Back Pressure<Injection> | 0.300 - 0.700 MPa |
Screw Speed <Injection> | 40 - 70 rpm |
Vent Depth <Injection> | 0.038 - 0.076 mm |
Drying Time, Cumulative<Injection> | 8 hrs |