Feature: | Oxidative Degradable |
---|---|
CAS No.: | 32131-17-2 |
Formula: | (C12h22n2o2)N |
Samples: |
---|
Customization: |
---|
Shipping Cost:
Estimated freight per unit. |
about shipping cost and estimated delivery time. |
---|
Payment Method: | |
---|---|
Initial Payment Full Payment |
Currency: | US$ |
---|
Return&refunds: | You can apply for a refund up to 30 days after receipt of the products. |
---|
Suppliers with verified business licenses
Polyamide 6 mineral filler flame retardant halogen red phosphorous for injection moulding
https://forever-plastics.en.made-in-china.com/product/rJwRvlcdZpWD/China-Nylon-PA6-GF33-PA66-Granules-PA6-with-30GF-Polyamide-PA66-30-GF-PA6-Material.html Heat-conducting nylon
(DOMAMID 6M30GT96M) Polyamide 6, 30% mineral filler, flame retardant, halogen and red phosphorous free, for injection moulding | ||
General | ||
Form Resin Pellets | ||
Filler 30 % Mineral | ||
Non-Brominated & Non- | ||
Feature | Chlorinated Flame | |
Retardant | ||
Physical | Nominal Value | Test Method |
Density / Specific Gravity | 1.40 g/cm³ | ISO 1183 |
Molding Shrinkage, Across Flow(50% RH;23 °C;72 hr) | 0.70 - 0.90 % | ISO 2577 |
Molding Shrinkage, Flow(50% RH;23 °C;72 hr) | 0.70 - 0.90 % | ISO 2577 |
Mechanical | Nominal Value | Test Method |
Tensile Modulus | 5600 MPa | ISO 527-2/1 |
Tensile Stress, Break | 80.0 MPa | ISO 527-2/5 |
Tensile Strain, Break | 3.0 % | ISO 527-2/5 |
Flexural Modulus(2 mm/min) | 5400 MPa | ISO 178 |
Flexural Stress(2 mm/min) | 125 MPa | ISO 178 |
C harpy Notched Impact Strength(23 °C) | 4.5 kJ/m² | ISO 179 1eA |
C harpy Unnotched Impact Strength(23 °C) | 30 kJ/m² | ISO 179 1eU |
Notched Izod Impact Strength(23 °C) | 4.0 kJ/m² | ISO 180/1A |
Unnotched Izod Impact Strength(23 °C) | 30 kJ/m² | ISO 180/1U |
Thermal | Nominal Value | Test Method |
Heat Deflection Temperature, Unannealed 0.45 MPa 1.8 MPa |
200 °C 100 °C |
ISO 75-2/B ISO 75-2/A |
Vicat Softening Temperature | 205 °C | ISO 306/B50 |
Melting Point | 221 °C | ISO 11357-3 |
Burning rate | < 100 mm/min | FMVSS 302 |
Flame Rating 0.8 mm 1.5 mm 3 mm |
V-2 V-2 V-2 |
UL 94 |
Glow Wire Flammability Index(1 - 3 mm) | 960 °C | IEC 60695-2-12 |
Glow Wire Ignition Temperature [GWIT](1 - 3 mm) | 700 °C | IEC 60695-2-13 |
Electrical | Nominal Value | Test Method |
Surface Resistivity | 1.0E+13 ohms | IEC 60093 |
Volume Resistivity | 1.0e+15 ohms ·cm | IEC 60093 |
Comparative Tracking Index, Solution A | 500 V | IEC 60112 |
Processing | Nominal Value | |
Drying Temperature<Injection> | 75 - 85 °C | |
Drying Time<Injection> | 2.0 - 4.0 hr | |
Processing Temp, Melt<Injection> | 240 - 260 °C | |
Mold Temperature<Injection> | 70 - 90 °C |